Degradable non-woven fabric and preparation method thereof

A technology of non-woven fabric and pineapple leaf fiber, which is applied in the directions of melt spinning, non-woven fabric, rayon manufacturing, etc., can solve problems such as difficulty in degradation, and achieve the effect of moderate softness, good degradable performance and improved strength of the finished product

Pending Publication Date: 2021-01-08
惠州市杰佰净化有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The main raw material of nonwovens is polypropylene. However, PP is a linear saturated hydrocarbon, which is difficult

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Degradable non-woven fabric and preparation method thereof
  • Degradable non-woven fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0033]Specifically, the present invention provides a preparation method of the above-mentioned degradable non-woven fabric, the preparation method includes the following steps:

[0034]Raw material mixing: Put the toughened polylactic acid fiber, polyester fiber and pineapple leaf fiber into a mixing container at a mass ratio of 5-7:2~3:1, pour deionized water into the mixing container, and stir until the toughened polylactic acid The fiber, polyester fiber and pineapple leaf fiber are mixed evenly, and the mixed raw materials are taken out and drained;

[0035]Opening: using an opening machine to open and break up the mixed raw materials to prepare a mixed fiber;

[0036]Pre-carding: Pre-carding the mixed fiber with a carding machine;

[0037]Laying: Conveying the pre-carded mixed fibers into the laminating machine to make a composite fiber web;

[0038]Main carding: The composite fiber web is transported to the main carding machine for secondary carding to obtain the upper thin web and the lower...

Example Embodiment

[0064]Example 1

[0065]The degradable non-woven fabric of Example 1 of the present invention was prepared by the following method:

[0066]Raw material mixing: put the toughened polylactic acid fiber, polyester fiber and pineapple leaf fiber into a mixing container at a mass ratio of 5:2:1, pour deionized water into the mixing container, and stir until the toughened polylactic acid fiber and polyester fiber Mix well with pineapple leaf fiber, remove the mixed raw materials and drain the water;

[0067]Opening: using an opening machine to open and break up the mixed raw materials to prepare a mixed fiber;

[0068]Pre-carding: Pre-carding the mixed fiber with a carding machine;

[0069]Laying: Conveying the pre-carded mixed fibers into the laminating machine to make a composite fiber web;

[0070]Main carding: The composite fiber web is transported to the main carding machine for secondary carding to obtain the upper thin web and the lower thin web;

[0071]Hot press rewinding: the upper thin web and the...

Example Embodiment

[0076]Example 2

[0077]The degradable non-woven fabric of Example 2 of the present invention was prepared by the following method:

[0078]Raw material mixing: Put the toughened polylactic acid fiber, polyester fiber and pineapple leaf fiber into a mixing container at a mass ratio of 6:3:1, pour deionized water into the mixing container, and stir until the toughened polylactic acid fiber and polyester fiber Mix well with pineapple leaf fiber, remove the mixed raw materials and drain the water;

[0079]Opening: using an opening machine to open and break up the mixed raw materials to prepare a mixed fiber;

[0080]Pre-carding: Pre-carding the mixed fiber with a carding machine;

[0081]Laying: Conveying the pre-carded mixed fibers into the laminating machine to make a composite fiber web;

[0082]Main carding: The composite fiber web is transported to the main carding machine for secondary carding to obtain the upper thin web and the lower thin web;

[0083]Hot press rewinding: the upper thin web and the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a degradable non-woven fabric. The preparation method comprises the following steps of mixing raw materials, specifically, putting toughened polylacticacid fibers, polyester fibers and pineapple leaf fibers into a mixing container according to a mass ratio of (5-7):(2-3):1, injecting deionized water into the mixing container, stirring until the toughened polylactic acid fibers, the polyester fibers and the pineapple leaf fibers are uniformly mixed, fishing out the mixed raw materials, and draining off water; opening, specifically, utilizing an opener to open and scatter the mixed raw materials to prepare mixed fibers; pre-carding, specifically, pre-carding the mixed fibers by using a carding machine; lapping, specifically, conveying the pre-carded mixed fibers into a lapping machine to prepare a composite fiber net; main carding, specifically, conveying the composite fiber net into a main carding machine for secondary carding to obtain an upper-layer thin net and a lower-layer thin net; and hot-pressing and rolling, specifically, conveying the upper-layer thin net and the lower-layer thin net to a heat-sealing forming machine, and rolling and storing the degradable non-woven fabric obtained after heat-sealing operation.

Description

Technical field[0001]The invention belongs to the technical field of non-woven fabrics, and specifically relates to a degradable non-woven fabric and a preparation method thereof.Background technique[0002]Non-woven fabrics, also known as non-woven fabrics, non-woven fabrics, are composed of oriented or random fibers. It is called cloth because of its appearance and certain properties. It is widely used in agriculture, industry, sanitation and daily life. For example, polypropylene (PP material) pellets are mostly used as raw materials, which are produced by a continuous one-step method of high-temperature melting, spinning, laying, and hot pressing.[0003]According to the applicant’s research, the following problems exist in the prior art:[0004]The main raw material of non-woven fabrics is polypropylene. However, PP is a linear saturated hydrocarbon, which is difficult to degrade in nature, making the development and production of degradable materials a worldwide environmental issue....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D04H1/541D04H1/559D01D5/08D01C1/00D01F6/92D01F1/10
CPCD01C1/00D01D5/08D01F1/10D01F6/92D04H1/541D04H1/559
Inventor 黄马壮
Owner 惠州市杰佰净化有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka