Manufacture method of linear low density polyethylene lawn-shape ground cushion

A linear low density, polyethylene technology for use in the direction of household components, applications, home appliances

Inactive Publication Date: 2007-03-14
付博 +1
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the problems existing in the existing mat preparation methods, the present

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacture method of linear low density polyethylene lawn-shape ground cushion
  • Manufacture method of linear low density polyethylene lawn-shape ground cushion
  • Manufacture method of linear low density polyethylene lawn-shape ground cushion

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The linear low-density polyethylene (LLDPE, 7047) is used as raw material, and industrial pigment (reduced bright green FFB) is added, and the added amount accounts for 0.8% of the linear low-density polyethylene (LLDPE) according to the weight percentage.

[0028] The processing steps are as follows:

[0029] The raw materials are stirred, and the raw materials are respectively added into a high-speed mixer, stirred and mixed, and the stirring speed is 5000 rpm, and the time is 50 minutes.

[0030] High temperature and high pressure injection molding. Put the mixed raw materials into a high-temperature and high-pressure injection molding machine, and perform injection molding at a temperature of 180° C. and a pressure of 2 MPa.

[0031] Injection molding. The injection molding material is added to the mold cast according to the shape of the product, and is shaped by the mold.

[0032] Composite, bonding non-woven fabric and heat-resistant non-slip mesh on the bottom...

Embodiment 2

[0037] The linear low-density polyethylene (LLDPE, 7540) is used as raw material, and industrial pigment (reduced olive green B) is added, and the added amount accounts for 0.01% of the linear low-density polyethylene (LLDPE) according to the weight percentage.

[0038] The processing steps are as follows:

[0039] The raw materials are stirred, and the raw materials are respectively added into a high-speed mixer, stirred and mixed, and the stirring speed is 1000 rpm, and the time is 150 minutes.

[0040] High temperature and high pressure injection molding. Put the mixed raw materials into a high-temperature and high-pressure injection molding machine, and perform injection molding at a temperature of 170° C. and a pressure of 0.5 MPa.

[0041] Injection molding. The injection molding material is added to the mold cast according to the shape of the product, and is shaped by the mold.

[0042] Composite, bonding non-woven fabric and heat-resistant non-slip mesh on the botto...

Embodiment 3

[0047] The linear low-density polyethylene (LLDPE, 7042) is used as a raw material, and an industrial pigment (phthalocyanine green G) is added, and the added amount accounts for 2% of the linear low-density polyethylene (LLDPE) according to the weight percentage.

[0048] The processing steps are as follows:

[0049] The raw materials are stirred, and the raw materials are respectively added into a high-speed mixer, and stirred and mixed at a stirring rate of 10000 rpm for 5 minutes.

[0050] High temperature and high pressure injection molding. Put the mixed raw materials into a high-temperature and high-pressure injection molding machine, and inject them under the conditions of a temperature of 190° C. and a pressure of 5 MPa.

[0051] Injection molding. The injection molding material is added to the mold cast according to the shape of the product, and is shaped by the mold.

[0052] Composite, bonding non-woven fabric and heat-resistant non-slip mesh on the bottom surfa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for producing linear low-density polythene grass pad. Wherein, it uses linear low-density polythene grass pad as material, uses industrial dope; and the production comprises that mixing materials, injecting at high temperature and high pressure, combining, demoulding, finishing, coiling and packing. And the invention uses environment friend material, without toxicity and irritant odor. And it has long service life and can be recycled.

Description

technical field [0001] The invention relates to a method for preparing floor mats for removing dust and dirt on shoe soles at doors, or for places with water such as bathrooms, in particular to a method for preparing lawn-shaped linear low-density polyethylene mats. Background technique [0002] In daily life, the commonly used plastic floor mat materials are polyvinyl chloride (pvc). According to the information currently available, polyvinyl chloride is a polymer called vinyl chloride chemical substance. Vinyl chloride itself is harmful to the human body. Although its polymer, polyvinyl chloride, is harmless in principle, any chemical substance The polymerization of PVC is not complete, so a certain amount of vinyl chloride is not completely polymerized, but it cannot be separated from it. These unpolymerized vinyl chloride is the "culprit" of carcinogenicity in PVC materials. [0003] At the same time, since PVC itself is relatively hard, plasticizers are generally added...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C69/00B29C45/76B29C65/00B29B7/28C08J3/20C08L23/06B29K23/00B29L31/58
Inventor 付辉
Owner 付博
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap