A high-elongation low-temperature rapid degradation magnesium alloy and its preparation method

A high-elongation, rapid-degradation technology, applied in the field of magnesium alloy materials, can solve problems such as not being able to meet the requirements of the production area, and achieve the effects of refining alloy grains, increasing strength, and increasing degradation speed

Active Publication Date: 2021-06-25
CHONGQING UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Taking an oil and gas production area in my country as an example, due to the shallow drilling depth and the influence of natural factors, the downhole temperature is less than 40°C. However, the working temperature of magnesium alloy fracturing ball products on the market is mostly above 90°C, and the higher the working temperature , the degradation rate of magnesium alloy fracturing balls is correspondingly faster, so the current commercial magnesium alloy fracturing ball materials cannot meet the requirements of this production area

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-elongation low-temperature rapid degradation magnesium alloy and its preparation method
  • A high-elongation low-temperature rapid degradation magnesium alloy and its preparation method
  • A high-elongation low-temperature rapid degradation magnesium alloy and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A magnesium alloy with high elongation and rapid degradation at low temperature, the magnesium alloy contains the following components in terms of mass percentage: Gd6.0%, Ni0.18%, Zr0.5%, unavoidable impurities≤0.3%, and the balance is Mg. The magnesium alloy is prepared as follows:

[0027] (1) Melt the magnesium ingot at 710°C, add Mg-Zr master alloy, Mg-Gd master alloy, and Mg-Ni master alloy after melting, then keep it at 700°C for 30 minutes, and then pass it into argon for 15 minutes of refining , and then remove the slag from the alloy melt and let it stand at 700°C until the impurities settle, and finally make a semi-continuous ingot after semi-continuous casting at 680°C;

[0028] (2) Homogenization treatment: heat the semi-continuous ingot prepared in step (1) to 350° C. for 8 hours, then keep it warm for 24 hours, then air-cool it to room temperature, heat it up to 480° C. for 12 hours again, and keep it warm for 12 hours;

[0029] (3) Quenching treatment: ...

Embodiment 2

[0032] A magnesium alloy with high elongation and rapid degradation at low temperature. The magnesium alloy contains the following components in terms of mass percentage: Gd6.5%, Ni0.1%, Mn0.8%, unavoidable impurities≤0.3%, and the balance is Mg. The magnesium alloy is prepared as follows:

[0033] (1) Melt the magnesium ingot and the Mg-Mn master alloy together at 690°C, and then add the Mg-Gd master alloy and Mg-Ni master alloy after melting, then keep it at 680°C for 25 minutes, and then pass it into argon for refining After 5 minutes, the alloy melt was deslagged and left to stand at 690°C until the impurities settled, and finally semi-continuously cast at 675°C to obtain a semi-continuous ingot;

[0034](2) Homogenization treatment: heat the semi-continuous ingot prepared in step (1) to 330° C. for 6 hours, then keep it warm for 28 hours, then air-cool it to room temperature, heat it up to 460° C. for 8 hours again, and keep it warm for 18 hours;

[0035] (3) Quenching t...

Embodiment 3

[0038] A high-elongation low-temperature rapid degradation magnesium alloy, the magnesium alloy contains the following components by mass percentage: Gd5.0%, Ni 0.25%, Zr 0.25%, Mn 0.6%, unavoidable impurities ≤ 0.3%, the balance is Mg. The magnesium alloy is prepared as follows:

[0039] (1) Melt the magnesium ingot and the Mg-Mn master alloy together at 710°C, then add the Mg-Zr master alloy, Mg-Gd master alloy, and Mg-Ni master alloy after melting, and then keep the temperature at 720°C for 20 minutes. Then pass through the argon gas for refining for 10 minutes, then remove the slag from the alloy melt and let it stand at 710°C until the impurities settle, and finally make semi-continuous ingots after semi-continuous casting at 685°C;

[0040] (2) Homogenization treatment: heat the semi-continuous ingot prepared in step (1) to 380° C. for 12 hours, then keep it warm for 16 hours, then air-cool it to room temperature, heat it up to 470° C. for 10 hours again, and keep it wa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The invention relates to a high-elongation low-temperature rapid-degradation magnesium alloy and a preparation method thereof, belonging to the technical field of magnesium alloy materials. The alloy contains the following components by mass percentage: Gd 5.0-6.5%, Ni 0.1-0.25%, Zr 0.05-0.5% and / or Mn 0.4-1.0%, unavoidable impurities ≤ 0.3%, and the balance is Mg. Comprehensively considering the effects of various alloying elements, using the synergistic effect of alloying elements, a magnesium alloy with high plasticity and high low-temperature degradation rate is obtained, and the alloy has fewer types of elements, less addition of each element, and low price. Therefore, the cost of alloy preparation does not increase significantly, and the preparation process does not change much compared with commercial magnesium alloys, which is suitable for expanded production.

Description

technical field [0001] The invention belongs to the technical field of magnesium alloy materials, and in particular relates to a high-elongation low-temperature rapid-degradation magnesium alloy and a preparation method thereof. Background technique [0002] In oil and gas drilling technology, fracturing technology is the core technology, which directly determines the success of staged fracturing. The multi-stage sliding sleeve staged fracturing technology is a new type of oil and natural gas stimulation technology newly developed in the field of oil and gas well engineering technology in recent years. In the multi-stage sliding sleeve segmental fracturing technology, the fracturing ball plays a very important role. The fracturing ball mainly plays the following two roles in this technology: 1. 2. Cut off the fracturing fluid and pressure. After the fracturing of the rock production layer is completed, it is necessary to release the pressure of the tubing in the well to fa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C23/06C22C1/03C22F1/06
CPCC22C1/03C22C23/06C22F1/002C22F1/06
Inventor 余大亮黄家俊张丁非兰伟戴庆伟杨青山柴森森曹鹏军
Owner CHONGQING UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap