Drill bit housing steel and preparation method thereof

A steel and shell technology, which is applied in the direction of drill bits, earthwork drilling, drilling equipment, etc., can solve the problems of short service life and wear resistance defects of drill bit shells, and improve high temperature mechanical properties, hardness and wear resistance properties, good strength and wear resistance

Pending Publication Date: 2020-08-07
ZHEJIANG PULANKA ROCK TOOLS CO LTD
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In the actual application process of the above technical solution, it has relatively good performance, but there are still defects in wear resistance, resulting in a short service life of the bit shell, which needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Drill bit housing steel and preparation method thereof
  • Drill bit housing steel and preparation method thereof
  • Drill bit housing steel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] A steel material for the drill bit shell, the chemical composition of which is shown in Table 3.

[0051] Such as figure 1 Shown, the preparation method of this drill bit shell comprises the following steps:

[0052] S1, ironmaking, reducing sintered ore to molten iron in a blast furnace, the temperature of the blast furnace is 1500-1700°C;

[0053] S2, steelmaking, alloy raw materials are weighed according to the weight ratio of each element, and the alloy raw materials are put into molten iron in the converter or electric furnace to make steel. The temperature of the ladle is 1550-1650 ° C. The molten steel after smelting is in the LF refining furnace and VD furnace for refining treatment, the refined molten steel is poured into continuous casting slabs in the continuous casting machine, and the steelmaking-continuous casting cycle is 6h;

[0054] S3, steel rolling, the temperature of the heating furnace is 900-1100°C, the continuous casting slab is heated by the he...

Embodiment 2

[0071] The difference from Example 1 is that the chemical composition of the drill bit shell steel is shown in Table 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses drill bit housing steel and a preparation method thereof, and relates to the technical field of rock drilling tools. The steel is prepared from the chemical components: 0.22-0.34% of C, 0.10-0.35% of Si, 0.40-0.60% of Mn, less than or equal to 0.030% of P, less than or equal to 0.030% of S, 1.10-1.40% of Cr, 0.20-0.45% of Mo and 3.90-4.30% of Ni. Chromium in the steel enhances the hardenability of the steel and has a secondary hardening effect, a drill bit housing has good corrosion resistance and oxygen resistance, and the hardness and wear resistance of high carbon steel are improved without embrittling the steel. Meanwhile, through the adoption of chromium, the high-temperature mechanical properties of the steel are improved, and the performance impact of high temperature generated in the rock drilling process on the drill bit housing is reduced. In terms of chemical components, vanadium is replaced with chromium, so that more uniform strength, toughness andfatigue strength of the drill bit housing are obtained, and better strength and wear resistance of the drill bit housing are obtained. Meanwhile, through the proportion adjustment of other metal elements, the drill bit housing is more suitable for rock drilling in limestone areas.

Description

technical field [0001] The invention relates to the technical field of rock drilling tools, more specifically, it relates to the steel material of the drill bit shell and its preparation method. Background technique [0002] The drill bit is a kind of drilling tool used for rock drilling construction, and is widely used in various mining projects and stonework projects. [0003] The Chinese patent with the notification number CN205618084U discloses a threaded drill bit, which includes a drill bit shell arranged in a cylindrical shape, a number of buttons are arranged on the top of the drill bit shell, and the outer peripheral surface of the drill bit shell is located on the drill bit. Both ends of the shell diameter are respectively provided with a positioning hole and a positioning post matched with the positioning hole, and a fixing part for fixing the positioning post is arranged in the positioning post. [0004] The Chinese patent whose publication number is CN1034396A ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/44C21D8/00C22C33/04E21B10/46
CPCC21D8/005C21D2211/001C22C33/04C22C38/02C22C38/04C22C38/44E21B10/46
Inventor 沈国华
Owner ZHEJIANG PULANKA ROCK TOOLS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap