A kind of r-t-b series magnetic material and preparation method thereof

A R-T-B, magnetic material technology, applied in the direction of magnetic materials, magnetic objects, inductor/transformer/magnet manufacturing, etc., can solve the problems of high cost, no significant improvement, limited improvement, etc., to achieve the best remanence effect.

Active Publication Date: 2022-05-20
FUJIAN CHANGJIANG GOLDEN DRAGON RARE EARTH CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although there are a few reports in the prior art that substituting part of praseodymium for neodymium can improve the performance of magnet materials, the degree of improvement is limited and there is still no significant improvement
On the other hand, the NdFeB magnet material with better coercive force and remanent magnetism in the prior art also needs to rely on the addition of a large amount of heavy rare earth elements, and the cost is relatively expensive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of r-t-b series magnetic material and preparation method thereof
  • A kind of r-t-b series magnetic material and preparation method thereof
  • A kind of r-t-b series magnetic material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0106] (1) Melting process: According to the formula shown in Table 1, take 50-500 kg of the prepared raw materials, put them into a crucible made of alumina, and heat them in a high-frequency vacuum induction melting furnace at 5×10 -2 Vacuum melting is carried out at 1400-1500°C in a vacuum of Pa.

[0107] (2) Casting process: after vacuum smelting, Ar gas is passed into the smelting furnace to make the air pressure reach 55,000 Pa, and then casting is carried out at 10 2 ℃ / sec-10 4°C / sec cooling rate to obtain quenched alloy.

[0108] (3) Hydrogen crushing process: At 20-25°C, vacuumize the hydrogen crushing furnace where the quenched alloy is placed 5×10 -2 Pa, and then feed hydrogen gas with a purity of 99.9% into the hydrogen crushing furnace to maintain the hydrogen pressure at 0.15MPa. powder.

[0109] (4) Micro-grinding process: Under a nitrogen atmosphere with a content of less than 150ppm, under the condition of a crushing chamber pressure of 0.38MPa, the powder...

Embodiment 2

[0115] (1) Melting process: According to the formula shown in Table 1, take 50-500 kg of the prepared raw materials, put them into a crucible made of alumina, and heat them in a high-frequency vacuum induction melting furnace at 5×10 -2 Vacuum melting is carried out at 1400-1500°C in a vacuum of Pa.

[0116] (2) Casting process: after vacuum smelting, Ar gas is passed into the smelting furnace to make the air pressure reach 55,000 Pa, and then casting is carried out at 10 2 ℃ / sec-10 4 °C / sec cooling rate to obtain quenched alloy.

[0117] (3) Hydrogen crushing process: At 20-25°C, vacuumize the hydrogen crushing furnace where the quenched alloy is placed 5×10 -2 Pa, and then feed hydrogen gas with a purity of 99.9% into the hydrogen crushing furnace to maintain the hydrogen pressure at 0.15MPa. powder.

[0118] (4) Micro-grinding process: Under a nitrogen atmosphere with a content of less than 150ppm, under the condition of a crushing chamber pressure of 0.38MPa, the powde...

Embodiment 3

[0124] (1) Melting process: According to the formula shown in Table 1, take 50-500 kg of the prepared raw materials, put them into a crucible made of alumina, and heat them in a high-frequency vacuum induction melting furnace at 5×10 -2 Vacuum melting is carried out at 1400-1500°C in a vacuum of Pa.

[0125] (2) Casting process: after vacuum smelting, Ar gas is passed into the smelting furnace to make the air pressure reach 55,000 Pa, and then casting is carried out at 10 2 ℃ / sec-10 4 °C / sec cooling rate to obtain quenched alloy.

[0126] (3) Hydrogen crushing process: At 20-25°C, vacuumize the hydrogen crushing furnace where the quenched alloy is placed 5×10 -2 Pa, and then feed hydrogen gas with a purity of 99.9% into the hydrogen crushing furnace to maintain the hydrogen pressure at 0.15MPa. powder.

[0127] (4) Micro-grinding process: Under a nitrogen atmosphere with a content of less than 150ppm, under the condition of a crushing chamber pressure of 0.38MPa, the powde...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an R-T-B-based magnetic material, which is characterized in that, in terms of weight percentage, it comprises the following components: 29.50wt.% to 33.00wt.% of R; the R is a rare earth element , which contains Pr and R H ; said Pr≥15.00wt.%; said R H Contains Tb and / or Dy; 0.24wt.% to 0.80wt.% Cu; 0.08wt.% to 0.19wt.% Zr; 0wt.% to 1.52wt.% Al; 0.90wt.% to 1.03wt. % B; and, 0.05 wt.% to 1.50 wt.% Ga. The magnetic material has better remanence, coercive force, temperature coefficient, etc.

Description

technical field [0001] The invention relates to an R-T-B series magnetic material and a preparation method thereof. Background technique [0002] Take Nd 2 Fe 14 Neodymium-iron-boron (NdFeB) magnet material with B as the main component has high remanence, coercive force and maximum magnetic energy product, and excellent comprehensive magnetic properties. It is used in wind power generation, new energy vehicles, and frequency conversion home appliances. The rare earth components in the current NdFeB magnet materials in the prior art are usually mainly neodymium, with only a small amount of praseodymium. Although there are a few reports in the prior art that substituting part of praseodymium for neodymium can improve the performance of magnet materials, the degree of improvement is limited and there is still no significant improvement. On the other hand, the NdFeB magnet materials with better coercive force and remanent magnetism in the prior art also need to rely on the ad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01F1/057H01F41/02
CPCH01F1/0577H01F41/0253H01F41/0266Y02E10/72
Inventor 付刚黄佳莹黄清芳许德钦
Owner FUJIAN CHANGJIANG GOLDEN DRAGON RARE EARTH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap