A kind of neodymium iron boron material and its preparation method and application
A kind of NdFeB technology, which is applied in the direction of magnetic materials, inductors/transformers/magnet manufacturing, magnetic objects, etc., can solve the problems of magnet performance deterioration, and achieve uniform magnetic performance, good magnetic performance, and good temperature stability. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1~25 and comparative example 1~9
[0283] The raw materials used to prepare NdFeB materials in Examples 1-25 and Comparative Examples 1-9 are shown in Table 1, and the preparation process is as follows:
[0284] (1) Melting process: according to the formula shown in Table 1, take the prepared raw materials and put them into a crucible made of alumina, and put them in a high-frequency vacuum induction melting furnace at 5×10 -2 Vacuum smelting at a temperature below 1500°C in a vacuum of Pa to obtain a melt.
[0285] (2) Casting process: Ar gas is introduced into the smelting furnace after vacuum smelting to make the air pressure reach 55,000 Pa, and then the casting is carried out, and the molten liquid is passed through a copper roller with a speed of 29 rpm to obtain a speed of 0.12-0.35mm thickness. Condensed gold sheet, during the casting process, the copper roller needs to be fed with chilled water, and the temperature of the water inlet is ≤25°C.
[0286] (3) Hydrogen crushing process: Vacuumize the hydr...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap