Translucent veneering for a dental prosthesis formed by a press to metal process

Abstract

A dental prosthesis, typically formed in a press to metal process, includes application of a porcelain composition sufficient to form a veneer on a dental prosthesis supporting metal structure, the composition having an integrated tooth-like translucency providing an aesthetic appearance. The composition is formed of a dentin frit and an enamel frit, typically sintered into a desired ingot shape including an amount of composition sufficient to veneer the prosthesis. The porcelain composition is a component of a kit that includes opaquers, other porcelains and stains useful in finishing to provide an aesthetic prosthesis.

Description

FIELD OF THE INVENTION [0001] The invention relates to dental prostheses comprising porcelain fused to a metal supporting structure or coping. Particularly, the invention relates to prostheses made by pressing a heated ceramic material into a mold onto said coping, wherein the mold is typically made by the lost wax process. BACKGROUND OF THE INVENTION [0002] A majority of crown and bridge restorations of teeth continue to be porcelain fused to a metal supporting structure or coping that provides strength for the prosthesis. While “all-ceramic” prostheses are of increasing importance, porcelain fused to metal (PFM) remains cost effective and provides satisfactory aesthetics. [0003] Since the metal substructures used in these restorations are not naturally tooth colored, esthetic veneering porcelains are applied that mimic the color and form of natural teeth. The veneering process plays a critical role in providing a satisfactory restoration. Typically the process of making a PFM rest...

AI Technical Summary

Benefits of technology

[0006] It is an object of the present invention to provide porcelain materials and processing methods wherein skilled, intensive, and costly hand layering is further reduced.

[0007] The invention is a dental prosthesis that includes a metal coping for supporting said prosthesis on tooth surfaces to be repaired. The metal coping is provided with an opaque layer that covers surfaces of the coping that would interfere with achieving an acceptable tooth-like appearance of the finished PFM. The opaque layer may be formed from a mixture of frits in powder or paste form and applied by spraying, a slurry dip, electrodeposit, or other forms or methods known to those skilled in the art. A porcelain layer, having an optimized, integrated translucency that blends dentin and enamel shades is fused to said opaqued surface by pressing the porcelain material onto said coping contained in a mold at fusing temperatures. The result is a strong and tough dental crown or bridge substructure that is veneered with porcelain having an integrated transparency, blending dentin and enamel character, such that further hand layering processes are eliminated or greatly reduced.

Problems solved by technology

Achieving consistent, aesthetic results is time consuming and adds significant cost to the final product, as well as requiring people who have a scarce skill and necessary experience.

However, a remaining difficulty has been that the initial pressing must still often be followed by a hand layering with enamel porcelain, particularly to develop incisal edge translucency.