A cable filling strip with anti-electromagnetic interference function and excellent thermal conductivity and its preparation method

An anti-electromagnetic interference and cable filling technology, applied in the field of polymer materials, can solve the problems of poor thermal conductivity and heat dissipation performance of the filler strip, failure to provide anti-electromagnetic interference, complex production process, etc. The effect of large-scale production and simple production process

Active Publication Date: 2021-06-04
苏州铂韬新材料科技有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 1) For the crosstalk of signals between wires, it fails to provide effective anti-electromagnetic interference capabilities;
[0006] 2) The thermal conductivity and heat dissipation performance of the filling strip made of traditional filling materials is not good;
[0007] 3) The production process is more complex and cumbersome

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A cable filling strip with anti-electromagnetic interference function and excellent thermal conductivity and its preparation method
  • A cable filling strip with anti-electromagnetic interference function and excellent thermal conductivity and its preparation method
  • A cable filling strip with anti-electromagnetic interference function and excellent thermal conductivity and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A cable filling strip with anti-electromagnetic interference function and excellent thermal conductivity, the cable filling strip includes the following components in terms of weight components: 20 parts of SBS thermoplastic elastomer, 20 parts of hydrogenated petroleum resin, and 20 parts of graphite powder , 10 parts of ferrite filter material, 10 parts of tributyl phosphate flame retardant, 10 parts of additives.

[0035] The preparation method of the above-mentioned cable filler strip with anti-electromagnetic interference function and excellent thermal conductivity comprises the following steps:

[0036] 1) Add thermoplastic elastomers, hydrogenated petroleum resins, flame retardants, and additives into the kneader, control the temperature in the kettle to 100°C, rotate at a speed of 40r / min, and knead at a low speed to obtain a flame-retardant mixed colloid A;

[0037] 2) Add graphite powder evenly into the kneader, adjust the speed to 100r / min, carry out high-spe...

Embodiment 2

[0041] A cable filling strip with anti-electromagnetic interference function and excellent thermal conductivity, the cable filling strip includes the following components in terms of weight components: 100 parts of TPB thermoplastic elastomer, 100 parts of DCPD, 80 parts of graphite powder, carbon nano 50 parts of tube filter material, 50 parts of hydroxyaluminum flame retardant, and 50 parts of auxiliary agent.

[0042] The preparation method of the above-mentioned cable filler strip with anti-electromagnetic interference function and excellent thermal conductivity comprises the following steps:

[0043] 1) Add thermoplastic elastomer, DCPD, flame retardant, and additives into the kneader, control the temperature in the kettle to 200°C, rotate at 40r / min, and knead at a low speed to obtain flame-retardant mixed colloid A;

[0044] 2) Add graphite powder evenly into the kneader, adjust the rotating speed to 200r / min, carry out high-speed dispersion mixing, and mix and stir for...

Embodiment 3

[0048] A cable filling strip with anti-electromagnetic interference function and excellent thermal conductivity, said cable filling strip includes the following components in terms of weight components: 60 parts of TPEE thermoplastic elastomer, 80 parts of C5 hydrogenated petroleum resin, 50 parts of graphite powder 15 parts of FeCuSiBCV metal powder filter material, 30 parts of melamine cyanuric acid flame retardant, and 25 parts of additives.

[0049] The preparation method of the above-mentioned cable filler strip with anti-electromagnetic interference function and excellent thermal conductivity comprises the following steps:

[0050] 1) Add thermoplastic elastomers, petroleum resins, flame retardants, and additives into the kneader, control the temperature in the kettle to 150°C, rotate at a speed of 60r / min, and knead at a low speed to obtain a flame-retardant mixed colloid A;

[0051] 2) Add graphite powder evenly into the kneader, adjust the rotating speed to 180r / min, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

A cable filling strip with anti-electromagnetic interference function and excellent thermal conductivity, the cable filling strip includes the following components in terms of weight components: thermoplastic elastomer, petroleum resin, graphite powder, filter material, flame retardant, auxiliary agent. The cable filling strip with anti-electromagnetic interference function and excellent thermal conductivity described in the present invention can absorb most of the electromagnetic waves projected on its surface by using electromagnetic wave absorbing materials, and convert electromagnetic energy into Heat energy or other forms of energy are consumed, and the reflection, scattering and transmission are very small. While meeting the requirements of traditional cable filler strips for flame retardancy, thermal conductivity and physical and mechanical properties, it can have excellent anti-electromagnetic interference performance. , to avoid the problem of signal crosstalk between the wires caused by the large partial capacitance and mutual inductance between the core wires.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and relates to a cable filling strip with anti-electromagnetic interference function and excellent thermal conductivity and a preparation method thereof. Background technique [0002] In electronic equipment and systems, various cables are an indispensable link for signal transmission, and at the same time, cables are the main factor causing various electromagnetic compatibility (EMC) problems. The parallel transmission distance of the wires in the cable is relatively long, so there is a large partial capacitance and mutual inductance between the core wires, which will cause signal crosstalk between the wires and cause unnecessary electromagnetic pollution to the surrounding environment . In the production process of the cable, in order to ensure the roundness of the cable and avoid the mutual friction between the core wires, it is usually necessary to add a cable filler strip between ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L53/02C08L57/02C08L77/00C08K3/04C08K3/22C08K5/521
CPCC08L53/02C08L57/02C08L2203/20C08K3/04C08K3/22C08K5/521C08L77/00
Inventor 袁兴平王建斌姜桂君李建波刘慧远
Owner 苏州铂韬新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap