Mei Youji waterproof mascara and preparing method thereof

A mascara and quality technology, which is applied to the field of Meiyuji waterproof mascara and its preparation, can solve the problems of mascara being prone to dizziness, poor waterproof performance, sticky feeling and the like, and achieves good anti-ultraviolet radiation performance and anti-static properties. Good performance, easy absorption effect

Inactive Publication Date: 2019-05-14
普宁市嘉宝日用化工有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Different mascaras focus on different effects, but most of the existing mascaras are easy to smudge, thicker and sticky, easy to take off when exposed to water, sweat, rain, etc., and have poor waterproof performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A kind of Miyuki waterproof mascara, which is prepared from the following components in mass ratio:

[0047] Isododecane: 46.4%

[0048] Polydisiloxane: 4%;

[0049] Trimethylsiloxysilicate: 5%;

[0050] CI 77499: 8%;

[0051] Carnauba (COPERNICIA CERIFERA) wax: 5%;

[0052] Distearyl dimethyl ammonium hectorite: 4%;

[0053] Candelilla (EUPHORBIA CERIFERA) wax: 5%;

[0054] Dextrin Palmitate / Ethylhexanoate: 1%;

[0055] Propylene carbonate: 5%;

[0056] Nylon-6: 2%;

[0057] Silica: 1%;

[0058] Magnesium stearate: 1%;

[0059] Glyceryl isostearate: 4%;

[0060] Camellia (CAMELLIA JAPONICA) seed oil: 4%;

[0061] Caprylic / capric triglycerides: 4%;

[0062] p-Hydroxyacetophenone: 0.6%;

[0063] The CI 77499 is ferric oxide.

[0064] Two of the tasks of the present invention are achieved through the following technical solutions:

[0065] A preparation method of the above-mentioned Meyuji waterproof mascara, comprising the following steps:

[0066] A. Weigh...

Embodiment 2

[0070] Example 1:

[0071] A kind of Miyuki waterproof mascara, which is prepared from the following components in mass ratio:

[0072] Isododecane: 31%

[0073] Polydisiloxane: 5%;

[0074] Trimethylsiloxysilicate: 6%;

[0075] CI 77499: 10%;

[0076] Carnauba (COPERNICIA CERIFERA) wax: 6%;

[0077] Distearyldimethylammonium hectorite: 5%;

[0078] Candelilla (EUPHORBIA CERIFERA) wax: 6%;

[0079] Dextrin Palmitate / Ethylhexanoate: 2%;

[0080] Propylene carbonate: 6%;

[0081] Nylon-6: 3%;

[0082] Silica: 2%;

[0083] Magnesium stearate: 2%;

[0084] Glyceryl isostearate: 5%;

[0085] Camellia (CAMELLIA JAPONICA) seed oil: 5%;

[0086] Caprylic / capric triglycerides: 5%;

[0087] p-Hydroxyacetophenone: 1%;

[0088] The CI 77499 is ferric oxide.

[0089] Two of the tasks of the present invention are achieved through the following technical solutions:

[0090] A preparation method of the above-mentioned Meyuji waterproof mascara, comprising the following steps: ...

Embodiment 3

[0095] A kind of Miyuki waterproof mascara, which is prepared from the following components in mass ratio:

[0096] Isododecane: 38.7%

[0097] Polydisiloxane: 4.5%;

[0098] Trimethylsiloxysilicate: 5.5%;

[0099] CI 77499: 9%;

[0100] Carnauba (COPERNICIA CERIFERA) wax: 5.5%;

[0101] Distearyldimethylammonium hectorite: 4.5%;

[0102] Candelilla (EUPHORBIA CERIFERA) wax: 5.5%;

[0103] Dextrin Palmitate / Ethylhexanoate: 1.5%;

[0104] Propylene carbonate: 5.5%;

[0105] Nylon-6: 2.5%;

[0106] Silica: 1.5%;

[0107] Magnesium stearate: 1.5%;

[0108] Glyceryl isostearate: 4.5%;

[0109] Camellia (CAMELLIA JAPONICA) seed oil: 4.5%;

[0110] Caprylic / capric triglycerides: 4.5%;

[0111] p-Hydroxyacetophenone: 0.8%;

[0112] The CI 77499 is ferric oxide.

[0113] Two of the tasks of the present invention are achieved through the following technical solutions:

[0114] A preparation method of the above-mentioned Meyuji waterproof mascara, comprising the following...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Melting pointaaaaaaaaaa
Boiling pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of cosmetics, in particular to Mei Youji waterproof mascara and a preparing method thereof. The Mei Youji waterproof mascara is prepared from, by mass, 31-46.4% of isododecane, 4-5% of polydisiloxane, 5-6% of trimethylsiloxysilicate, 8-10% of CI 77499, 5-6% of copernicia cerifera (COPERNICIA CERIFERA) wax, 4-5% of disteardimonium hectorite, 5-6% of euphorbia cerifera (EUPHORBIA CERIFERA) wax, 1-2% of dextrin palmitate / ethylhexoate and the like. The Mei Youji waterproof mascara can effectively realize the professional waterproof performance for swimming water, rain, sweat, tears, oily skin and the like and can only be removed with a mascara cleansing lotion in the invention.

Description

technical field [0001] The invention relates to the technical field of cosmetics, in particular to a meyuki waterproof mascara and a preparation method thereof. Background technique [0002] A pair of charming and bright eyes, together with thick and curly long eyelashes, will make your beauty more perfect. But not all people are born with eyelashes like a small fan, so mascara was born. Applying mascara can make up for the lack of sparse and short eyelashes, making the eyelashes appear thicker, longer and curled, making the eyes more attractive. Mascara on the market is roughly divided into five types: precision mascara, waterproof mascara, thickening mascara, lengthening mascara, and repairing mascara. You can choose according to your own situation. Precise mascara makes the eyelashes clear, waterproof mascara is not easy to take off makeup, thick eyelashes contain thickening factors to make eyes deep and smooth, fibers in lengthening mascara make eyelashes flicker like ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61K8/92A61K8/19A61K8/25A61K8/35A61K8/37A61K8/49A61K8/58A61K8/73A61K8/88A61K8/891A61Q1/10
Inventor 周伟茂韩磊
Owner 普宁市嘉宝日用化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap