A preparation method of porous multi-branched pt-ni-cu alloy nanoparticles

A kind of alloy nano, multi-branch technology, applied in the direction of nanotechnology, nanotechnology, nanotechnology, etc. for materials and surface science, can solve the problems of low utilization rate, high price of Pt nanostructure catalyst, easy poisoning, etc., and achieve high activity The effects of high bit density, green and efficient preparation method, and wide application prospects

Active Publication Date: 2021-01-26
UNIV OF JINAN
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the above-mentioned technical problems, the present invention solves the technical problems of current Pt nanostructure catalysts such as high price, low utilization rate and easy poisoning, prepares a kind of porous and multi-branched Pt-Ni-Cu alloy nanoparticles with high-density active sites, and improves the Pt Performance of Nanostructured Catalysts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of porous multi-branched pt-ni-cu alloy nanoparticles
  • A preparation method of porous multi-branched pt-ni-cu alloy nanoparticles
  • A preparation method of porous multi-branched pt-ni-cu alloy nanoparticles

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Measure 2.0mL of 19.3mmol / L chloroplatinic acid aqueous solution, 1.0mL of 20mmol / L nickel chloride and 1.0mL of 20mmol / L copper chloride aqueous solution and 0.7mL of 1,3-propanediol in 50mL Then add glycine, polyvinylpyrrolidone K30 and NaF into the beaker, stir and dissolve with a magnetic stirrer, then transfer to a microwave reactor, after absolutely sealing, transfer to a microwave synthesizer and heat at 200°C for 30min for reaction, after the reaction is completed, Water and ethanol centrifugal washing, freeze-drying and other processing steps, wherein, the dosage range of polyvinylpyrrolidone K30 is 200mg, the dosage range of NaF is 580mg, the dosage range of glycine is 310mg, and the dosage range of 1.3-propanediol is 0.7mL to obtain porous multi-branched Pt-Ni-Cu alloy nanoparticles (such as figure 2 shown).

[0024] Methanol (formic acid) electro-oxidation test: The anode electro-oxidation performance test is carried out on a CHI650D electrochemical workst...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of porous multi-branch Pt-Ni-Cu alloy nanoparticles. The invention takes chloroplatinic acid, copper chloride and nickel chloride as raw materials, glycineand PVP as dual reducing agents, adopts specific addition amount of 1, 3- propylene glycol and NaF, the porous and multibranched Pt-Ni-Cu alloy nanoparticles which are highly selective are prepared through a microwave synthesis method, and the preparation method is green and efficient. The porous multibranched Pt-Ni-Cu alloy nanoparticles have many step atoms and high active site density, which show excellent electrochemical activity of methanol and formic acid, and have wide application prospects.

Description

technical field [0001] The invention belongs to the technical field of functional nanometer materials. Specifically, the present invention uses a microwave synthesis method to prepare a porous and multi-branched Pt-Ni-Cu alloy nanoparticle. Background technique [0002] Noble metal Pt nanostructure catalysts are widely used in environmental protection catalysis, biochemistry and other fields due to their excellent stability and good catalytic performance. However, due to the high cost of use and easy poisoning during use, this excellent nanocatalyst cannot be widely used on a large scale. One of the effective ways to solve these problems is to combine Pt with three-dimensional transition metals such as Ni, Cu, and Co to form Pt-based binary / multiple alloy catalysts. It has been proved that the catalytic activity of Pt-based alloy catalysts depends on the composition and composition of alloy nanoparticles. The surface topography, through the synergistic effect of electrons ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/92B82Y30/00
CPCB82Y30/00H01M4/921Y02E60/50
Inventor 吕一品杨绍寒高道伟陈国柱李春生
Owner UNIV OF JINAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com