A 2.5D anti-glare and anti-reflection cover plate and its manufacturing method
A manufacturing method and anti-glare technology, applied in the direction of coating, etc., can solve problems such as affecting the appearance experience and destroying the integrated black effect.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0042] A method for manufacturing a 2.5D anti-glare and anti-reflection cover plate, comprising the following steps:
[0043] S11. A 2.5D glass is provided, and the arc R of the arc area is 0.5 mm.
[0044] S12. Spraying an anti-glare chemical solution on the side of the 2.5D glass with a curved surface, the 2.5D glass is at a pre-curing temperature of 85° C. during spraying, and then completely cured to form an anti-glare coating.
[0045] Wherein, the components of the anti-glare medicinal solution contain by weight: 1% tetraethyl orthosilicate, 10% methanol, 30% 1-methoxy-2-propanol, 1-methoxy-2-acetate 25% propyl ester, 10% isopropanol, 3% N,N-dimethylformamide, 1% ammonia water, and make up 100% with water.
[0046] In the spraying process, the spraying speed is 300mm / sec, the height between the nozzle and the glass is 60mm, the liquid flow rate is controlled at 1g / 10sec, the complete curing temperature is 150°C, the curing time is 80min, and the thickness of the cured a...
Embodiment 2
[0051] A method for manufacturing a 2.5D anti-glare and anti-reflection cover plate, comprising the following steps:
[0052] S21. A 2.5D glass is provided, and the arc R of the arc area is 1 mm.
[0053] S22. Spraying an anti-glare chemical solution on the side of the 2.5D glass with a curved surface, the 2.5D glass is at a pre-curing temperature of 80° C. during spraying, and then completely cured to form an anti-glare coating.
[0054] Wherein, the components of the anti-glare medicinal solution contain by weight: 3% tetraethyl orthosilicate, 6% methanol, 35% 1-methoxy-2-propanol, 1-methoxy-2-acetate 40% propyl ester, 1% isopropanol, 8% N,N-dimethylformamide, 0.8% ammonia water, and make up the balance to 100% with water.
[0055] In the spraying process, the spraying speed is 250mm / sec, the height between the nozzle and the glass is 80mm, the liquid flow rate is controlled at 2g / 10sec, the complete curing temperature is 170°C, the curing time is 120min, and the thickness ...
Embodiment 3
[0060] A method for manufacturing a 2.5D anti-glare and anti-reflection cover plate, comprising the following steps:
[0061] S31. Provide a 2.5D glass, the arc R of the arc area is 2 mm.
[0062] S32. Spraying an anti-glare chemical solution on the side of the 2.5D glass with a curved surface, the 2.5D glass is at a pre-curing temperature of 100° C. during spraying, and then completely cured to form an anti-glare coating.
[0063] Wherein, the components of the anti-glare medicinal solution contain by weight: 5% tetraethyl orthosilicate, 4% methanol, 40% 1-methoxy-2-propanol, acetic acid-1-methoxy-2- 32% propyl ester, 7% isopropanol, 1% N,N-dimethylformamide, 0.1% ammonia water, and make up the balance to 100% with water.
[0064] In the spraying process, the spraying speed is 200mm / sec, the height between the nozzle and the glass is 70mm, the liquid flow rate is controlled at 0.5g / 10sec, the complete curing temperature is 160°C, the curing time is 100min, and the thickness ...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap