PVA-series melt special for optical film and preparation method thereof

A technology of optical film and melt, applied in optics, optical components, applications, etc., can solve problems such as insufficient surface finish of optical film, polycrystalline points of optical film, color spots, affecting the optical performance of the film, etc., to achieve the goal of reducing color spots Produce, smooth surface, facilitate the effect of dissolution and modification

Active Publication Date: 2019-01-11
CHINA PETROLEUM & CHEM CORP +2
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the optical films prepared by conventional preparation methods and conventional production lines tend to have the following technical problems: 1. There are many crystal points and color spots on the prepared optical films, which affect the optical properties of the film
2. When the optical film is used to prepare a polarizer and the optical film is stretched, the film is easy to break and the stretching performance is not good; and when the film is dyed, the dyeing is uneven
3. When producing wide-format optical films, the thickness of the two sides and the middle of the optical film is prone to inconsistency, which may cause the surface undulation height of the local area of ​​the optical film to be too large, resulting in insufficient surface finish of the optical film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PVA-series melt special for optical film and preparation method thereof
  • PVA-series melt special for optical film and preparation method thereof
  • PVA-series melt special for optical film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] This embodiment discloses a PVA-based melt with good fluidity. The PVA-based melt includes polyvinyl alcohol-based polymers, water, starch, n-butyraldehyde, plasticizers, surfactants and antioxidants. The PVA-based melts The melt has a melt flow index of 28 g / min at a temperature of 106° C., a load of 2.24 kg, and a water content of 40-80%. After several researches by the applicant, it was found that the optical film prepared from the PVA-based melt has a smooth surface, fewer crystal points, and excellent optical properties; The probability of film breakage during the process is very small; and when dyeing, the dye can be evenly distributed on the optical film to ensure the uniformity of film dyeing.

[0042] The flow index of the PVA-based melt is tested on a melt flow rate meter according to the test method of GB3682-2000.

[0043] A special PVA-based melt for optical films. The preparation steps of the PVA-based melt are completed under the protection of an inert g...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of manufacture of a film or a sheet and particularly discloses PVA-series melt special for an optical film and a preparation method thereof. The PVA-seriesmelt comprises a polyvinyl alcohol-based polymer, water, starch, n-butyraldehyde, a plasticizer, a surfactant and an antioxidant. The PVA-series melt has a melt flow index of 10 to 50 g / min under conditions of a temperature of 90-120 DEG C, load of 2.24kg and water content of 40-80%. An optical film prepared from the PVA-series melt has the advantages of few crystal spots of a crystal film, excellent optical properties, good stretchability, good ductility and uniform dyeing effects.

Description

technical field [0001] The invention belongs to the technical field of film or sheet manufacture, and in particular relates to a special PVA melt for optical films and a method for preparing the film. Background technique [0002] Liquid crystal display (LCD) has gradually replaced the traditional cathode ray tube (CRT) with its advantages of thinness, low power consumption, no radiation, stable image, and easy large-area display, and has become the mainstream product of terminal display in the information age. Optical film is an important raw material for making polarizers, the core component of liquid crystal displays (LCDs), and is one of the downstream high-end applications of PVA. Polarizer is a key component of LCD panel, its main function is to convert natural light into polarized light. With the development of LCD applications from small instruments such as calculators, testing instruments, various polarization microscopes, sunglasses, anti-glare goggles, and anti-g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L29/04C08L3/02C08L71/02C08J3/21C08J5/18G02B1/04B29D7/01
CPCB29D7/01C08J3/215C08J5/18C08J2329/04C08J2403/02C08J2471/02G02B1/04
Inventor 吕惠霞陆春因胡腊梅李永江
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products