A kind of preparation method of colorless transparent sodium polyacrylate dispersant

A technology of sodium polyacrylate and dispersant, which is applied in the field of preparation of sodium polyacrylate to achieve the effect of increasing shelf life, reducing production cost and preventing mold

Active Publication Date: 2021-10-08
SNF CHINA FLOCCULANT
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Prior to this, there were few relevant literature and patent reports aimed at the synthesis of colorless transparent sodium polyacrylate dispersant

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Step (1): Add a 3.4% sodium hypophosphite aqueous solution into the reactor as an initial solution, the liquid level of the initial solution is higher than the stirring blades of the reactor, and the temperature of the reactor is adjusted to 80°C;

[0031] Step (2): Add the acrylic acid aqueous solution, the ammonium persulfate aqueous solution and the sodium hypophosphite aqueous solution into the reactor at a constant speed and in parallel, wherein the mass ratio of the acrylic acid and ammonium persulfate is 40; the acrylic acid and sodium hypophosphite The mass ratio is 20; the stirring speed is kept at 300rpm during the dropping process, and the temperature of the reactor is maintained at 85°C until the dropping process ends;

[0032] Step (3): Adjust and maintain the temperature of the reactor at 70°C, add benzoyl peroxide to the reactor, wherein the mass ratio of acrylic acid to benzoyl peroxide is 300, when benzoyl peroxide After the acyl is fully stirred evenly...

Embodiment 2

[0034] Step (1): Add 3.4% sodium hypophosphite aqueous solution into the reaction kettle as the initial solution, the liquid level of the initial solution is higher than the stirring blade of the reaction kettle, and the temperature of the reaction kettle is adjusted to 60°C;

[0035] Step (2): Acrylic acid aqueous solution, benzoyl peroxide aqueous solution and sodium hypophosphite aqueous solution are respectively added in the reaction kettle at a constant speed in parallel, wherein the mass ratio of the acrylic acid and benzoyl peroxide is 40; acrylic acid and The mass ratio of sodium hypophosphite is 20; the stirring speed is kept at 300rpm during the dropping process; light is used for the first stage of irradiation in the reactor, and a 50W high-pressure mercury lamp is used for irradiation, the main wavelength is 365nm, and the irradiation area of ​​the light is the inside of the reactor 3 / 4 of the cross-sectional area, the distance between the reactor and the light emit...

Embodiment 3

[0038] Step (1): Add a 3.4% aqueous solution into the reaction kettle as an initial solution, the liquid level of the initial solution is higher than the stirring blade of the reaction kettle, and adjust the temperature of the reaction kettle to 80°C;

[0039] Step (2): Add the acrylic acid aqueous solution, the ammonium persulfate aqueous solution and the sodium hypophosphite aqueous solution into the reactor at a constant speed and in parallel, wherein the mass ratio of the acrylic acid and ammonium persulfate is 40; the acrylic acid and sodium hypophosphite The mass ratio is 20; the stirring speed is kept at 300rpm during the dropping process, and the temperature of the reactor is maintained at 85°C until the dropping process ends;

[0040] Step (3): The reaction kettle is irradiated with light in the second stage, using a 75W fluorescent lamp for irradiation, the main wavelength range is 450nm, and the irradiation area of ​​the light is 3 / 4 of the internal cross-sectional a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
wavelengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a colorless and transparent sodium polyacrylate dispersant. The low-molecular-weight polymerized acrylic acid is synthesized through light-assisted initiation of polymerization at the initial stage of polymerization. The polymerized acrylic acid is continuously irradiated with ultraviolet rays during the neutralization process with sodium hydroxide. light or visible light. Finally, a certain amount of benzoyl peroxide is added to the synthesized polymer to achieve the corresponding decolorization and antiseptic effects. The invention prepares a sodium polyacrylate dispersant, the sodium polyacrylate dispersant is in a colorless and transparent state, its chromaticity is excellent when tested by a spectrophotometer, and a good effect is achieved in the application field. The dispersant has simple preparation method, low cost, stable product performance and good dispersion performance.

Description

technical field [0001] The invention relates to the field of polymer synthesis, in particular to a preparation method of colorless and transparent sodium polyacrylate. [0002] technical background [0003] Sodium polyacrylate dispersant is often used in papermaking, coatings, textiles, water treatment, agriculture, daily chemicals, civil engineering, ceramics, etc. In the process of use, most of the sodium polyacrylate dispersant aqueous solutions can be used directly. In most applications, due to the chromaticity requirements of downstream products, it is necessary to use colorless and transparent sodium polyacrylate dispersants. Often cheap acrylic acid raw materials on the market, including acrylic acid waste liquid, the polymerized products are often yellow or pink, which cannot meet the needs of downstream application industries and limit its application range in many fields. How to synthesize high-quality colorless and transparent products with cheap raw materials has...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08F120/06C08F2/38C08F2/48C08F4/40C08F4/34C08F4/30C08F8/42C08F6/06
CPCC08F2/38C08F2/48C08F4/30C08F4/34C08F4/40C08F6/06C08F8/42C08F120/06C08L33/02
Inventor 陶倩云凌静丁健
Owner SNF CHINA FLOCCULANT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap