Thermal insulation daily-use ceramic product and preparation method thereof

A ceramic product and daily-use technology, which is applied in the field of heat-insulating daily-use ceramic products and its preparation, can solve problems such as low hardness and poor heat insulation performance, and achieve improved heat insulation performance, strong heat insulation performance, and excellent heat insulation performance. The effect of thermal performance

Inactive Publication Date: 2019-04-16
福建省德化县鹏欣陶瓷有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a heat-insulating daily-use ceramic product and its preparation method, which solves the problems of poor heat-insulation performance and low hardness of the current ceramic products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermal insulation daily-use ceramic product and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Embodiment 1: A heat-insulating daily-use ceramic product, which contains the following raw materials in parts by weight: 35 parts of kaolin, 20 parts of shells, 15 parts of vermiculite, 10 parts of hollow micropowder, 10 parts of zirconia, and 12 parts of water-based acrylic emulsion 8 parts of mangosteen shell, 8 parts of glass fiber, 3 parts of ethyl orthosilicate, 4 parts of vanadium pentoxide, 15 parts of epoxy resin, 2 parts of polyester resin, 1.5 parts of dispersant and 2 parts of silane coupling agent .

[0016] A method for preparing heat-insulating daily-use ceramic products, comprising the steps of:

[0017] 1) Pulverize kaolin, shells, vermiculite, hollow micropowder, and mangosteen shells, and pass through a 90-mesh sieve to obtain material 1;

[0018] 2) Mix the material 1 obtained in step 1) with zirconia, glass fiber, vanadium pentoxide, aqueous acrylic emulsion, tetraethyl orthosilicate, epoxy resin, polyester resin, add it to a ball mill and grind it...

Embodiment 2

[0021] Embodiment 2: A heat-insulating daily-use ceramic product, which contains the following raw materials in parts by weight: 30 parts of kaolin, 15 parts of shells, 10 parts of vermiculite, 5 parts of hollow micropowder, 5 parts of zirconia, and 10 parts of water-based acrylic emulsion 6 parts of mangosteen shell, 5 parts of glass fiber, 2 parts of ethyl orthosilicate, 3 parts of vanadium pentoxide, 10 parts of epoxy resin, 1 part of polyester resin, 1 part of dispersant and 1 part of silane coupling agent .

[0022] A method for preparing heat-insulating daily-use ceramic products, comprising the steps of:

[0023] 1) Pulverize kaolin, shells, vermiculite, hollow micropowder, and mangosteen shells, and pass through an 80-mesh sieve to obtain material 1;

[0024] 2) Mix the material 1 obtained in step 1) with zirconia, glass fiber, vanadium pentoxide, water-based acrylic emulsion, tetraethyl orthosilicate, epoxy resin, and polyester resin, add it to a ball mill and grind ...

Embodiment 3

[0027] Embodiment 3: A heat-insulating daily-use ceramic product, which contains the following raw materials in parts by weight: 40 parts of kaolin, 25 parts of shells, 20 parts of vermiculite, 15 parts of hollow micropowder, 14 parts of zirconia, and 15 parts of water-based acrylic emulsion 10 parts of mangosteen shell, 10 parts of glass fiber, 4 parts of ethyl orthosilicate, 5 parts of vanadium pentoxide, 20 parts of epoxy resin, 4 parts of polyester resin, 2 parts of dispersant and 3 parts of silane coupling agent .

[0028] A method for preparing heat-insulating daily-use ceramic products, comprising the steps of:

[0029] 1) Pulverize kaolin, shells, vermiculite, hollow micropowder, and mangosteen shells, and pass through a 100-mesh sieve to obtain material 1;

[0030] 2) Mix the material 1 obtained in step 1) with zirconia, glass fiber, vanadium pentoxide, water-based acrylic emulsion, tetraethyl orthosilicate, epoxy resin, polyester resin, add it to a ball mill and gri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a thermal insulation daily-use ceramic product and a preparation method thereof. The ceramic product comprises, by weight, the following raw materials: 30-40 parts of kaolin, 15-25 parts of a shell, 10-20 parts of vermiculite, 5-15 parts of a hollow micro powder, 5-14 parts of zirconia, 10-15 parts of an aqueous acrylic emulsion and 6-10 parts of a mangosteen shell, 5-10 parts of a glass fiber, 2-4 parts of ethyl orthosilicate, 3-5 parts of vanadium pentoxide, 10-20 parts of an epoxy resin, 1-4 parts of a polyester resin, 1-2 parts of a dispersing agent and 1-3 parts ofa silane coupling agent. The thermal insulation daily-use ceramic product is simple in production technology, free of pollution in the production technology and low in raw material cost, and by meansof a scientific raw material formula, the heat conductivity coefficient of the prepared ceramic product is low and the thermal insulation daily-use ceramic product has an excellent thermal insulationperformance and is healthy, environmentally friendly and durable.

Description

technical field [0001] The invention belongs to the technical field of daily-use ceramics, and in particular relates to a heat-insulating daily-use ceramic product and a preparation method thereof. Background technique [0002] Ceramics are various products made of natural clay and various natural minerals as the main raw materials through crushing, kneading, molding and calcination. Ceramic products are widely used in our life and production because of their strength similar to metal, rich decorative effects, good wear resistance, chemical stability and corrosion resistance. [0003] China is one of the first countries in the world to use ceramics. Due to the advancement of science and technology, ceramics have appeared many materials that can replace porcelain vessels, such as stainless steel and plastic. Compared with traditional ceramic products, there are many defects, such as low hardness, poor wear resistance, poor heat insulation performance, and low ductility. In ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/80C04B33/04C04B33/36C04B33/13C04B33/132
CPCC04B35/803C04B33/04C04B33/1305C04B33/131C04B33/132C04B33/36C04B2235/3239C04B2235/3244C04B2235/3463C04B2235/5216Y02P40/60
Inventor 李文韧方丽珍
Owner 福建省德化县鹏欣陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com