Low-yellowing material fading prevention UV primer and preparation method thereof

A material and low-yellow technology, applied in the field of low-yellowing and anti-fading UV primer and its preparation field, can solve the problems of affecting the quality of dyed wood furniture, easy discoloration of dyed wood, fading of dyed wood, etc., and improve UV curing. Moderate performance, hardness and flexibility, and improved adhesion

Inactive Publication Date: 2021-06-11
东莞大宝化工制品有限公司 +2
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, stained wood is easy to fade due to ultraviolet radiation during production and use, which in turn affects the quality of stained wood furniture
And UV paint, especially the UV primer that is in direct contact with the surface of the stained wood, needs to be irradiated by an ultraviolet lamp to form a cured film after painting. In this way, when the UV lamp irradiates the UV primer, it will also irradiate the stained wood. surface, making it easier to fade stained wood
[0004] Therefore, there is an urgent need to develop a kind of low yellowing performance, which can effectively prevent stained wood from fading during UV curing and use, and also has good UV primer with stained wood surface adhesion, so as to effectively avoid stained wood during production and use. Defects that are easy to change color and fall off during use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-yellowing material fading prevention UV primer and preparation method thereof
  • Low-yellowing material fading prevention UV primer and preparation method thereof
  • Low-yellowing material fading prevention UV primer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A kind of low-yellowing anti-fading UV primer of the present embodiment consists of the following raw materials in parts by weight:

[0035]

[0036]

[0037] Among them, the photoinitiator is composed of methyl benzoylformate and 2,4,6-trimethylbenzoyl-diphenylphosphine oxide in a mass ratio of 1:0.1.

[0038] Among them, the ultraviolet light absorber is composed of a benzotriazole ultraviolet absorber and a hindered amine ultraviolet absorber in a mass ratio of 1:0.8. The benzotriazole UV absorber is 2-(2′-hydroxyl-3′,5′-di-tert-phenyl)-5-chlorinated benzotriazole. The hindered amine UV absorber is composed of UV-770 and UV-3853 in a mass ratio of 1:0.6. The antioxidant is a phosphite antioxidant.

[0039] Wherein, the particle size of the talcum powder is 500 mesh. The defoamer is an acrylic defoamer. The dispersant is a polymer dispersant. The anti-settling agent is fumed silica.

[0040] A kind of preparation method of the UV primer of anti-yellowing a...

Embodiment 2

[0045] A kind of low-yellowing anti-fading UV primer of the present embodiment consists of the following raw materials in parts by weight:

[0046]

[0047]

[0048] Among them, the photoinitiator is composed of methyl benzoylformate and 2,4,6-trimethylbenzoyl-diphenylphosphine oxide in a mass ratio of 1:0.3.

[0049] Among them, the ultraviolet light absorber is composed of a benzotriazole ultraviolet absorber and a hindered amine ultraviolet absorber in a mass ratio of 1:0.5. Benzotriazole UV absorber consists of 2-(2ˊ-hydroxy-3ˊ,5ˊ-di-tert-phenyl)-5-chlorinated benzotriazole and 2-(2ˊ-hydroxy-5ˊ-methylphenyl)benzo Triazoles are composed at a mass ratio of 1:0.2. The hindered amine UV absorber is UV-770. The antioxidant is composed of hindered phenolic antioxidant and phosphite antioxidant in a mass ratio of 1:1.

[0050] Wherein, the particle size of talcum powder is 400 mesh. The defoamer is an acrylic defoamer. The dispersant is a polymer dispersant. The anti-...

Embodiment 3

[0056] A kind of low-yellowing anti-fading UV primer of the present embodiment consists of the following raw materials in parts by weight:

[0057]

[0058]

[0059] Among them, the photoinitiator is composed of methyl benzoylformate and 2,4,6-trimethylbenzoyl-diphenylphosphine oxide in a mass ratio of 1:0.5.

[0060] Among them, the ultraviolet light absorber is composed of a benzotriazole ultraviolet absorber and a hindered amine ultraviolet absorber in a mass ratio of 1:0.8. Benzotriazole UV absorber consists of 2-(2ˊ-hydroxy-3ˊ,5ˊ-di-tert-phenyl)-5-chlorinated benzotriazole and 2-(2ˊ-hydroxy-5ˊ-methylphenyl)benzo Triazoles are composed at a mass ratio of 1:0.2. The hindered amine UV absorber is composed of UV-770 and UV-622 in a mass ratio of 1:0.3. The antioxidant is a phosphite antioxidant. The antioxidant is a hindered phenolic antioxidant.

[0061] Wherein, the particle size of the talcum powder is 350 mesh. The defoamer is an acrylic defoamer. The dispersa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a low-yellowing material fading prevention UV primer and a preparation method thereof. The UV primer comprises, by weight, hexafunctional aliphatic polyurethane acrylate, organic silicon modified trifunctional aliphatic polyurethane acrylate, bifunctional aliphatic polyurethane acrylate, ethoxylated trimethylolpropane triacrylate, 1, 6-hexanediol diacrylate, a photoinitiator, talcum powder, an ultraviolet light absorber, an antioxidant, a defoaming agent, a dispersing agent and an anti-settling agent according to specific parts. The photoinitiator comprises methyl benzoylformate and 2, 4, 6-trimethylbenzoyl-diphenyl phosphine oxide according to the mass ratio of 1: (0.1-0.5); and the ultraviolet light absorber is composed of a benzotriazole ultraviolet light absorber and a hindered amine ultraviolet light absorber according to the mass ratio of 1: (0.3-0.8). The UV primer has low yellowing, can prevent color fading of dyed wood and has excellent adhesive force, and the defects that the dyed wood is easy to change color and fall off in the production and use processes can be effectively avoided.

Description

technical field [0001] The invention belongs to the technical field of wood ware paints, in particular to a low-yellowing and anti-fading UV primer and a preparation method thereof. Background technique [0002] With the continuous development of wood products, especially wooden furniture, the amount of original wood is also decreasing. Therefore, in the field of wooden furniture, people gradually replace the original wood with technological wood, such as stained wood. [0003] However, stained wood is easy to fade due to ultraviolet radiation during production and use, thereby affecting the quality of stained wood furniture. And UV paint, especially the UV primer that is in direct contact with the surface of the stained wood, needs to be irradiated by an ultraviolet lamp to form a cured film after painting. In this way, when the UV lamp irradiates the UV primer, it will also irradiate the stained wood. surface, making stained wood more susceptible to discoloration. [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D7/00C09D7/48C09D5/00
CPCC08L2201/08C08L2205/025C08L2205/03C09D5/002C09D7/00C09D175/14C09D7/48C08L75/14C08K13/04C08K3/34C08K5/3475C08K5/3435C08K5/524C08K7/26
Inventor 刘海军
Owner 东莞大宝化工制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products