Composition for adjusting temperature of asphalt pavement, preparation method and use thereof

A technology of asphalt pavement and composition, which is applied in the field of thermosetting methacrylic resin-based composition for adjusting the temperature of asphalt pavement and the field of preparation thereof, can solve the problems of poor temperature adjustment function of asphalt pavement and the like, achieves good temperature adjustment function and enhanced temperature Conditioning ability, effect of good adhesion ability

Active Publication Date: 2022-06-17
CHONGQING ZONJO RENEWABLE RESOURCES DEV CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Hollow ceramic microbeads and silica airgel are heat insulating materials, and their temperature regulation function is not good when applied to asphalt pavement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composition for adjusting temperature of asphalt pavement, preparation method and use thereof
  • Composition for adjusting temperature of asphalt pavement, preparation method and use thereof
  • Composition for adjusting temperature of asphalt pavement, preparation method and use thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0046] According to one embodiment of the present invention, component A includes:

[0047]

[0048] Component B

[0049] Component B of the present invention includes a curing agent. In certain embodiments, Component B consists of a curing agent.

[0050] The curing agent can be T-SD50, which can be purchased from Zhejiang Jinzhili Chemical Co., Ltd. The dosage of the curing agent is 5.0-23.0 parts by weight; preferably 8.0-20.0 parts by weight; more preferably 10.0-15.0 parts by weight. According to an embodiment of the present invention, the amount of the curing agent used is 13.6 parts by weight.

[0051]

[0052] The preparation method of the composition for adjusting the temperature of the asphalt pavement of the present invention comprises the following steps:

[0053] (1) stirring the thermosetting methacrylic resin and the solvent at 100-1000r / min for 0.5-5h to obtain the first mixture; (2) mixing the first mixture, rutile titanium dioxide and near-infrared...

Embodiment 1

[0072] The composition for regulating the temperature of asphalt pavement consists of component A and component B:

[0073] Component A consists of the following raw materials:

[0074]

[0075]

[0076] Component B consists of the following raw materials:

[0077] Curing agent 13.6 parts by weight

[0078] The preparation method of component A comprises the steps:

[0079] (1) stirring thermosetting methacrylic resin, butyl acetate, propylene glycol methyl ether acetate, xylene and methyl isobutyl ketone under the condition of 500r / min for 2h to obtain the first mixture;

[0080] (2) stirring the first mixture, rutile titanium dioxide and near-infrared reflective titanium dioxide for 20min under the condition of 1500r / min to obtain the second mixture;

[0081] (3) stirring the second mixture, silica powder, silica microspheres and matting powder for 20min under the condition of 1000r / min to obtain the third mixture;

[0082] (4) The third mixture and the dispersant ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a composition for regulating the temperature of asphalt pavement, a preparation method and application thereof. The composition for adjusting the temperature of asphalt pavement includes component A and component B; wherein, component A includes thermosetting methacrylic resin, solvent, rutile titanium dioxide, near-infrared reflective titanium dioxide, silica powder, and silica microspheres , matting powder and dispersant; wherein, component B includes: curing agent. The composition for adjusting the temperature of the asphalt pavement has a good temperature regulating function on the asphalt pavement.

Description

technical field [0001] The present invention relates to a composition for adjusting the temperature of asphalt pavement, its preparation method and use, in particular to a thermosetting methacrylic resin-based composition for adjusting the temperature of asphalt pavement, its preparation method and use. Background technique [0002] Asphalt pavement has good flatness, driving comfort and noise reduction ability, so it is widely used in various high-grade pavements. Asphalt is an endothermic material, which absorbs a wide range of wavelengths of solar radiation, and a large amount of heat accumulates in the asphalt surface layer, which increases the temperature of the road surface. This high temperature environment can easily lead to the urban "heat island effect", which seriously affects the atmospheric temperature. Therefore, there is an urgent need to develop a composition for adjusting the temperature of asphalt pavement that not only satisfies the temperature adjustment...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/00C09D7/61E01C7/35E01C11/24
CPCC09D133/00C09D7/61E01C7/35E01C11/24C08K2003/2241C08K3/22C08K3/36C08K7/18C08K13/04
Inventor 达瓦扎西陈先勇战琦琦田浩袁秀香杜姣姣谢磊李亚张明明
Owner CHONGQING ZONJO RENEWABLE RESOURCES DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com