Iron-based superconducting tape and preparation method thereof

An iron-based superconductor and iron-based superconductor technology, which is applied in the usage of superconductor elements, superconducting devices, superconducting/high-conducting conductors, etc. Uneven changes in core thickness and width, etc., achieve consistent deformation, uniform deformation, and improve superconducting performance

Active Publication Date: 2020-04-10
INST OF ELECTRICAL ENG CHINESE ACAD OF SCI
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Therefore, the technical problem to be solved by the present invention is to overcome the problem that the compression deformation in the middle of the superconducting strip is larger than that in the edge in the prior art, which causes the superconducting core to vary unevenly in thickness and width, and the superconducting core in the middle of the strip is easy to deform. Defects such as fracture occur, thereby providing an iron-based superconducting tape and a preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Iron-based superconducting tape and preparation method thereof
  • Iron-based superconducting tape and preparation method thereof
  • Iron-based superconducting tape and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] This embodiment provides a single-core iron-based superconducting tape and a preparation method thereof. The preparation method includes the following steps,

[0035] Under an inert atmosphere, the simple substances of iron, potassium, barium and arsenic were mixed and ball-milled and then put into a niobium tube, and calcined for 35 hours at 900°C and 10Mpa to obtain an iron-based superconducting precursor powder (Ba 1-x K x Fe 2 As 2 ), then put the iron-based superconducting precursor powder into the silver tube, seal the two ends with a softer metal, swage, and draw the silver tube filled with the superconducting precursor powder circularly until the diameter of the iron-based superconducting wire is 2.1mm, and then use the square mold in Table 1 to draw the iron-based superconducting wire in a square shape until a square strip with a side length of 1.45mm and a rounded corner of 0.2mm is formed, and then roll it into a side length of 4mm and 0.3mm thick strips, ...

Embodiment 2

[0040] This embodiment provides a multi-core iron-based superconducting tape and a preparation method thereof. The preparation method includes the following steps,

[0041]Under an inert atmosphere, the simple substances of iron, potassium, barium and arsenic were mixed and ball-milled, put into a niobium tube, and calcined at 650 °C and 50 MPa for 10 h to obtain an iron-based superconducting precursor powder (Ba 1-x K x Fe 2 As 2 ), then put the iron-based superconducting precursor powder into the silver tube, seal the two ends with a softer metal, swage, and draw the silver tube filled with the superconducting precursor powder circularly until the diameter of the iron-based superconducting wire is 1.96mm, and then cut the round wire strip into 7 sections of the same length, and wipe it clean to obtain 7 superconducting cores, and then put them into a copper-silver alloy metal tube with an inner diameter of 6mm and an outer diameter of 8mm, Obtain composite wire;

[0042]...

Embodiment 3

[0044] This embodiment provides a single-core iron-based superconducting tape and a preparation method thereof. The preparation method includes the following steps,

[0045] Under an inert atmosphere, the simple substances of iron, sodium and arsenic were mixed and ball-milled and put into a niobium metal tube, and calcined for 35 hours at 900°C and 10Mpa to obtain iron-based superconducting precursor powder (NaFeAs), and then the iron-based superconducting precursor Put the powder into the silver tube, seal both ends with a softer metal, swage, and draw the silver tube filled with superconducting precursor powder circularly until the diameter of the iron-based superconducting wire is 1.95mm, and then use a square mold to shape the iron tube. The base superconducting wire is drawn in a square until a square strip with a side length of 1.55 mm and a rounded corner of 0.3 mm is formed, and then rolled into a strip with a side length of 3.8 mm and a thickness of 0.3 mm, and then r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of iron-based superconductors, and particularly relates to an iron-based superconducting tape and a preparation method thereof. The method comprises: in aninert atmosphere, carrying out rotary swaging, circular drawing, square drawing, rolling and sintering on iron-based superconducting precursor powder to obtain the iron-based superconducting tape. Inthe prior art, the superconducting material is processed in a round wire manner; square drawing is adopted in the invention, so the section shape of the superconducting material is changed; the section shape is square before rolling, in the rolling process, the upper side face and the lower side face of the superconducting strip make contact with a roller at the same time, the deformation amountof the middle and the edge of the superconducting strip is consistent, deformation of the superconducting core is more uniform, the problems that the middle superconducting core is broken, the edge superconducting core is not compact and the phase texture degree is low are solved, and the superconducting performance of the superconducting strip is improved; and the processing mode of enabling thesuperconducting core to deform more uniformly makes it possible to prepare a long wire with higher uniformity.

Description

technical field [0001] The invention belongs to the technical field of iron-based superconductors, and in particular relates to an iron-based superconducting tape and a preparation method thereof. Background technique [0002] Iron-based superconducting material is a new type of high-temperature superconducting material discovered by Japanese scientist Hosono in 2008. So far, four different iron-based superconducting material systems have been discovered: (1) "11" system, mainly including FeSe, FeTe, etc.; (2) "111" system, mainly including AFeAs (A=Li, Na ), etc.; (3) "122" system mainly includes AFeAs (A=Ba, Sr, K, Ca, Eu), etc.; (4) "1111" system mainly includes LnOFeAs (Ln=La, Ce, Pr, Nd , Sm, Gd, Tb, Dy, Ho, Y) and DvOFeAs (Dv=Ca, Sr), etc., are also systems with the highest iron-based superconducting transition temperature (55K). [0003] Compared with traditional superconducting materials, iron-based superconducting materials have the advantages of high upper critic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01B12/02H01B12/06
CPCH01B12/02H01B12/06Y02E40/60
Inventor 刘聪马衍伟张现平王栋樑
Owner INST OF ELECTRICAL ENG CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com