Sound absorption ceramic panel using kitchen waste as raw material and preparation method thereof

A technology of ceramicizing kitchen waste, which is applied in the field of sound-absorbing ceramic plates and its preparation, can solve the problems of clogged drainage pipes, generation of sewage and odor, and reduction of drainage capacity of urban sewers, etc., and achieves the effect of simple process and low cost

Inactive Publication Date: 2007-10-17
ZHEJIANG SCI-TECH UNIV
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The crushing and direct discharge method is only suitable for units with a small output of kitchen waste. It is easy to generate sewage and odor during treatment, which breeds germs, mosquitoes and flies, and causes the spread of diseases. The condensation of oil into blocks will cause blockage of drain pipes and reduce the drainage of urban sewers. ability
The cost of biological treatment is high, and it is not suitable for the treatment of moldy, severely deteriorated and chemically polluted kitchen waste, so as not to contaminate downstream products
The kitchen waste made into feed cannot deteriorate, and it is necessary to classify the kitchen waste. Since the kitchen waste is mixed with various impurities (table paper, chopsticks, disposable tablecloths, etc.), sorting is difficult
In short, the existing kitchen waste treatment technology has its limitations, and the degree of resource utilization is not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] 1) Take 500g of kitchen waste and put it in a constant temperature drying oven after cutting, mixing and simple treatment, and keep it at 105±1°C for 10 hours. After the kitchen waste is dried, it is crushed into a size of 3-5mm.

[0019] 2) Put the dried garbage in a ceramic cup and carbonize it in a high-temperature nitrogen protection furnace. Keep the furnace pressure at 0.10-0.15MPa, start heating from room temperature, control the temperature rise rate at 2°C / min, keep it for 20 minutes when the temperature rises to 120°C, then raise the temperature to 600°C at 1°C / min, and keep at 600°C for 80 minutes minute. Finally, let it cool down to room temperature naturally to make porous carbonized material.

[0020] 3) Grinding the charcoal into a size of 1-2 mm, then mixing 40% of the porous charcoal, 10% of stearic acid, 25% of PVC (polyvinyl chloride) resin powder, and 25% of epoxy vinyl resin, and then uniformly stirred and ultrasonically Vortex to mix the mixture...

Embodiment 2

[0022] 1) Take 500g of kitchen waste, shred it, mix it briefly, put it in a constant temperature drying oven, and keep it at 105±1°C for 11 hours. After the kitchen waste is dried, it is crushed into a size of 3-5mm.

[0023] 2) Put the dried garbage in a ceramic cup and carbonize it in a high-temperature nitrogen protection furnace. Keep the furnace pressure at 0.10-0.15MPa, start heating from room temperature, control the heating rate at 3°C / min, keep it for 15 minutes when the temperature rises to 140°C, then raise the temperature to 700°C at 1.6°C / min, and keep at 700°C for 70 minutes minute. Finally, let it cool down to room temperature naturally to make porous carbonized material.

[0024] 3) Grinding the charcoal into a size of 1-2 mm, then mixing 30% of the porous charcoal, 30% of stearic acid, 20% of PVC resin powder, and 20% of epoxy vinyl resin, and thoroughly mixing the mixture through uniform stirring and ultrasonic vibration . After the vibration is over, pla...

Embodiment 3

[0026] 1) Take 500g of kitchen waste, shred it, mix it briefly, put it in a constant temperature drying oven, and keep it at (105±1)°C for 12 hours. After the kitchen waste is dried, it is crushed into a size of 3-5mm.

[0027] 2) Put the dried garbage in a ceramic cup and carbonize it in a high-temperature nitrogen protection furnace. Keep the furnace pressure at 0.10-0.15MPa, start heating from room temperature, control the heating rate at 2.5°C / min, keep it for 17min when the temperature rises to 150°C, then raise the temperature to 800°C at 2°C / min, and keep at 800°C for 60 minutes minute. Finally, let it cool down to room temperature naturally to make porous carbonized material.

[0028] 3) Grinding the charcoal into a size of 1-2 mm, then mixing 35% of the porous charcoal, 20% of stearic acid, 22% of PVC resin powder, and 23% of epoxy vinyl resin, and the mixture is fully mixed through uniform stirring and ultrasonic vibration . After the vibration is over, place the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a sound-absorbing ceramic plate using kitchen waste as raw material and preparation method thereof. Through a drying process, organic matter of kitchen solid waste ecological material are used as raw material, charring in a high temperature nitrogen protective stove to form porosint. Smashing charring matter then adding with pore forming agent such as eleaostearic acid, oxene resin and PVC resin powder, the mixture is mixed fully through uniform stirring and supersonic wave oscillation. After oscillation, the mixture material is filled in a molding cavity under pressure, then putting into an oven to cure; a sound-absorbing ceramic plate is got after natural cooling. The preparation technology of the invention is simple, has low cost, raw material is kitchen waste, can get harmless rubbish with decrement, resource treatment when getting sound-absorbing ceramic plates. The sound-absorbing ceramic plate can be applied to construction business and decoration field.

Description

technical field [0001] The invention relates to solid waste treatment, in particular to a sound-absorbing ceramic plate made of kitchen waste and a preparation method thereof. Background technique [0002] In today's society, environmental problems are becoming more and more prominent, and the problem of resource shortage is also becoming more and more serious. How to turn waste into wealth and recycle resources has attracted the attention of all walks of life. [0003] Kitchen waste includes various organic wastes such as leftovers, leftovers, vegetable leaves, fruit peels and packaging bags, which account for about 30% to 40% of domestic waste. Kitchen waste is rich in nutrients and used to be a good feed for pigs, but it is likely to contain pathogenic microorganisms if it is not treated. After the publication of the document "Forbidden to use swill to feed pigs", the utilization of resources has become the key. [0004] At present, the main treatment methods of kitche...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/10C04B14/00
Inventor 冯新星陈建勇唐宗留刘平峰夏年鑫阮斐斐郭玉海张华鹏
Owner ZHEJIANG SCI-TECH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap