A kind of alloyed hot-dip galvanized dh980 steel and preparation method thereof

Abstract

The invention discloses an alloyed hot-dip galvanized DH980 steel and a preparation method thereof. Contained in steel, C: 0.16% to 0.23%, Mn: 1.5% to 2.5%, Si: 0.2% to 0.9%, Al: 0.02% to 0.9%, Cr: 0.02% to 0.70%, P≤0.01%, S ≤0.01%, Nb≤0.05%, V≤0.05%, Ti≤0.05%, and Si+Al: 0.6%~1.5%, the rest is iron and unavoidable impurities. Slab heating temperature 1150-1300°C, starting rolling temperature 1000-1150°C, finishing rolling temperature ≥ 880°C, coiling temperature 500-700°C; cold rolling reduction rate 40%-80%; annealing temperature 760-880°C , annealing time 30 ~ 300s, galvanizing temperature 450 ~ 470 ℃, alloying temperature 470 ~ 530 ℃, alloying holding time 5 ~ 60s. The tensile strength of the finished steel plate is 980-1100MPa, and the high-cycle fatigue limit strength is ≥370MPa. Excellent hole expansion performance.

Description

technical field [0001] The invention belongs to the technical field of cold-rolled steel, and relates to a DH980 alloyed hot-dip galvanized automobile steel plate with high strength, high plasticity and excellent fatigue resistance and a preparation method thereof. Background technique [0002] In the automotive industry, higher requirements have been put forward for body weight reduction, emission restrictions, and safety standards. In order to better serve users, the automotive industry has more and more demands for parts with high formability. Traditional dual-phase steels are difficult to meet the requirements of high-drawability complex punching cups, and TRIP steels are widely used due to high alloy content and expensive production costs. DH steel is the English abbreviation of Dual Phase Steels with Improved Formability, which was first mentioned in the VDA 239-100 cold-formed steel plate standard issued by the German Association of Automobile Manufacturers in 2016. ...

AI Technical Summary

Problems solved by technology

[0003] Patent document CN 106119716 A discloses a 1000MPa grade cold-rolled hot-dip galvanized dual-phase steel with enhanced plasticity and its manufacturing method. Its main chemical components are: C: 0.15%-0.23%, Si: 0.1%-0.5%, Mn: 1.8%~2.3%, P≤0.01%, S≤0.01%, Al: 0.5%~1.0%, Cr: 0.3%~0.6%, Ti: 0.01%~0.04%, the balance is Fe and unavoidable impurities , the patented production process mainly adopts hot-dip galvanizing process, the product has poor plasticity and insufficient fatigue resistance

[0004] Patent document CN 109554616 A discloses a 700MPa hot-rolled TRIP-assisted dual-phase steel and its preparation method. Its main chemical components are: C: 0.14%-0.16%, Si: 0.42%-0.65%, Mn: 1.6% ~1.7%, Al: 0.5%~0.8%, P≤0.014%, S≤0.003%, the production process mainly adopts hot rolling, the strength level is 700MPa, the strength level of this patented product is far from meeting the performance requirements of DH980