Aviation aluminum alloy pre-stretching plate and production method thereof

A production method and pre-stretching technology are applied in the field of aluminum alloy pre-stretched sheet and its production, which can solve the problems of deformation processing yield of aluminum alloy sheet and other problems.

Active Publication Date: 2007-09-19
NORTHEAST LIGHT ALLOY CO LTD
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims to solve the problems that existing aluminum alloy plates are easily deformed and the processing yield is low after machining

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0004] Specific Embodiment 1: In this embodiment, the aluminum alloy pre-stretched sheet for aviation is composed of 0.20 parts of Si, 0.20 parts of Fe, 4.2 parts of Cu, 0.70 parts of Mn, 1.5 parts of Mg, and 0.6 parts by weight. Ni, 0.1 parts of Zn, 0.10 parts of Ti and the rest of Al, totaling 100 parts.

specific Embodiment approach 2

[0005] Specific embodiment two: the production method of aviation aluminum alloy pre-stretched plate in this embodiment is realized through the following steps: 1. According to the ratio of parts by weight, 0.20 parts of Si, 0.20 parts of Fe, 4.2 parts of Cu, 0.70 parts of Mn, 1.5 parts of Mg, 0.6 parts of Ni, 0.1 parts of Zn, 0.10 parts of Ti and the rest of Al are fully mixed, and the total is 100 parts; 2. The conditions of mixing the mixed metals at 700-750 ° C Smelting under high temperature for 5-12 hours, then casting the smelted metal at a temperature of 690-710°C and a casting speed of 90-95mm / min, and casting the metal into an ingot with a cross-sectional size of 255×1500mm; 3. Soak the ingot at a temperature of 490-500°C for 18-20 hours, and then plan, saw and mill the soaked ingot in a conventional way according to actual needs; 4. At 400-430 Under the temperature of ℃, according to the actual needs, the thickness of the ingot is hot-rolled, and the length of the w...

specific Embodiment approach 3

[0006] Embodiment 3: The difference between this embodiment and Embodiment 2 is that in Step 2, the mixed metals are smelted at 720-740° C. for 6-10 hours. Other steps are the same as in the second embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to aluminium alloy pretensioning plates for aviation and a method for producing the same in order to solve the problem that the existing aluminium alloy plates are easy to be deformed in the machining and machining yield is low. The aliminium alloy pretensioning plates for aviation comprise, based on weight shares, Si of 0.20, Fe of 0.2, Cu of 4.2, Mn of 0.70, Mg of 1.5, Ni of 0.6, Zn of 0.1, Ti of 0.1, and the residuel of Al, the total of 100. The method for producing the aliminium alloy pretensioning plates for aviation includes the steps of : 1) admixture; 2) casting; 3) soak heating treat; 4) heating, hot rolling and cutting; 5) quenching, straightening, and pretensioning, sawing the plates according to the requirement of the product to produce aliminium alloy pretensioning plates for aviation. The plates product of the invention has steady properties, and the plates can not be deformed in machining, while the machining yield can be improved.

Description

technical field [0001] The invention relates to an aluminum alloy pre-stretched plate and a production method thereof. Background technique [0002] The aluminum alloy sheet for aviation requires that the deformation of the sheet is low after machining. The speed is inconsistent, there is a cooling gradient, the surface layer of the plate is subject to additional compressive stress, and the neutral layer is subject to additional tensile stress, resulting in residual stress in the plate, resulting in processing deformation when the plate in the finished state is machined, affecting the quality of the parts The appearance shape and size increase the cost and reduce the processing yield. Contents of the invention [0003] The invention aims to solve the problems that the existing aluminum alloy plates are easily deformed and the processing yield is low after machining. The aluminum alloy pre-stretched sheet for aviation is composed of 0.20 parts of Si, 0.20 parts of Fe, 4.2...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/12C22C1/02B22D21/04B21B37/74C22F1/057
Inventor 赵永军谢延翠王学书马英义陶志民
Owner NORTHEAST LIGHT ALLOY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com