A kind of aluminum-lithium alloy and forging method

A technology of aluminum-lithium alloy and forging ratio, which is applied in the field of aluminum-lithium alloy materials and their forging, can solve the problems of residual original grain boundaries, unsuitability for the manufacture of large and thick parts with a thickness of more than 40mm, and low elongation in the high direction, and achieve improved The effect of high elongation

Active Publication Date: 2019-06-28
AVIC BEIJING INST OF AERONAUTICAL MATERIALS
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Critically saturated alloying elements will produce a large number of grain boundary precipitated phases. These phases have a "pinning" effect in the plastic forming process, resulting in a large number of original grain boundary residues, resulting in low elongation in the high direction, which is not suitable for manufacturing large thickness specifications above 40mm parts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of aluminum-lithium alloy and forging method
  • A kind of aluminum-lithium alloy and forging method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Alloy composition: 4.0% Cu, 0.8% Mg, 1.2% Li, 0.4% Ag, 0.10% Zr, 0.4% Mn, 0.4% Zn, Si≤0.08%, Fe≤0.10%, other impurities individually ≤0.05%, total ≤0.15%, the balance is Al.

[0021] Homogenization treatment: heat the blank to 420°C, hold for 2 hours; continue to heat up to 480°C, hold for 38 hours; cool to 200°C with the furnace, and air cool to room temperature;

[0022] Ingot forging billet opening: initial forging temperature 380°C, final forging temperature 350°C, forging ratio 3;

[0023] Low temperature forging: initial forging temperature 340℃, forging ratio 2.6;

[0024] High temperature forging: the initial forging temperature is 400°C, the final forging temperature is 380°C, and the forging ratio is 4.

Embodiment 2

[0026] Alloy composition: 4.0% Cu, 0.4% Mg, 1.2% Li, 0.4% Ag, 0.10% Zr, 0.4% Mn, Si≤0.08%, Fe≤0.10%, other impurities individually ≤0.05%, total ≤0.15%, The balance is Al.

[0027] Homogenization treatment: heat the blank to 420°C, hold for 6 hours; continue to heat up to 490°C, hold for 40 hours; cool to 200°C with the furnace, and air cool to room temperature;

[0028] Ingot forging billet opening: initial forging temperature 400°C, final forging temperature 300°C, forging ratio 3.3;

[0029] Low temperature forging: initial forging temperature 340℃, forging ratio 2.6;

[0030] High temperature forging: the initial forging temperature is 410°C, the final forging temperature is 380°C, and the forging ratio is 4.2.

Embodiment 3

[0032] Alloy composition: 3.2% Cu, 1.2% Mg, 1.0% Li, 0.4% Ag, 0.10% Zr, 0.4% Mn, Si≤0.08%, Fe≤0.10%, other impurities individually ≤0.05%, total ≤0.15%, The balance is Al.

[0033] Homogenization treatment: heat the blank to 430°C, hold for 8 hours; continue to heat up to 500°C, hold for 45 hours; cool to 200°C with the furnace, and air cool to room temperature;

[0034] Ingot forging billet opening: initial forging temperature 420°C, final forging temperature 350°C, forging ratio 4;

[0035] Low temperature forging: initial forging temperature 260°C, forging ratio 2.7;

[0036] High temperature forging: the initial forging temperature is 420°C, the final forging temperature is 380°C, and the forging ratio is 4.5.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of metallic material engineering and relates to an aluminum-lithium alloy material and a forging method thereof. The aluminum-lithium alloy material comprises the alloy components of, by mass, 3%-4.2% of Cu, 0.2%-1.4% of Mg; 0.6%-1.5% of Li, 0-1% of Ag, 0.06%-0.15% of Zr, 0.2%-0.6% of Mn, 0-0.8% of Zn, 0.08% of Si or the less, 0.10% of Fe or the less and the balance Al and other impurities, wherein the mass of one of the other impurities is smaller than or equal to 0.05%, and the total mass of the other impurities is smaller than or equal to 0.15%. The forging method comprises the following steps of homogenization treatment and forging. According to the aluminum-lithium alloy material and the forging method thereof, the situation that a large number of grain boundary precipitation phases are generated by critical saturated alloy elements, and thus a large number of original grain boundary residues are caused can be avoided, the high elongation rate isincreased, and the requirement for manufacturing workpieces with the large thickness specifications of 40 mm or above is met.

Description

technical field [0001] The invention belongs to the field of metal material engineering and relates to an aluminum-lithium alloy material and a forging method thereof. Background technique [0002] Due to the addition of lithium element, aluminum-lithium alloy has obtained low density and high modulus characteristics, and has broad application prospects in aerospace, nuclear industry, transportation, sporting goods, weapons and other fields. In recent years, with the improvement of aluminum metallurgical equipment technology and metallurgical basic technology, the development trend of aluminum alloy is high purity, high performance and high alloying. The 500MPa aluminum-lithium alloy has been maturely applied in advanced fighter jets, large airliners and aerospace delivery equipment. The amount of alloying elements added to the current aluminum-lithium alloy is close to or exceeds the high-temperature critical saturation solid solution of aluminum solid solution. Criticall...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/18C22F1/057
CPCC22C21/14C22C21/16C22C21/18C22F1/057
Inventor 冯朝辉王胜强何维维陆政
Owner AVIC BEIJING INST OF AERONAUTICAL MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com