Preparation method of polyoxyethylene water-soluble film

A technology of polyethylene oxide and water-soluble film, which is applied in the field of water-soluble film preparation and can solve problems such as the mechanical strength of easily oxidized films

Inactive Publication Date: 2019-03-08
SHANGHAI RES INST OF CHEM IND +2
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a method for preparing a polyoxyethylene water-soluble film in order to overcome the problems of easy oxidation and low mechanical strength of the film when the single PEO resin is processed in the above-mentioned prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of polyoxyethylene water-soluble film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] In the formula, the amount of PEO (200,000 viscosity-average molecular weight, mixed with 600,000) is 100%, the amount of ethylene glycol is 30%, the content of water-soluble starch is 15%, and the content of liquid paraffin is 0.4%. After mixing according to the above formula, first carry out extrusion granulation, the granulation temperature from machine head to film mouth is: 110°C, 130°C, 130°C, 135°C. The blowing temperature from the machine head to the film mouth is: 115°C, 130°C, 130°C, 135°C. The properties of the obtained film are shown in the table.

Embodiment 2

[0025] The formula is 100% of PEO (viscosity-average molecular weight 400,000, mixed with 800,000), ethylene glycol 35%, water-soluble starch 10%, and liquid paraffin 0.3%. After mixing according to the above formula, first carry out extrusion granulation. The granulation temperature from the machine head to the film mouth is: 105°C, 125°C, 125°C, 130°C. The blowing temperature from the machine head to the film mouth is: 110°C, 125°C, 125°C, 130°C. The properties of the obtained film are shown in the table.

Embodiment 3

[0027] The formula is that the amount of PEO (100,000 viscosity-average molecular weight, 600,000 mixed) is 100%, the amount of ethylene glycol is 20%, the content of cross-linked polyvinylpyrrolidone is 5%, and the content of liquid paraffin is 0.5%. After mixing according to the above formula, first carry out extrusion granulation, the granulation temperature from machine head to film mouth is: 100°C, 115°C, 115°C, 120°C. The blowing temperature from the machine head to the film mouth is: 105°C, 115°C, 115°C, 120°C. The properties of the obtained film are shown in the table.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a polyoxyethylene water-soluble film. According to the method, polyoxyethylene serves as a raw material, additives are added, and the polyoxyethylene water-soluble film is prepared by an extruding and blow molding method. Compared with the prior art, the thickness of the prepared PEO film is 20-50 micrometers, the tensile strength of the film is higher than or equal to 10Mpa, the breaking elongation of the film is higher than or equal to 500%, and the dissolve time of the film is 20-150 seconds at the water temperature of 30 DEG C.

Description

technical field [0001] The invention relates to the field of preparation of water-soluble films, in particular to a preparation method of polyoxyethylene water-soluble films. Background technique [0002] Water-soluble film is a film material with both water solubility and degradability, because it can quickly dissolve in water to release the packaged object, without affecting the use effect of the packaged object, and can be destroyed by microorganisms, light, etc. Or oxygen and other degradation, will not cause environmental pollution, is an excellent environmental protection material. [0003] At present, water-soluble films have been approved by the environmental departments of Europe, America, Japan and other countries, and are widely used in product packaging in agriculture, chemical industry, daily chemical industry, medical treatment and other fields. Typical uses include quantitative packaging for chemical products such as pesticides, fertilizers, pigments, dyes, f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L71/02C08L3/02C08L91/06C08L39/06C08L29/04C08L1/04C08K5/053C08K5/06C08J5/18
CPCC08J5/18C08J2371/02C08J2403/02C08J2401/04C08J2429/04C08J2439/06C08J2471/02C08K5/053C08K5/06C08J2491/06
Inventor 柴延军孔猛李从严刘婷婷徐玄之罗勇储根初陆平晔
Owner SHANGHAI RES INST OF CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap