Al-Ca-Fe alloy contg. trace carbon, low slilicon, low phosphorus, low sulphur used for steelmaking
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A low-carbon, low-silicon, and alloy technology, which is applied in the ferroalloy field for steelmaking in the metallurgical field, can solve problems such as poor final deoxidation effect, achieve good deoxidation and desulfurization effects, improve deoxidation, and high yield
Active Publication Date: 2006-09-13
本溪冶炼集团有限公司
View PDF0 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] In view of the above-mentioned deficiencies, the purpose of the present invention is to provide a kind of Al-Ca-Fe alloy with low carbon, low silicon, low phosphorus and low sulfur for steelmaking, so as to solve the problem of poor final deoxidation effect existing in the prior art. Problem, as a final deoxidizer for steelmaking, it does not need to refine the steel, improves the quality of the steel, and reduces the cost. It is suitable for smelting steel types that require Als and low C, low P, and low S.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0025] Embodiment 1 (percentage by weight)
[0026] Al 55, Ca 10, C 0.019, Si 0.9, P 0.018, S 0.019, Fe balance.
[0027] Use the above alloy as the final deoxidizer of AH32, and add the alloys: Mn-Fe, Si-Fe, Si-Mn when the molten steel reaches 1 / 4 of the large tank, and the order of addition is weak, medium and strong, and finally add the final deoxidizer Al-Ca-Fe alloy must be added when the molten steel reaches 3 / 4 of the large tank. The slag-stopping must be achieved, and the tap hole must be large. The deoxidizer has a good deoxidation degree, a good steel refining rate, a good steel quality, and mechanical properties that meet the requirements of the national standard.
[0028]
[0029]
[0030] In the above table, d represents the diameter of the bending center, and a represents the thickness of the sample.
Embodiment 2
[0032] Difference with embodiment 1 is: (percentage by weight)
[0033] Al 58, Ca 5, C 0.017, Si 0.8, P 0.016, S 0.017, Fe balance.
Embodiment 3
[0035] Difference with embodiment 1 is: (percentage by weight)
[0036] Al 60, Ca 15, C 0.014, Si 0.6, P 0.015, S 0.014, Fe balance.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a micro low carbon, low silicon, low phosphor, and low sulfur Al-Ca-Fe alloy used in steel-making. It uses as deoxidizer and contains 20-85wt% Al, 1-20wt% Ca, C less than 0.02wt%, Si less than 1.0wt%, P less than 0.02wt%, S less than 0.02wt%, the rest is Fe. It is smelted from line frequency furnace. The invention has the advantage of easy to use, stable, and could improve the recovery factor of the metal element. The molten steel treated by the deoxidizer has good fluidity, high work rates, high benefits, etc. The deoxidizer could discharge the impurity, and it has good mechanical behavior, good quality, long useful life and good social benefit.
Description
technical field [0001] The invention relates to an iron alloy for steelmaking in the field of metallurgy, in particular to a slightly low-carbon, low-silicon, low-phosphorus and low-sulfur Al-Ca-Fe alloy for steelmaking. Background technique [0002] The rapid development of all walks of life requires the quality of steel to be better and better, and the service life to be longer. Relatively speaking, it is required that the final deoxidizer used in steelmaking must meet the needs of steelmaking, and develop in the direction of micro-low carbon, low silicon, low phosphorus, and low sulfur. [0003] In the past, ferromanganese was used for smelting boiling steel, and finally Al ingot was used for final deoxidation. Ferrosilicon, ferromanganese, and silicomanganese were used for smelting killed steel, and Al ingot was used for final deoxidation. Due to the light specific gravity of aluminum, low melting point, and easy burning loss, the yield of aluminum deoxidation is low, w...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more