Impact-resistant abrasion-resistant composite steel plate

A composite steel plate, impact-resistant technology, applied in the direction of welding medium, welding/cutting medium/material, layered products, etc., can solve the problems of low wear resistance, high cost of precious metals, low C content, etc., and achieve good wear resistance Effect with impact resistance, good impact resistance

Active Publication Date: 2018-12-25
江苏沃盾耐磨新材料有限公司
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the deficiencies in the prior art, the purpose of the present invention is to provide an impact-resistant and wear-resistant composite steel plate, which overcomes the defects of high cost of adding precious metals to the traditional wear-resistant layer and low wear-resistant strength caused by low C content; Low vanadium, purification and deterioration, grain refinement, is more conducive to the alloying of impact-resistant and wear-resistant composite steel plates, and improves the wear-resistant performance of the wear-resistant layer; within the composition and proportioning range of the present invention, the C content is increased, However, the wear-resistant layer still has good toughness, breaking the incompatibility between the wear-resistant strength and toughness of C in the traditional wear-resistant layer, so that the composite steel plate has both good wear-resistant strength and toughness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Impact-resistant abrasion-resistant composite steel plate
  • Impact-resistant abrasion-resistant composite steel plate
  • Impact-resistant abrasion-resistant composite steel plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029]An impact-resistant and wear-resistant composite steel plate, including a substrate layer and a wear-resistant layer, the components contained in the substrate layer and their weight percentages are: carbon: 0.20%; manganese: 1.50%; silicon: 0.45%; S<0.04%; P<0.03%; the balance is iron. The wear-resistant layer is a high-strength alloy composite layer, including components and their weight percentages: chromium: 55.00%; carbon: 8.00%; manganese: 0.50%; silicon: 3.00%; vanadium: 1.50%; nickel: 0.25%; Molybdenum: 0.25%; S<0.04%; P<0.03%; the balance is iron.

Embodiment 2

[0031] An impact-resistant and wear-resistant composite steel plate, including a substrate layer and a wear-resistant layer, the components contained in the substrate layer and their weight percentages are: carbon: 0.12%; manganese: 0.50%; silicon: 0.20%; S<0.04%; P<0.03%; the balance is iron. The components and weight percentages included in the wear-resistant layer are: chromium: 25.00%; carbon: 3.00%; manganese: 4.00%; silicon: 0.10%; vanadium: 0.10%; nickel: 3.00%; 0.04%; P<0.03%; the balance is iron.

Embodiment 3

[0033] An impact-resistant and wear-resistant composite steel plate, including a substrate layer and a wear-resistant layer, the components contained in the substrate layer and their weight percentages are: carbon: 0.15%; manganese: 0.80%; silicon: 0.25%; S<0.04%; P<0.03%; the balance is iron. The components and weight percentages of the wear-resistant layer are: chromium: 40.00%; carbon: 6.00%; manganese: 3.50%; silicon: 3.00%; vanadium: 0.10%; nickel: 2.50%; 0.04%; P<0.03%; the balance is iron.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
reduction of areaaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of metal welding materials, in particular to an impact-resistant abrasion-resistant composite steel plate. The impact-resistant abrasion-resistant composite steel plate comprises a base plate layer and an abrasion-resistant layer, wherein the base plate layer is a common steel plate, and the abrasion-resistant layer is a high-strength alloy composite layer. The abrasion-resistant layer comprises, by weight, 25.00%-55.00% of chromium, 3.00%-8.00% of carbon, 0.50%-4.00% of manganese, 0.10%-3.00% of silicon, 0.25%-3.00% of nickel, 0.25%-3.00% of molybdenum, 0.10%-1.50% of vanadium, and the balance iron and inevitable impurities. The impact-resistant abrasion-resistant composite steel plate overcomes the defects that precious metal adding in a traditional abrasion-resistant layer is high and the abrasion resistance is low caused by low C content. By adding a small amount of vanadium with lower cost, the abrasion resistance of the abrasion-resistant layer is improved. According to the impact-resistant abrasion-resistant composite steel plate, the C content is increased within the range of components and proportions, but the abrasion-resistantlayer still has better toughness, so that the composite steel plate has better abrasion-resistant strength and toughness.

Description

technical field [0001] The invention relates to the technical field of metal welding materials, in particular to an impact-resistant and wear-resistant composite steel plate. Background technique [0002] The traditional double-metal composite wear-resistant steel plate is composed of low-carbon steel plate and alloy wear-resistant layer. The wear-resistant layer generally accounts for 1 / 3-1 / 2 of the total thickness. When working, the matrix provides comprehensive properties such as strength, toughness and plasticity against external forces, and the wear-resistant layer provides wear-resistant properties that meet the requirements of specified working conditions. Wear-resistant steel plate has high wear resistance and good impact performance, can be cut, bent, welded, etc., and can be connected with other structures by welding, plug welding, bolt connection, etc., which saves time and Convenient and other features, it is widely used in metallurgy, coal, cement, electric pow...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C27/06C22C30/00C22C37/08C22C37/10C22C38/02C22C38/04B32B15/01B23K35/30
CPCB23K35/3086B32B15/011B32B15/013C22C27/06C22C30/00C22C37/08C22C37/10C22C38/02C22C38/04
Inventor 马俊青邓航海任海强李昆
Owner 江苏沃盾耐磨新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap