Plant-derived nylon master batch and preparation method thereof

A plant-sourced nylon technology, which is applied in the field of plant-sourced nylon masterbatch and its preparation, can solve the problems of affecting moisture absorption performance, easy broken filaments, and easy roll winding, so as to achieve fiber moisture absorption performance without weakening, stable production process, and traction. good stretch effect

Inactive Publication Date: 2019-04-12
ZHONGKE TEXTILE RES INST QINGDAO CO LTD
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] (1) The uniformity of plant source nylon masterbatch is poor, easy to connect grains, and poor hygroscopicity;
[0009] (2) Fibers prepared from plant-derived masterbatches have poor spinnability, affect drawability, are easy to wrap around rolls, e

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Plant-derived nylon master batch and preparation method thereof
  • Plant-derived nylon master batch and preparation method thereof
  • Plant-derived nylon master batch and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] Embodiment 1 A kind of preparation method of grass coral plant source nylon masterbatch

[0057] Step 1, the preparation of modified grass coral extract

[0058] (1) Selection of raw materials

[0059] The extract of Coral praecox was selected as the plant source raw material of this embodiment, and 100% of the extract of Coral praecox passed through a 10,000 mesh sieve, the appearance of powder was loose, no agglomeration, the color was brownish yellow, and uniform; the content of active ingredients ≥ 98%, the content of isopyridine is 0.72%, the moisture content is ≤5%, the total number of colonies is less than 99cfu / g, Salmonella and Escherichia coli cannot be detected, and the shelf life is 18 months.

[0060] (2) Preparation of modified grass coral extract

[0061] Mix 65 parts of Grass coral extract with 25 parts of chitin and 7 parts of starch, adjust the pH to 8 with sodium carbonate, add 70 parts of deionized water and heat to 65°C and mix for 30 minutes, the...

Embodiment 2

[0087] Embodiment 2 A kind of preparation method of grass coral plant source nylon masterbatch

[0088] Step 1, the preparation of modified grass coral extract

[0089] (1) Selection of raw materials

[0090] The extract of Coral praecox was selected as the plant source raw material of this embodiment, and 100% of the extract of Coral praecox passed through a 10,000 mesh sieve, the appearance of powder was loose, no agglomeration, the color was brownish yellow, and uniform; the content of active ingredients ≥ 98%, the content of isopyridine is 0.72%, the moisture content is ≤5%, the total number of colonies is less than 99cfu / g, Salmonella and Escherichia coli cannot be detected, and the shelf life is 18 months.

[0091] (2) Preparation of modified grass coral extract

[0092] Add 21 parts of chitin and 6.5 parts of starch to 65 parts of Grass coral extract, mix, adjust the pH to 7.6 with sodium carbonate, add 64 parts of deionized water, heat to 63°C and mix for 30 minutes,...

Embodiment 3

[0118] Embodiment 3 A kind of preparation method of grass coral plant source nylon masterbatch

[0119] Step 1, the preparation of modified grass coral extract

[0120] (1) Selection of raw materials

[0121] The extract of Coral praecox was selected as the plant source raw material of this embodiment, and 100% of the extract of Coral praecox passed through a 10,000 mesh sieve, the appearance of powder was loose, no agglomeration, the color was brownish yellow, and uniform; the content of active ingredients ≥ 98%, the content of isopyridine is 0.72%, the moisture content is ≤5%, the total number of colonies is less than 99cfu / g, Salmonella and Escherichia coli cannot be detected, and the shelf life is 18 months.

[0122] (2) Preparation of modified grass coral extract

[0123] Add 15 parts of chitin and 4 parts of starch to 65 parts of Grass coral extract, mix, adjust the pH to 7 with sodium carbonate, add 50 parts of deionized water and heat to 50°C and mix for 30 minutes, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Breaking strengthaaaaaaaaaa
Densityaaaaaaaaaa
Apparent viscosityaaaaaaaaaa
Login to view more

Abstract

The invention provides a plant-derived nylon master batch. The plant-derived nylon master batch is mainly prepared by blending and melting nylon master batch and modified sarcandra glabra extract; themass ratio of the nylon master batch to the modified sarcandra glabra extract is 84:16. The invention further provides a preparation method of the cellulose fiber. The plant-derived nylon master batch prepared by the preparation method is regular in shape and free of continuous particles, no debris is generated, the particle size uniformity is 95.9-97.2%, and the water content is 0.081-0.089%; for the prepared fiber, the fiber breaking strength is 7.4-8.1 cN/dtex, the elongation at break is 36.2-37.4%, the fiber moisture absorption rate is 11.8-12.2%, and the moisture absorption performance is durable after multiple times of washing.

Description

technical field [0001] The invention relates to a plant source nylon masterbatch and a preparation method thereof, belonging to the field of fiber masterbatch preparation. Background technique [0002] Nylon masterbatch refers to the basic pellets for making nylon fiber, which is an important variety of synthetic fibers. Polyamide is commonly known as nylon (Nylon), and its English name is Polyamide (referred to as PA). It is a general term for thermoplastic resins containing repeated amide groups—[NHCO]—on the main chain of the molecule. It has many varieties and large output. It is a material with a wide range of applications. . However, due to the poor hygroscopicity of the polyamides used to make nylon, its application in the field of moisture-absorbing and moisture-permeable materials such as sportswear is limited. [0003] Plants in nature, such as wormwood, Folium Folium, mint, grass coral, etc., are widely welcomed by technical enthusiasts in the fiber field due to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29B9/12B29B9/06
CPCB29B9/12B29B9/06
Inventor 刘洁刘宇黄效龙黄效谦
Owner ZHONGKE TEXTILE RES INST QINGDAO CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap