Chromium-free passivation method for zinc powder

A technology of chromium-free passivation and zinc powder, applied in metal material coating technology, photovoltaic power generation, etc., can solve the problem of losing anti-rust pigments, etc., achieve good stability, unaffected electrochemical performance, and low environmental equipment requirements Effect

Pending Publication Date: 2022-06-07
上海库曜新材料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method makes the zinc powder completely

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chromium-free passivation method for zinc powder
  • Chromium-free passivation method for zinc powder
  • Chromium-free passivation method for zinc powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-15

[0045] Embodiment 1-15 relates to a kind of zinc powder passivation method, specifically comprises the steps:

[0046] S1. Add the general dispersing aid for water and oil into the water-soluble organic solvent, and stir evenly;

[0047] S2. Add zinc powder to the medium mixed evenly in step S1, and stir evenly;

[0048] S3. Add deionized water, molybdenum-containing compound, and silver hexafluoroantimonate into the uniformly mixed medium in step S2, and stir uniformly to prepare a passivated water-based zinc paste.

[0049] Wherein, after uniform stirring in step S2, in order to ensure uniform mixing, secondary stirring is performed for 20-90 minutes.

[0050] After the stirring is uniform in step S3, in order to ensure uniform mixing, secondary stirring is performed for 20-90 minutes. An aqueous zinc paste was prepared.

[0051]The substances and process parameters involved in the zinc powder passivation method of Examples 1-15 of the present invention are shown in Table...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a chromium-free passivation method for zinc powder. The preparation method comprises the following steps: adding a dispersing aid universal for water and oil into a water-soluble organic solvent, and uniformly stirring; adding zinc powder into the uniformly mixed medium, and uniformly stirring; and adding deionized water, a molybdenum-containing compound and silver hexafluoroantimonate, and uniformly stirring to obtain the passivated water-based zinc paste. According to a traditional zinc powder passivation method, zinc powder can be completely wrapped, so that the zinc powder loses the effect of an anti-rust pigment. According to the chromium-free passivation method for the zinc powder, the zinc powder can be stably stored in water for more than 6 months, and the electrochemical protection function of the zinc powder is not lost.

Description

technical field [0001] The invention relates to a chromium-free passivation technology for zinc powder; in particular, it relates to a chromium-free passivation technology for zinc powder, which can not only make zinc powder stably stored in water for more than 6 months, but also keep the electrochemical protection function of zinc powder not lost. method. Background technique [0002] At present, zinc-rich coatings on the market, as heavy-duty anti-corrosion coatings, have anti-corrosion properties unmatched by other coatings. However, since the zinc powder in the zinc-rich paint will react with water, this greatly affects the water-based nature of the zinc-rich paint. [0003] Water-based zinc-rich coatings on the market today are usually two-component, and zinc powder and another water-based component are temporarily mixed when used. This often results in short pot life, difficult field operations and high VOCs. [0004] Chinese patent CN104356938B discloses a chromium...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C22/42C23C22/44
CPCC23C22/44C23C22/42Y02E10/50
Inventor 姚下银王国强
Owner 上海库曜新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap