Impact-resistant and wear-resistant composite lining plate and preparation method thereof

An impact-resistant and wear-resistant, composite liner technology, applied in the field of wear-resistant materials, can solve problems such as poor toughness and poor impact resistance, and achieve the effects of good bonding, improved load transmission, and improved toughness

Active Publication Date: 2021-10-29
XIAN UNIV OF TECH +1
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] One object of the present invention is to provide an impact-resistant and wear-resistant composite liner, which solves the problems of poor toughness and poor impact resistance of the existing composite liner

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Impact-resistant and wear-resistant composite lining plate and preparation method thereof
  • Impact-resistant and wear-resistant composite lining plate and preparation method thereof
  • Impact-resistant and wear-resistant composite lining plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The preparation of an impact-resistant and wear-resistant composite liner comprises the following steps:

[0034] Step 1, roll the H08A low carbon steel strip with a width of 5mm and a thickness of 0.08mm into a U-shaped steel strip, mix Ta wire, iron powder and graphite powder evenly, then put the mixture into the U-shaped steel strip, and then put the U-shaped steel strip Steel strip encapsulation and rolling to obtain metal fibers with an outer diameter of 1 mm;

[0035] The mass percentage of Ta wire in the mixture is 82.7%, the mass percentage of iron powder is 12%, and the mass percentage of graphite powder is 5.3%; 5μm;

[0036] Step 2, weave the metal fibers prepared in step 1 into a fiber mesh prefabricated body, and the distance between the fibrous reinforcements in the thickness direction d 1 =3mm, distance between transverse fibrous reinforcements d 2 = 2mm, longitudinal fibrous reinforcement spacing d 3 = 2mm;

[0037] Step 3, using an intermediate fre...

Embodiment 2

[0050] The preparation of an impact-resistant and wear-resistant composite liner comprises the following steps:

[0051] Step 1, roll the H08A low carbon steel strip with a width of 4mm and a thickness of 0.06mm into a U-shaped steel strip, mix Ti wire, iron powder and graphite powder evenly, then put the mixture into the U-shaped steel strip, and then put the U-shaped steel strip Steel strip encapsulation and rolling to obtain metal fibers with an outer diameter of 1.5mm;

[0052] The mass percentage of Ti wire in the mixture is 60.1%, the mass percentage of iron powder is 28.9%, and the mass percentage of graphite powder is 11%; 5μm;

[0053] Step 2, weave the metal fibers prepared in step 1 into a fiber mesh prefabricated body, and the distance between the fibrous reinforcements in the thickness direction d 1 = 3mm, distance d between transverse fibrous reinforcements 2 = 2mm, longitudinal fibrous reinforcement spacing d 3 = 2mm;

[0054] Step 3, using an intermediate ...

Embodiment 3

[0066] The preparation of an impact-resistant and wear-resistant composite liner comprises the following steps:

[0067] Step 1, roll the H08A low carbon steel strip with a width of 6mm and a thickness of 0.1mm into a U-shaped steel strip, mix Nb wire, iron powder and graphite powder evenly, then put the mixture into the U-shaped steel strip, and then put the U-shaped steel strip Steel strip encapsulation and rolling to obtain metal fibers with an outer diameter of 2mm;

[0068] The mass percentage of Nb wire in the mixture is 72.5%, the mass percentage of iron powder is 18.8%, and the mass percentage of graphite powder is 8.7%; 5μm;

[0069] Step 2, weave the metal fibers prepared in step 1 into a fiber mesh prefabricated body, and the distance between the fibrous reinforcements in the thickness direction d 1 = 3mm, distance d between transverse fibrous reinforcements 2 = 3mm, longitudinal fibrous reinforcement spacing d 3 = 3mm;

[0070] Step 3, using an intermediate fr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
widthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an impact-resistant and wear-resistant composite lining plate. The impact-resistant and wear-resistant composite lining plate comprises a composite layer and a high manganese steel layer which are overlapped, wherein the composite layer consists of a fibrous reinforcement body and a high manganese steel matrix; the fibrous reinforcement body comprises a low-carbon steel transition layer, carbide reinforcement phases, high-toughness metal fibers and a steel matrix; the carbide reinforcement phases are distributed around the high-toughness metal fibers; and the low-carbon steel transition layer is positioned on the outermost side of the fibrous reinforcement body. The invention further discloses a preparation method of the impact-resistant and wear-resistant composite lining plate. The prepared impact-resistant and wear-resistant composite lining plate consists of the fibrous reinforcement body, the high-toughness metal fibers and the carbide reinforcement phases for toughening, so that the effects of high modulus and high hardness of the gathered carbide reinforcement phases are exerted, and the strength and the wear resistance of the lining plate are improved; the steel matrix and the high-toughness metal fibers connected in the fibrous reinforcement body can improve the damage tolerance of the lining plate and improve the toughness; and the low-carbon steel transition layer is internally and externally provided with the homogeneous steel matrix, so that the macroscopic interface bonding is excellent, the transfer load can be effectively improved, and the stress is released.

Description

technical field [0001] The invention belongs to the technical field of wear-resistant materials, and relates to an impact-resistant and wear-resistant composite liner and a preparation method thereof. Background technique [0002] Wear-resistant linings are widely used in metallurgy, mining, building materials, chemicals and other industrial fields. With the development of large-scale, high-efficiency and high-speed related equipment, higher requirements are put forward for the performance of lining boards. For example, the liner used in the ball mill is directly subjected to high impact load and strong wear from the grinding body and materials during service, so the liner is required not only to have high strength and good wear resistance, but also to have excellent impact resistance performance. [0003] At present, the preparation technology of the liner is mainly the surface modification technology and the melting and casting composite technology. The surface modifica...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C47/18C22C49/14B32B15/18
CPCC22C47/18C22C49/14B32B15/18
Inventor 钟黎声白海强吕振林武宏许梦婷赵梓源
Owner XIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap