A kind of composite heat carrier medium anticorrosion coating and preparation method thereof

A technology of composite heat carrier and anti-corrosion coating, which is applied in the direction of coating, metal material coating process, fusion spraying, etc., can solve problems such as equipment pipeline and oil field injection system corrosion, oil field economic loss, failure accidents, etc., to achieve Improve the spray atomization effect, increase the density and binding force, and improve the effect of density

Active Publication Date: 2022-01-04
BC P INC CHINA NAT PETROLEUM CORP +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, since the composite heat carrier is a mixture composed of high-temperature and high-pressure water vapor, nitrogen, carbon dioxide, and residual oxygen, etc., it is highly corrosive, and equipment pipelines and oilfield injection systems face great corrosion risks.
Therefore, failure accidents often occur, which bring huge economic losses and potential safety hazards to the oil field.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] The invention provides an anticorrosion coating suitable for composite heat carrier medium and a preparation method thereof. The coating is calculated by weight percentage, and its element composition includes: Al: 3.0-7.5%, Cr: 20.0-23.0%, Ni: 23.0-26.0%, Co: 23.0-26.0%, Re: 0.5-2.0%, Si: 0.5-1.5% and Fe: 22.0-25.0%.

[0026] The coating is prepared by a low-pressure plasma spraying method, and the coated substrate material is carbon steel or low-alloy steel; the coating is composed of a single FCC solid solution phase; there is an interdiffusion layer at the interface between the coating and the substrate, The interdiffusion layer contains Fe, Cr, Ni, Co and Al elements, and the thickness of the interdiffusion layer is 5 μm to 10 μm;

[0027] The preparation method of described coating comprises the following steps:

[0028] Step 1: Prepare coating material

[0029] (1) By weight percentage, Al: 3.0-7.5%, Cr: 20.0-23.0%, Ni: 23.0-26.0%, Co: 23.0-26.0%, Re: 0.5-2.0%...

Embodiment 1

[0037] Step 1: Prepare coating material

[0038] (1) By weight percentage, Al: 5.5%, Cr: 21.5%, Ni: 24.0%, Co: 24.0%, Re: 1.0%, Si: 1.0%, Fe: 23.0%, are mixed evenly and then ground to produce Obtain alloy powder with a particle size of 250-400 mesh;

[0039] (2) After mixing the alloy powder prepared in step (1) with a binder, grinding to obtain a mixed powder with a particle size of 250 to 400 mesh;

[0040] (3) spraying, drying and granulating the mixed powder prepared in step (2) to obtain a coating material with a particle size of 200 to 250 mesh;

[0041] The second step: substrate surface treatment

[0042] After thermally cleaning the N80 substrate at 400°C for 1 hour, the surface of the carbon steel substrate was sandblasted with a sandblasting machine. After sandblasting, the surface roughness of the substrate was R Z =40~80μm;

[0043] The third step: low-pressure plasma spraying coating

[0044] The parameters of plasma spraying are: tank pressure 8~20×10 3 p...

Embodiment 2

[0048] Step 1: Prepare coating material

[0049] (1) By weight percentage, Al: 3%, Cr: 20%, Ni: 26%, Co: 23%, Re: 2%, Si: 1.0%, Fe: 25.0%, are mixed evenly and then ground to produce Obtain alloy powder with a particle size of 250-400 mesh;

[0050] (2) After mixing the alloy powder prepared in step (1) with a binder, grinding to obtain a mixed powder with a particle size of 250 to 400 mesh;

[0051] (3) spraying, drying and granulating the mixed powder prepared in step (2) to obtain a coating material with a particle size of 200 to 250 mesh;

[0052] The second step: substrate surface treatment

[0053] After the N80 material substrate was thermally cleaned at 400°C for 1 hour, the surface of the low-alloy steel substrate was sandblasted with a sandblasting machine. After sandblasting, the surface roughness of the substrate was R Z =40~80μm;

[0054] The third step: low-pressure plasma spraying coating

[0055] The parameters of plasma spraying are: tank pressure 8~20×10 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
surface roughnessaaaaaaaaaa
Login to view more

Abstract

A composite heat transfer medium anti-corrosion coating and a preparation method thereof, including the following elements by weight percentage: Al: 3.0-7.5%, Cr: 20.0-23.0%, Ni: 23.0-26.0%, Co: 23.0-26.0% , Re: 0.5‑2.0%, Si: 0.5‑1.5% and Fe: 22.0‑25.0%. The main components of the coating are Al, Cr, Ni, Co, Fe five elements, these five elements can form Al in the present invention x The CoCrFeNi high-entropy alloy has good mechanical properties, and at the same time, these five elements all have excellent corrosion resistance and high temperature resistance; the bonding force between the coating prepared by the invention and the N80 carbon steel base material reaches more than 145 MPa.

Description

technical field [0001] The invention relates to material surface anticorrosion technology, in particular to a composite heat carrier medium anticorrosion coating and a preparation method thereof. Background technique [0002] Composite heat carrier foam flooding is a high-temperature composite heat carrier composed of water vapor, nitrogen and carbon dioxide by fully combusting diesel or gasoline with air in high-temperature and high-pressure equipment. The generated high-temperature composite heat carrier and foaming agent are organically combined, coordinated and compatible, and injected into the downhole oil layer through the foam generator to evenly displace the remaining oil in the oil layer and improve the ultimate recovery. It has multiple advantages such as chemical flooding, nitrogen flooding, carbon dioxide flooding, steam thermal flooding and foam flooding, etc. It can be used as an effective replacement technology in the late stage of oilfield tertiary oil recove...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C23C4/134C23C4/06C22C30/00
CPCC23C4/134C23C4/06C22C30/00
Inventor 蔡锐韩燕李发根徐秀清吕乃欣袁军涛
Owner BC P INC CHINA NAT PETROLEUM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap