A preparation method of white molecular adsorption coating with thermal control function
A molecular adsorption and white technology, applied in coatings, reflective/signal coatings, alkali metal silicate coatings, etc., can solve the problems of large size, insufficient absorption area, inflexible installation position, etc., to improve the bonding strength, Improve structural stability and dispersion, improve the effect of comprehensive performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
specific Embodiment approach 1
[0044] (1) Heat and dry 13X-type zeolite molecular sieve powder with micropores and / or mesoporous channels with a pore size less than 20 nm to discharge excess water vapor in the zeolite and facilitate rapid pumping during the atomic layer deposition process. The specific operation is: heat the zeolite molecular sieve powder in a tube furnace, heat it to 200°C within 0.5h, vacuumize it to -0.1MPa, keep it warm for 2h, and cool it down to room temperature naturally.
[0045] (2) Zeolite molecular sieve powder, zinc oxide and a certain amount of ZrO after the above-mentioned treatment 2 Put the grinding balls together into the ball mill tank, cover the lid, use the two air holes reserved on the tank cover to fill in the argon gas with a purity of 99.99% for 10 minutes to completely discharge the air, and finally fix the ball mill tank to the ball mill Here, set the rotating speed of the ball mill to 600rpm, and the ball milling time to 4h. Wherein, the zinc oxide particle size ...
PUM
Property | Measurement | Unit |
---|---|---|
pore size | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
adsorption capacity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com