Organic hydrogel with adjustable mechanical properties as well as preparation method and application thereof

An adjustable, hydrogel technology, applied in the field of organic hydrogels with adjustable mechanical properties and its preparation, can solve the problems of fragile mechanical properties, great influence on the performance of flexible electronic devices, lack of research, etc., and achieves a wide range of applications. Effect

Active Publication Date: 2021-01-08
HUBEI UNIV +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Generally, the mechanical properties of hydrogels have a great influence on the performance of flexible electronic devices, while conventional hydrogels prepared with water as a solvent have fragile mechanical properties; currently, there is a lack of research on hydrogels with adjustable mechanical properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic hydrogel with adjustable mechanical properties as well as preparation method and application thereof
  • Organic hydrogel with adjustable mechanical properties as well as preparation method and application thereof
  • Organic hydrogel with adjustable mechanical properties as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The invention provides a method for preparing an organic hydrogel with adjustable mechanical properties, such as figure 1 shown, including the following steps:

[0030] S1. Add monomers, cross-linking agents and cross-linking accelerators to the complex solvent, shake and dissolve to obtain the first solution;

[0031] S2, adding the initiator into the complex solvent, shaking and dissolving to obtain the second solution;

[0032] S3. Add the second solution to the first solution, and obtain the organic hydrogel after curing and molding;

[0033] Wherein, the monomer includes one of acrylamide, acrylic acid, and N-isopropylacrylamide; the composite solvent is a mixture of alcohol and water, and the alcohol includes ethylene glycol, glycerol, hexyl alcohol, polyethylene glycol, and polyethylene glycol. at least one of vinyl alcohol.

[0034] It should be noted that, in the examples of the present application, the composite solvent can be formed by mixing water and eth...

Embodiment 2

[0043] The invention provides a method for preparing an organic hydrogel with adjustable mechanical properties, such as figure 1 shown, including the following steps:

[0044] S1. Add monomers, cross-linking agents and cross-linking accelerators to the complex solvent, shake and dissolve to obtain the first solution;

[0045] S2, adding the initiator into the complex solvent, shaking and dissolving to obtain the second solution;

[0046] S3. Add the second solution to the first solution, and obtain the organic hydrogel after curing and molding;

[0047] Specifically, S1 in this application is specifically: take 1g of acrylamide and 0.016g of N,N-methylene

[0048] Add 160 μL N,N,N',N',-Tetramethylethylenediamine to a compound solvent (mass ratio of glycerol to water: 1:1) mixed with glycerol and water, shake Dissolving to obtain the first solution;

[0049] S2 is specifically: taking 0.1 g of ammonium persulfate and adding it to a composite solvent formed by mixing glycero...

Embodiment 3

[0054] The invention provides a method for preparing an organic hydrogel with adjustable mechanical properties, such as figure 1 shown, including the following steps:

[0055] S1. Add the monomer, crosslinking agent and crosslinking accelerator into the composite solvent, shake and dissolve to obtain

[0056] to the first solution;

[0057] S2, adding the initiator into the complex solvent, shaking and dissolving to obtain the second solution;

[0058] S3. Add the second solution to the first solution, and obtain the organic hydrogel after curing and molding;

[0059] Specifically, S1 in this application is specifically: take 1g of acrylamide, 0.016g of N,N-methylenebisacrylamide, and 160 μL of N,N,N',N',-tetramethylethylenediamine and add In the composite solvent (glycerol and water mass ratio is 1:2) that glycerol and water are mixed, shake and dissolve, obtain the first solution;

[0060] S2 is specifically: taking 0.1 g of ammonium persulfate and adding it to a composi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides organic hydrogel with adjustable mechanical properties as well as a preparation method and application thereof. The method comprises the following steps of adding a monomer, a cross-linking agent and a cross-linking accelerant into a composite solvent, and oscillating and dissolving to obtain a first solution, adding an initiator into the composite solvent, and oscillating and dissolving to obtain a second solution, adding the second solution into the first solution, and curing and molding to obtain organic hydrogel, wherein the monomer comprises one of acrylamide, acrylic acid and N-isopropylacrylamide, the composite solvent is formed by mixing alcohol and water, and the alcohol comprises at least one of ethylene glycol, glycerol, hexanehexol, polyethylene glycol and polyvinyl alcohol. The mixture of alcohol and water is used as the composite solvent, and the mass ratio of alcohol to water and the mass ratio of alcohol to water to acrylamide are adjusted, so that the mechanical properties of the obtained organic hydrogel can be adjusted.

Description

technical field [0001] The invention relates to the technical field of preparation of flexible materials, in particular to an organic hydrogel with adjustable mechanical properties and a preparation method and application thereof. Background technique [0002] Hydrogel is one of the most promising soft materials, widely used in drug controlled release, polyelectrolyte, ion touch panel, etc. Generally, the mechanical properties of hydrogels have a great influence on the performance of flexible electronic devices, while the conventional hydrogels prepared with water as a solvent have fragile mechanical properties; currently, there is a lack of research on hydrogels with adjustable mechanical properties. [0003] Based on this, it is necessary to provide an organic hydrogel with adjustable mechanical properties. Contents of the invention [0004] In view of this, the present invention proposes an organic hydrogel with adjustable mechanical properties and its preparation meth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/56C08F222/38C08J3/075C08L33/26
CPCC08F220/56C08J3/075C08J2333/26C08F222/385
Inventor 何云斌程欢易铭徐雅欣卢寅梅常钢黎明锴柯鹏杨连遇吉
Owner HUBEI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap