A kind of lead-free relaxation antiferroelectric ceramic energy storage material and preparation method thereof

An energy storage material and antiferroelectric technology, applied in the field of energy storage ceramic materials, can solve the problems of immature mass production technology, limited use range, small dielectric constant, etc., to improve energy storage density and energy storage efficiency , Improve energy storage efficiency and energy storage density, the effect of high density

Active Publication Date: 2020-10-27
XI AN JIAOTONG UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The second category is organic film-based materials, such as polypropylene film, polyester film, polyvinylidene fluoride film, etc., which have very high breakdown field strength, but the dielectric constant is very small, and the scope of use is severely limited.
The third category is the composite dielectric of ceramics and polymers or glass. This type of material has a breakdown field strength far exceeding that of general applications. It is mainly aimed at pulse power systems, and its mass production technology is not yet mature.
The fourth category is antiferroelectric materials, and the research mainly focuses on lead zirconate titanate (Pb(Zr,Ti)O 3 ) system and silver niobate (AgNbO 3 ) system energy storage research, under the action of an external electric field, this kind of material will undergo a rapid transition from antiferroelectric phase to ferroelectric phase, and the dielectric constant shows a strong nonlinear effect, resulting in its polarization strength far exceeding the same strength Linear or near-linear media under the action of an electric field, so their energy storage density far exceeds the first three types of dielectric materials, and become a research hotspot at this stage. Despite the above advantages, such materials generally have large energy dissipation for energy storage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of lead-free relaxation antiferroelectric ceramic energy storage material and preparation method thereof
  • A kind of lead-free relaxation antiferroelectric ceramic energy storage material and preparation method thereof
  • A kind of lead-free relaxation antiferroelectric ceramic energy storage material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The preparation method of the lead-free relaxor antiferroelectric ceramic energy storage material according to the present invention comprises the following steps:

[0028] 1) Based on La with a purity of 99.99% 2 O 3 Carry out batching, and then use anhydrous ethanol as a medium for ball milling for 12 hours to reduce the particle size of rare earth elements, and then dry at 200 ° C to obtain La 2 O 3 powder;

[0029] 2) Bi with a purity of 99.99% 2 O 3 , 99.99% Na 2 CO 3 and 99.99% TiO 2 As raw materials, weigh 116.52 grams, 26.63 grams and 80.06 grams respectively, and then put them into a ball-milling jar for ball-milling and mixing. During the ball-milling process, the volume of the raw material: the volume of the agate ball: the volume of the ball-milled meson anhydrous ethanol is equal to 1:2:4, The ball milling time was 12h, and then the ball-milled raw materials were put into an oven and dried at 80°C for 10h. After drying, the raw material was pressed...

Embodiment 2

[0035] The preparation method of the lead-free relaxor antiferroelectric ceramic energy storage material according to the present invention comprises the following steps:

[0036] 1) Based on Sm with a purity of 99.99% 2 O 3 Carry out batching, and then use anhydrous ethanol as a medium for ball milling for 12 hours to reduce the particle size of rare earth elements, and then dry at 200 ° C to obtain Sm 2 O 3 powder;

[0037] 2) Bi with a purity of 99.99% 2 O 3 , 99.99% Na 2 CO 3 and 99.99% TiO 2 As raw materials, weigh 116.52 grams, 26.63 grams and 80.06 grams respectively, and then put them into a ball-milling jar for ball-milling and mixing. During the ball-milling process, the volume of the raw material: the volume of the agate ball: the volume of the ball-milled meson anhydrous ethanol is equal to 1:2:4, The ball milling time was 12h, and then the ball-milled raw materials were put into an oven and dried at 80°C for 10h. After drying, the raw material was pressed...

Embodiment 3

[0042] The preparation method of the lead-free relaxor antiferroelectric ceramic energy storage material according to the present invention comprises the following steps:

[0043] 1) Based on Dy with a purity of 99.99% 2 O 3 Carry out batching, and then use anhydrous ethanol as a medium for ball milling for 12 hours to reduce the particle size of rare earth elements, and then dry at 200 ° C to obtain Dy 2 O 3 powder;

[0044] 2) Bi with a purity of 99.99% 2 O 3 , 99.99% Na 2 CO 3 and 99.99% TiO 2 As raw materials, weigh 116.52 grams, 26.63 grams and 80.06 grams respectively, and then put them into a ball-milling jar for ball-milling and mixing. During the ball-milling process, the volume of the raw material: the volume of the agate ball: the volume of the ball-milled meson anhydrous ethanol is equal to 1:2:4, The ball milling time was 12h, and then the ball-milled raw materials were put into an oven and dried at 80°C for 10h. After drying, the raw material was pressed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a lead-free relaxation antiferroelectric ceramic energy storage material, and a preparation method thereof. The chemical formula is (1-x-y)(Na<0.5>Bi<0.5>)TiO<3-x>(Sr<0.7>Bi<0.2>)TiO<3-y>Me<2>O<3>, wherein Me is used for representing one or two elements selected from La, Sm, and Dy, x and y are used for representing molar fractions, 0.2<=x<=0.7, and 0.01<=y<=0.2. The lead-free relaxation antiferroelectric ceramic energy storage material is relatively in energy storage density, energy storage efficiency, and possesses relaxation characteristics, and the preparation method is simple.

Description

technical field [0001] The invention belongs to the technical field of energy storage ceramic materials, and relates to a lead-free relaxation antiferroelectric ceramic energy storage material and a preparation method thereof. Background technique [0002] Dielectric energy storage materials with high energy storage density and high reliability play an increasingly important role in various power and electronic systems, especially in the field of high-energy pulsed power technology. Related devices and products are developing in the direction of miniaturization, light weight and multi-function, which puts forward higher requirements for the energy storage density of devices. Dielectric material with good stability. [0003] At present, the existing dielectric energy storage materials can be roughly divided into four categories. The first category is barium titanate-based materials. The production technology of related capacitors is very mature and has been widely used. This...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/475C04B35/622
CPCC04B35/475C04B35/622C04B2235/3201C04B2235/3213C04B2235/3224C04B2235/3227
Inventor 李景雷李飞杨帅刘金凤徐卓张树君
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap