dlc and cd fixing substrates, dlc and cd fixing products

A fixing base and base material technology, applied in textiles, papermaking, fiber treatment, etc., can solve problems such as unavailable, easy oxidation of the surface, and limited film-forming objects, so as to improve quality and yield, improve fixation strength, Effect with high ripple effect

Active Publication Date: 2022-06-24
MIYAKO ROLLER IND
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The conventional DLC film forming method is carried out in a vacuum chamber in a high-temperature atmosphere range of 150°C to 350°C, so the film-forming object (film-forming object) lacks heat resistance, for example, when it is a product or part made of resin or aluminum sometimes deformed
In particular, the surface is easily oxidized and the thermal expansion coefficient is high in the case of an aluminum roll, so high adhesion cannot be obtained when the processing temperature is 200°C or higher.
Therefore, there are restrictions on the object of film formation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • dlc and cd fixing substrates, dlc and cd fixing products
  • dlc and cd fixing substrates, dlc and cd fixing products
  • dlc and cd fixing substrates, dlc and cd fixing products

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0035] (Embodiment of DLC and CD fixing substrate)

[0036] In the DLC and CD fixing bases of the present invention, the DLC fixing bases are used to fix DLC on substrates made of various materials and structures such as paper, leather, resin-made films and sheets, woven fabrics, and textiles, etc., and further fix made of CD.

[0037] [Pretreatment of substrates]

[0038] When producing the DLC and CD-fixed base materials of the present invention, the base material 1 to which the DLC is fixed is prepared. The substrate 1 may be any of cloth, paper, natural leather, artificial leather, resin film, resin sheet, knitted fabric, textile, etc., regardless of the material or structure. Preferably, it is easy to cut and sew (easy to manufacture) and comfortable to use as a product. When specified as underwear fabrics, elastic and easy-to-wear fabrics are suitable. The substrate 1 is preferably cleaned (washed) in advance.

[0039] The base material 1 may be used after pretreatm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The object of the present invention is to firmly fix DLC and CD to substrates of various materials and structures such as paper, leather, resin films, sheets, woven fabrics, and textiles. The present invention is to fix DLC on substrates made of various materials and structures such as paper, leather, resin films, sheets, woven fabrics and textiles, etc., and to fix DLC and CD fixation on the DLC fixation substrate. Substrate. The product of the present invention is a product manufactured using the above-mentioned DLC and CD fixing substrate.

Description

technical field [0001] The present invention relates to fixing (fixing) both CD (Cyclo Dextrin: Cyclo Dextrin) and DLC (Diamond Like Carbon) to paper, leather, resin film, resin sheet, animal fiber (wool, silk, etc.), Substrates formed on fabrics (substrates) such as wovens and textiles of vegetable fibers (cotton, hemp, etc.), chemical fibers (rayon, polyester, etc.), and underwear and diapers using these fixing substrates , physiological products, clothes, umbrellas, coatings, curtains, towels, bedding, carpets, furniture and other products. Background technique [0002] DLC has a crystal structure between diamond and graphite, with high hardness, low friction coefficient, wear resistance, electrical insulation, chemical resistance, antibacterial, hydrophilic, hydrophobic, UV cut-off, gas barrier (not various properties (physical properties) such as air permeability). Therefore, it has been used in various fields. For example, it is used for film formation on the surfac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): D06M15/03D06M11/74
CPCD06M15/03D06M11/74
Inventor町田成司町田成康中本智美寺尾启二石田善行高桥隆一
OwnerMIYAKO ROLLER IND