A method for forming fiber-aluminum alloy composite parts

A composite material and aluminum alloy technology, applied in the field of composite materials, can solve the problems of low elongation of fiber materials

Active Publication Date: 2021-07-06
WUHAN UNIV OF TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] This application provides a method for forming fiber-aluminum alloy composite parts, which overcomes the defect of low elongation of fiber materials in the stamping forming process, and further improves the quality of fiber-aluminum alloy composite materials through solid solution and aging treatment of aluminum alloys. strength of parts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for forming fiber-aluminum alloy composite parts
  • A method for forming fiber-aluminum alloy composite parts
  • A method for forming fiber-aluminum alloy composite parts

Examples

Experimental program
Comparison scheme
Effect test

no. 1 example

[0057] Please refer to figure 1 , with reference to figure 2 and Figure 5 , the embodiment of the present application provides a fiber-aluminum alloy composite part forming process, which can overcome the defect of low elongation of the fiber material in the stamping forming process, and can improve the strength of the fiber-aluminum alloy composite part.

[0058] The implementation steps of the process method for forming the fiber-aluminum alloy composite parts are as follows:

[0059] S1, according to the shape of the part, the aluminum alloy plate (including the first aluminum alloy plate 1 and the second aluminum alloy plate 3) and the fiber cloth 2 are cut according to the shape of the part to obtain a blank of 400 mm × 250 mm;

[0060] S2, performing solid solution treatment on the first aluminum alloy plate 1 and the second aluminum alloy plate 3 at 535° C. for 30 minutes, and immediately performing the first solid solution treatment on the first aluminum alloy plat...

no. 2 example

[0066] Please refer to Figure 6 , with reference to the first embodiment figure 1 , figure 2 , Figure 4 as well as Figure 5 The embodiment of the present application provides another method for forming fiber-aluminum alloy composite parts, which can overcome the defect of low elongation of fiber materials during stamping and forming, and can improve the strength of fiber-aluminum alloy composite parts.

[0067] The implementation steps of the process method for forming the fiber-aluminum alloy composite parts are as follows:

[0068] S1, according to the shape of the part, the aluminum alloy plate (including the first aluminum alloy plate 1 and the second aluminum alloy plate 3) and the fiber cloth 2 are cut according to the shape of the part, and the blanks of 1000mm×500mm are respectively obtained;

[0069] S2, performing solid solution treatment on the first aluminum alloy plate 1 and the second aluminum alloy plate 3 at 535° C. for 30 minutes, and immediately perfo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The application provides a method for forming a fiber-aluminum alloy composite material part, which includes the following steps: 1. Cutting the aluminum alloy plate and fiber cloth according to the shape of the part; 2. Carrying out solid solution treatment to the aluminum alloy plate, and immediately The melted aluminum alloy plate is pre-pressed, so that the surface glued with the fiber cloth is evenly distributed with grid-shaped grooves, and then the pre-pressed aluminum alloy plate is quenched; 3. The quenched aluminum alloy plate is Degreasing treatment, and prepreg the fiber cloth in epoxy resin glue; 4. Make sandwich panels in the order of aluminum alloy plate-fiber prepreg-aluminum alloy plate, and pre-preg the sandwich panel 5. Place the obtained sandwich panel in a stamping mold, close the mold, keep warm and solidify to obtain a fiber-aluminum alloy composite material part. This method overcomes the problem of low elongation in the forming process of fiber materials and improves the strength of composite parts.

Description

technical field [0001] The present application relates to the technical field of composite materials, in particular to a method for forming fiber-aluminum alloy composite parts. Background technique [0002] Due to the advantages of high specific strength, specific stiffness and good corrosion resistance, fiber-reinforced resin-based composite materials are widely used in aerospace and automobile and other transportation fields. However, the inherent defects of the resin itself, such as: easy aging, easy creep, poor flame resistance and other shortcomings, these defects limit the further application of fiber-reinforced resin-based composite materials. In order to overcome these shortcomings of the resin matrix, aluminum alloys can be combined with fiber composite materials, so that while overcoming the weakness of poor heat and humidity resistance, the characteristics of good plasticity, impact resistance and ease of processing of aluminum alloys can be brought into play. I...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B37/10B32B37/06B32B37/12B32B38/00
CPCB32B37/06B32B37/10B32B37/12B32B38/00
Inventor 华林于海洋胡志力
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com