A Method for Dendrite Corrosion and Measurement of High Carbon Steel Slab

A high-carbon steel and slab technology, which is applied in the field of high-carbon steel slab dendrite corrosion and measurement, can solve the problems of dendrite structure damage, large amount of chemical reagents, and slab structure errors, etc. organization clarity effect

Active Publication Date: 2020-10-02
MAANSHAN IRON & STEEL CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the existing slab dendrite corrosion method is mainly based on low-power acid etching method, the amount of chemical reagents is large, the corrosion degree is deep, and the dendrite structure is damaged to a certain extent, which will bring serious problems in the subsequent measurement of slab structure parameters. big error

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A Method for Dendrite Corrosion and Measurement of High Carbon Steel Slab
  • A Method for Dendrite Corrosion and Measurement of High Carbon Steel Slab

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The sample in the embodiment of the present invention, its chemical composition is C: 0.65%, Si: 0.8%, Mn: 0.5%, P: 0.015%, S: 0.020% high carbon steel continuous casting round billet sample, from the round billet Continuously cut samples with a length of 30 mm and a width of 20 mm from the surface layer to the radius of the core.

[0020] A method for dendrite corrosion and measurement of high carbon steel slab, comprising the following steps:

[0021] 1) Grind and polish the cross-section of the sample billet to a mirror surface according to the requirements of conventional metallographic inspection;

[0022] 2) Prepare a corrosive agent, dissolve picric acid and cuprous chloride in distilled water, then add detergent, stir and mix to obtain the product; the mass concentration of picric acid is 0.3%, and the mass concentration of cuprous chloride is 0.1%. The concentration of essence is 1%, and the balance is distilled water.

[0023] 3) Immerse the polished sample ...

Embodiment 2

[0026] The sample in the embodiment of the present invention, its chemical composition is C: 0.60%, Si: 0.75%, Mn: 0.55%, P: 0.013%, S: 0.015% high carbon steel continuous casting round billet sample, from the round billet Continuously cut samples with a length of 30 mm and a width of 20 mm from the surface layer to the radius of the core.

[0027] A method for dendrite corrosion and measurement of high carbon steel slab, comprising the following steps:

[0028] 1) Grind and polish the cross-section of the sample billet to a mirror surface according to the requirements of conventional metallographic inspection;

[0029] 2) Configure corrosive agent, dissolve picric acid and cuprous chloride in distilled water, then add detergent, stir and mix to get final product; the mass concentration of picric acid is 0.3%, the mass concentration of cuprous chloride is 0.15%, and the The concentration of essence is 1.5%, and the balance is distilled water.

[0030] 3) Immerse the polished...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for high-carbon steel casting blank dendritic crystal corrosion and measurement. The method comprises the following steps of (1) flatly grinding a test specimen according to the conventional golden phase inspection requirement; performing polishing to be with a mirror surface; (2) preparing a corrosive: dissolving picric acid and cuprous chloride into distilled water; then, adding cleanser essence; performing stirring and mixing to obtain the corrosive; (3) polishing the test specimen; then, soaking the test specimen into the corrosive; next, taking out the testspecimen. Compared with the prior art, the corrosive used by the method has the advantages that during the preparation, the consumption of used chemical reagents is low; the corrosion degree depth isproper; no damage is caused on the dendritic crystal tissues; the clear casting blank dendritic crystal tissues photos can be obtained and are used for quantitatively evaluating the dendritic crystaltissues; the method belongs to an environment-friendly and accurate test method.

Description

technical field [0001] The invention belongs to the technical field of metal material detection, and in particular relates to a method for dendrite corrosion and measurement of high-carbon steel slabs. Background technique [0002] The solidification microstructure of cast slab is the basic factor to determine its internal quality. By observing the solidification structure of the continuous casting slab and studying its morphological characteristics, it is possible to measure data such as the deflection angle of the columnar crystals and the secondary crystal spacing of the dendrites, and then speculate on its solidification conditions, which can provide a lot of information for improving the solidification conditions and the quality of the continuous casting slab. Valuable technical information. For example, for the same type of steel, although the smelting method and specifications are different, as long as the secondary grain distance is measured, the cooling rate can be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N17/00G01N1/28
CPCG01N1/28G01N17/00
Inventor 杨峥王德宝刘志军牟祖茂徐辉程志远
Owner MAANSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com