Aqueous transfer membrane demolding agent as well as preparation method and application thereof

A transfer film and release agent technology, applied in the direction of chemical paint/ink remover, coating, etc., can solve the problems of substrate damage, high cost of transfer film, complicated operation, etc., and achieve long service life, The effect of fast and efficient film removal and good application prospects

Active Publication Date: 2019-12-03
INST OF RESOURCES UTILIZATION & RARE EARTH DEV GUANGDONG ACAD OF SCI
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the characteristics of high cost of transfer film in the prior art, relatively complicated operation during use, and easy damage to the substrate.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] This embodiment provides a water-based transfer film release agent, the preparation method of which is as follows.

[0053] Weigh 500.0g of sodium hydroxide and add it into a container containing 1000.0g of water to stir, slowly add 375.0g of ethylene glycol monomethyl ether dropwise, then add 250.0g of monoethanolamine, 200.0g of benzyl alcohol, and 50.0g of chelating agent PH- E, 125.0g C 8～10 Alcohol polyoxyethylene ether phosphate ester salt, prepared into 2500g solution, continue stirring for a period of time, until the solution forms a uniform and stable phase to obtain the release agent product.

[0054] Take 300g of the release agent and transfer it into a 500mL beaker, put the beaker into a heatable ultrasonic cleaner, set the temperature of the ultrasonic cleaner to 90-95 degrees Celsius, and after the temperature of the release agent rises to 90 degrees Celsius, put the 30 The diameter of the film is 10mm. Put the sapphire cover plate into the release agent ...

Embodiment 2

[0056] This embodiment provides a water-based transfer film release agent, the preparation method of which is as follows.

[0057] Weigh 900.0g of sodium hydroxide, add it into a container containing 450.0g of water and stir, slowly add 800.0g of ethylene glycol monomethyl ether dropwise, and then add 1000.0g of monoethanolamine, 1000.0g of benzyl alcohol, and 750.0g of PH- E, 100.0g C 8～10Alcohol polyoxyethylene ether phosphate ester salt, prepared into 5000.0g solution, continue stirring for a period of time, until the solution forms a uniform and stable phase to obtain the release agent product.

[0058] Take 300g of the release agent solution and transfer it into a 500mL beaker, put the beaker into a heatable ultrasonic cleaner, set the temperature of the ultrasonic cleaner to 90-95 degrees Celsius, and after the temperature of the release agent rises to 90 degrees Celsius, place the Put 50 pieces of sapphire covers with a diameter of 10mm into the release agent and start...

Embodiment 3

[0060] This embodiment provides a water-based transfer film release agent, the preparation method of which is as follows.

[0061] Weigh 1100.0g of sodium hydroxide and add it into a container containing 1400.0g of water, stir, slowly add 800.0g of ethylene glycol monomethyl ether dropwise, and then add 750.0g of monoethanolamine, 750.0g of benzyl alcohol, 50.0g of EDTA Sodium, 150.0g C8~10 alcohol polyoxyethylene ether phosphate ester salt, prepare 5000.0g solution, continue stirring for a period of time, until the solution is uniform and stable to obtain the release agent product.

[0062] Take 300.0g of the release agent solution and transfer it into a 500mL beaker, put the beaker into a heatable ultrasonic cleaner, set the temperature of the ultrasonic cleaner to 90-95 degrees Celsius, and wait until the temperature of the release agent rises to 90 degrees Celsius, Put 50 pieces of sapphire cover plates with a diameter of 10mm to be removed into the release agent, and star...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to an aqueous transfer membrane demolding agent as well as a preparation method and application thereof. The aqueous transfer membrane demolding agent consists of the following components in parts by mass: 10-25% of an inorganic strong base, 10-20% of an organic weak base, 8-20% of a main solvent, 5-20% of a cosolvent, 2-5% of a surfactant, 1-15% of a chelating agent and thebalance of water. The aqueous transfer membrane demolding agent provided by the invention has the properties of rapidness and high efficiency, can be repeatedly used for a long time, has no influenceupon a substrate surface, particularly the precision of a sapphire cover plate, and has good application prospects in the precise processing industry.

Description

technical field [0001] The invention belongs to the technical field of chemical paint remover, and in particular relates to a water-based transfer film remover and its preparation method and application. Background technique [0002] Fingerprint recognition is the mainstream personal identification method for modern smartphones. Sapphire glass has the advantages of high hardness and corrosion resistance, and is widely used as the fingerprint identification cover of Apple mobile phones and some domestic high-end models. However, during the thermal transfer process, sapphire glass is prone to unqualified phenomena such as bumps, pits, pinholes, and unevenness, and some products cannot enter the next step. Due to the high processing cost of sapphire glass, if the thermal transfer film on the surface of unqualified products cannot be removed and reused, it will cause a large waste of resources. [0003] At present, the conventional transfer film release agent is mainly compose...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D9/04C09D9/00
CPCC09D9/04C09D9/005
Inventor 谢武杨改霞何佳正苏冬
Owner INST OF RESOURCES UTILIZATION & RARE EARTH DEV GUANGDONG ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap