A kind of hydrogen evolution electrocatalyst and its preparation method and application
An electrocatalyst and atomic technology, applied in the direction of electrodes, electrolytic components, electrolytic processes, etc., can solve the problems of poor activity and stability of non-platinum catalysts, complex synthesis of alloy catalysts, and limited improvement of activity, etc., to achieve fewer steps, The effect of mild conditions and excellent hydrogen evolution activity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0032] (1) 1568mg 2-methylimidazole was dissolved in 200ml methanol to obtain solution A; 1320mg hexahydrate zinc nitrate and 22.5mg nonahydrate cobalt nitrate were dissolved in 200ml methanol to obtain solution B; solutions A and B were mixed ultrasonically After 10 minutes, it was transferred to a hydrothermal kettle, and hydrothermally reacted in a blast oven at 120 °C for 6 hours;
[0033] After the hydrothermal reaction, the precipitate formed and settled on the bottom of the inner tank of the hydrothermal kettle. The supernatant liquid was sucked out with a plastic dropper, and the precipitate containing a little supernatant liquid was poured into a centrifuge tube, and then methanol was added to the centrifuge tube. Centrifuged and washed with methanol for three times, and the obtained precipitate was dried in a blast drying oven at 60 °C for 12 h;
[0034] The dried purple powder was poured into a mortar and fully ground, poured into a porcelain boat, placed in a quart...
Embodiment 2
[0043] The difference between this example and Example 1 is: in step 1, 1320 mg of zinc nitrate hexahydrate and 32 mg of cobalt dichloride are dissolved in 200 ml of methanol to obtain solution B.
Embodiment 3
[0045] The difference between this example and Example 1 is: in step (1), 1320 mg of zinc nitrate hexahydrate and 65 mg of cobalt sulfate are dissolved in 200 ml of methanol to obtain solution B.
PUM
Property | Measurement | Unit |
---|---|---|
electric potential / voltage | aaaaa | aaaaa |
electric potential / voltage | aaaaa | aaaaa |
volume | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com