Composition containing active mica and biological fermentation preparation method of composition containing active mica

A technology of biological fermentation and composition, applied in polishing compositions containing abrasives, fermentation, etc., can solve the problems of unreachable, complicated, difficult to control process, etc., and achieves lifting ability, excellent anti-rust performance, improving effect and efficacy Effect

Pending Publication Date: 2019-12-31
王希峰
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because the mechanism of biological fermentation is very complicated and the process is difficult to control, the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composition containing active mica and biological fermentation preparation method of composition containing active mica
  • Composition containing active mica and biological fermentation preparation method of composition containing active mica

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0052] The second aspect of the present invention provides a biofermentation preparation method of a composition containing active mica, at least including the following steps:

[0053] (1) Pulverizing and cleaning the silicate minerals; removing the core of the plum fruit;

[0054] (2) adding silicate minerals, solvent, and plum fruit into the fermenter, mixing and fermenting, the fermentation time is 130-150 days in total, to obtain the mixture;

[0055] (3) The mixture is filtered, and the obtained filtrate is a composition containing active mica.

[0056] In a preferred embodiment, the pulverized silicate minerals described in the present invention have a particle size of 0.5-0.8 cm.

[0057] The method for judging the particle size of the present invention is as follows: firstly separate the pulverized silicate minerals with a sieve with an aperture of 0.8 cm, take the small particles that fall out through the holes, and then separate these small particles with an apertu...

Embodiment 1

[0064] Embodiment 1 provides a composition containing active mica, and its preparation raw materials include: 4 parts of silicate minerals, 5 parts of solvent, and 1 part of plum fruit in parts by weight.

[0065] The silicate mineral is granite.

[0066] The solvent is water.

[0067] Described plum fruit is green plum.

[0068] The present invention also provides a biofermentation preparation method of a composition containing active mica, comprising the following steps:

[0069] (1) Pulverizing and cleaning the silicate minerals; removing the core of the plum fruit;

[0070] (2) Silicate minerals, solvents, and plums are added to the fermenter, mixed and fermented, and the fermentation time is 140 days in total to obtain the mixture;

[0071] (3) The mixture is filtered, and the obtained filtrate is a composition containing active mica.

[0072] The particle size of the pulverized silicate minerals in step (1) is 0.5-0.8 cm.

[0073] The method for determining the part...

Embodiment 2

[0079] Example 2 provides a composition containing active mica, and its preparation raw materials include: 2 parts of silicate minerals, 3 parts of solvent, and 0.5 part of plum fruit in parts by weight.

[0080] Described component raw material is with embodiment 1.

[0081]The present invention also provides a biological fermentation preparation method of a composition containing active mica, the specific steps of which are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to utilization of silicate minerals and bioengineering, in particular to a composition containing active mica and a biological fermentation preparation method of the compositioncontaining active mica. The composition containing active mica is prepared from the following raw materials in parts by weight of 2-6 parts of silicate minerals, 3-8 parts of solvents and 0.5-2 partsof vatica mangachapoi. The composition containing active mica, prepared through biological fermentation, does not contain various harmful components, is rich in effective active components, can degrade residues of pesticides and chemical fertilizers in grains, fruits and vegetables, and can degrade poisonous and harmful substances in household goods, and organic germanium in the composition can beused for treating various diseases of cancer and the like when the composition is used for preparing medicines. In addition, residues obtained through filtering a mixture in the process of preparingthe composition containing active mica through biological fermentation, having various effects, can also be obtained, the composition can be used as pigment of anticorrosive paint, is used for preparing refractory materials, quartz glass, optical fibers, important components of electronics industry, and the like, is used for preparing sun-proof products, is harmless to human bodies, is used as a disinfecting agent to be used for removing hazardous substances, and is used as an air purifying preparation to be used for protecting environment.

Description

technical field [0001] The invention relates to the technical field of silicate mineral utilization and bioengineering, in particular to a composition containing active mica and a biological fermentation preparation method thereof. Background technique [0002] Silicate minerals are an important class of non-metallic mineral resources, and are also the main components of various soils and sediments. They are widely distributed in nature, with various types and abundant reserves. They have been widely used in many production practice fields. Magnesium-containing compounds such as magnesium carbonate, magnesium oxide, and magnesium silicate can be prepared by using magnesium in silicate minerals, and iron-containing compounds such as ferrous oxalate, high-purity iron oxide, and iron-based industrial pigments can be prepared by using iron in them. Magnesium carbonate, magnesium oxide, magnesium silicate, ferrous oxalate, and high-purity iron oxide have high added value, but the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C12P3/00C12P1/00C09G1/02
CPCC09G1/02C12P1/00C12P3/00
Inventor 王希峰金东喆
Owner 王希峰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap