A kind of high-toughness fused corundum wear-resistant coating and preparation method thereof

A technology of fused corundum and wear-resistant coatings, which is applied in the field of coatings and can solve problems such as inability to protect, low toughness, and easy cracks

Active Publication Date: 2022-02-18
YIXING GUOQIANG FURNACE IND
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the raw materials in this application are only made by fusing high-strength raw materials together at high temperature, which has the disadvantage of low toughness, is prone to cracks, and cannot play a good protective role.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-toughness fused corundum wear-resistant coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0049] The preparation method of this wear-resistant coating comprises the steps:

[0050] Step S1, adding the fused corundum into the mixer according to its weight, and stirring at 300r / min for 2-3min;

[0051] Step S2, then add the weighed binder into the mixer, and continue to stir at 300r / min for 2-3min;

[0052] Step S3: Add additives and activated micropowder into the mixer, increase the stirring speed to 500r / min, stir for 4-5min, finally add silicon carbide, stir for 3-5min, after mixing evenly, add ethanol, stir at 600r / min for 2- 3min to obtain a wear-resistant coating.

Embodiment 1

[0054] A high-toughness fused corundum wear-resistant coating, made of the following raw materials in parts by weight: 30 parts of fused corundum, 5 parts of binder, 0.2 parts of auxiliary agent, 2 parts of activated micropowder, 1.6 parts of silicon carbide, and 7 parts of ethanol;

[0055] The wear-resistant coating is made by the following steps:

[0056] Step S1, adding the fused corundum into the mixer according to its weight, and stirring at 300r / min for 2min;

[0057] Step S2, then add the weighed binder into the mixer, and continue to stir at 300r / min for 2min;

[0058] Step S3, add the auxiliary agent and activated micropowder into the mixer, increase the stirring speed to 500r / min, stir for 4min, finally add silicon carbide, stir for 3-5min, after mixing evenly, add ethanol, stir for 2min at 600r / min, to obtain Grinding paint.

Embodiment 2

[0060] A high-toughness fused corundum wear-resistant coating, made of the following raw materials in parts by weight: 35 parts of fused corundum, 6.5 parts of binder, 0.25 parts of auxiliary agent, 2.5 parts of activated micropowder, 1.8 parts of silicon carbide, and 8.5 parts of ethanol;

[0061] The wear-resistant coating is made by the following steps:

[0062] Step S1, adding the fused corundum into the mixer according to its weight, and stirring at 300r / min for 2.5min;

[0063] Step S2, then add the weighed binder into the mixer, and continue to stir at 300r / min for 2.5min;

[0064] Step S3: Add additives and activated micropowder into the mixer, increase the stirring speed to 500r / min, stir for 4.5min, finally add silicon carbide, stir for 4min, after mixing evenly, add ethanol, stir for 2.5min at 600r / min, and obtain Grinding paint.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Rockwell hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-toughness fused corundum wear-resistant coating, which is made of the following raw materials in parts by weight: 30-40 parts of fused corundum, 5-8 parts of binder, 0.2-0.3 parts of auxiliary agent, and 2-2 parts of activated micropowder 3 parts, 1.6-2 parts of silicon carbide, and 7-10 parts of ethanol; the invention also discloses a preparation method of the wear-resistant coating. The invention uses fused corundum as the main wear-resistant matrix and modified phenolic resin as the binding agent of the wear-resistant matrix, which can not only combine and firmly attach the wear-resistant matrix to the surface of the matrix, but also form a dense friction layer on the surface of the matrix. layer; by adding active SiO to wear-resistant coatings 2 Micro-powder can reduce the friction between fused corundum particles, improve the fluidity of the coating, and can fill the pores of the wear-resistant coating to increase the density of the coating; the compounding of SiC can effectively strengthen and toughen, and obtain a A fused corundum coating with good wear resistance and high toughness is suitable for surface protection of equipment.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to a high-toughness fused corundum wear-resistant coating and a preparation method thereof. Background technique [0002] At present, many important components in the power plant, such as boiler four tubes, fan blades, pulverized coal pipe elbows, steam turbine final stage blades, etc., have greatly shortened their service life due to wear, high temperature corrosion, and water erosion, which seriously affects the unit. Safe operation directly affects the economic benefits of power production. Most of the domestic solutions to such problems are regular replacement of damaged parts, which requires a long construction period and a large investment. With the development of new materials for industrial use, special high-performance materials have become a new hotspot in material science research. Fused corundum material has extremely high temperature resistance, oxidation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/12
CPCC04B26/122C04B2111/00482C04B2201/50
Inventor 林国强
Owner YIXING GUOQIANG FURNACE IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com