Matt protective glaze for thin ceramic tiles with glossiness below 3 degrees, thin ceramic tiles and preparation method thereof

A glossy, ceramic tile technology, applied in the field of ceramic tile manufacturing, can solve the problem of serious light pollution of high-gloss ceramic products, and achieve the effects of good antifouling performance, good transparency, and delicate glaze texture

Active Publication Date: 2022-02-11
MONALISA GRP CO LTD
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problem of serious light pollution of high-gloss ceramic products in the prior art, the present invention provides a matt protective glaze for thin ceramic tiles with a glossiness of less than 3 degrees, thin ceramic tiles and a preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Step 1: Press and shape the green body powder to form a high white green body.

[0046] Step 2: drying the high-white green body at high temperature for 15-30 minutes, and controlling the water content of the dried green body within 0.5 wt%.

[0047] Step 3: Inkjet print the design pattern on the surface of the dried high white body.

[0048] Step 4: Prepare matt protective glaze according to the ratio. The mineral composition of the matt protective glaze is as follows: by mass percentage, potassium feldspar 18.0%, albite 7.0%, washed kaolin 24.0%, quartz 16.0%, barium carbonate 8.0%, burnt talc 1.5%, Strontium carbonate: 1.5%, high temperature matte frit 24.0%. The chemical composition of the matte protective glaze is: by mass percent, by mass percent, SiO 2 : 57.08%, Al 2 o 3 : 17.33%, Fe 2 o 3 : 0.36%, TiO 2 : 0.04%, CaO: 1.77%, MgO: 1.09%, K 2 O: 3.33%, Na 2 O: 1.94%, BaO: 8.95%, SrO: 1.50%, ZnO: 1.34%, loss on ignition: 5.13%.

[0049] Step 5: Apply matt...

Embodiment 2

[0055] Step 1: Press and shape the green body powder to form a high white green body.

[0056] Step 2: drying the high-white green body at high temperature for 15-30 minutes, and controlling the water content of the dried green body within 0.5 wt%.

[0057] Step 3: Inkjet print the design pattern on the surface of the dried high white body.

[0058] Step 4: Prepare matt protective glaze according to the ratio. The mineral composition of the matt protective glaze is: in terms of mass percentage, potassium feldspar 16.0%, albite 10.0%, washed kaolin 28.0%, quartz 14.0%, barium carbonate 9.0%, strontium carbonate: 0.5%, burnt talc: 2.5% %, high temperature matte frit 20.0%. The chemical composition of the matt protective glaze is: by mass percentage, SiO 2 : 56.40%, Al 2 o 3 : 18.28%, Fe 2 o 3 : 0.40%, TiO 2 : 0.04%, CaO: 1.53%, MgO: 1.34%, K 2 O: 3.07%, Na 2 O: 2.15%, BaO: 9.29%, SrO: 0.73%, ZnO: 1.11%, loss on ignition: 5.51%.

[0059] Step 5: Spray matte protective ...

Embodiment 3

[0065] Step 1: Press and shape the green body powder to form a high white green body.

[0066] Step 2: drying the high-white green body at high temperature for 15-30 minutes, and controlling the water content of the dried green body within 0.5 wt%.

[0067] Step 3: Inkjet print the design pattern on the surface of the dried high white body.

[0068] Step 4: Prepare matt protective glaze according to the ratio. The mineral composition of the matt protective glaze is as follows: by mass percentage, potassium feldspar: 20.0%, albite: 4.0%, washed kaolin: 20.0%, quartz: 18.0%, barium carbonate: 7.0%, strontium carbonate: 2.5% , burnt talc: 0.5%, high temperature matte frit: 28.0%. The chemical composition of the matt protective glaze is: by mass percentage, SiO 2 : 57.77%, Al 2 o 3 : 16.38%, Fe 2 o 3 : 0.32%, TiO 2 : 0.03%, CaO: 2.00%, MgO: 0.84%, K 2 O: 3.59%, Na 2 O: 1.74%, BaO: 8.60%, SrO: 2.28%, ZnO: 1.56%, loss on ignition: 4.74%.

[0069] Step 5: Spray matte prote...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
glossaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a matte protective glaze for thin ceramic tiles with a glossiness of less than 3 degrees, thin ceramic tiles and a preparation method thereof. The chemical composition of the matt protective glaze includes: in mass percent, SiO 2 : 55.0~60.0%, Al 2 o 3 : 16.0~20.0%, Fe 2 o 3 : 0.1~0.5%, TiO 2 : 0.01~0.2%, CaO: 0.5~2.5%, MgO: 0.5~2.0%, K 2 O: 2.5~4.0%, Na 2 O: 1.5-3.0%, BaO: 8.0-10.0%, SrO: 0.5-2.5%, ZnO: 0.5-2.0%, loss on ignition: 4.0-6.0%.

Description

technical field [0001] The invention relates to a matt protective glaze with a glossiness of less than 3 degrees for thin ceramic tiles, a thin ceramic tile using the matt protective glaze and a preparation method thereof, belonging to the technical field of ceramic tile production. Background technique [0002] Ceramics is a general term for various products made of natural clay, feldspar, quartz and other natural silicate minerals as the main raw materials through crushing, mixing, molding and calcination. Ceramic tiles are the most widely used ceramic products. . With the rapid development in recent decades, the output of ceramic tiles has been ranked first in the world for many years, causing many ceramic raw materials such as clay silicate minerals to face the problems of over-exploitation and resource depletion. , energy, and waste emissions, the development of green and environmentally friendly architectural ceramics has become the goal of the entire industry. The t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/04C04B41/86
CPCC03C8/04C04B41/86C04B41/5022
Inventor 潘利敏杨元东汪陇军王贤超郑贵友
Owner MONALISA GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com