Paper-making-stage bamboo wood pulp plate denaturalization producing technique

A production process and paper-making-grade technology, applied in the field of dissolving-grade viscose fiber pulp, can solve problems such as severe conditions, slow dissolution of hemicellulose, and difficulty in reducing polymerization, so as to increase the content of methylcellulose, reduce production costs, and reduce pollution Effect

Active Publication Date: 2008-03-26
YIBIN GRACE GROUP CO LTD
View PDF2 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] The technical problem to be solved by the present invention is that the above-mentioned existing denatured wood pulp production process has uneven impregnation of wood pulp board, slow dissolution of hemicellulose, difficulty in depolymerization, uneven cooking, single cooking method, single bleaching method and conditions. Serious and other deficiencies, provide a method for producing soluble wood pulp for viscose fiber with insoluble papermaking grade wood pulp board, especially for the denaturation production process of papermaking grade bamboo wood pulp board

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Embodiment 1: sulfite method one

[0044] 1. Use 6000Kg of paper-making grade bamboo wood pulp board, and paginate through the pagination machine.

[0045]2. Dipping into 4.0% pulp porridge with 14% NaOH.

[0046] 3. Use the porridge pump to send it into the press to squeeze and loosen the dispersed fibers.

[0047] 4. Put the squeezed wood pulp into the digester for cooking. The process conditions are: (1) Cooking agent: Na 2 SO 3 +NaOH, the total acid content of the cooking liquid is 7.5%, and the liquid ratio is 1:4.0; (2) The initial temperature of the cooking liquid is ≥40°C; (3) Preheating for 10-15 minutes to 105±5°C; (4) After the steam is stopped Then run dry for 25-30 minutes; (5) Use 3 times of small steam release and 4 times of heating curve, and the total heating time is 2 hours; (6) The holding temperature is 160±2°C.

[0048] 5. Send the above-mentioned wood pulp slurry obtained by cooking from the dumping tank to extrusion washing to extract the yell...

Embodiment 2

[0052] Embodiment 2: sulfite method two

[0053] 1. Use 6000Kg of paper-making grade bamboo wood pulp board, and paginate through the pagination machine.

[0054] 2. Dipping into 2.5% pulp porridge with 11% NaOH.

[0055] 3. Use the porridge pump to send it into the press to squeeze and loosen the dispersed fibers.

[0056] 4. Put the squeezed wood pulp into the digester for cooking. The process conditions are: (1) Cooking agent: Na 2 SO 3 +NaOH, the total acid content of the cooking liquid is 5%, and the liquid ratio is 1:4.0; (2) The initial temperature of the cooking liquid is ≥40°C; (3) Preheating for 10-15 minutes to 105±5°C; (4) After the steam is stopped Then run dry for 25-30 minutes; (5) adopt 2 times of small steam release and 3 times of heating curve, and the total heating time is 2 hours; (6) The holding temperature is 170±2°C.

[0057] 5. Send the above-mentioned wood pulp slurry obtained by cooking from the dumping tank to extrusion washing to extract the yel...

Embodiment 3

[0061] Embodiment 3: sulfite method three

[0062] 1. Use 6000Kg of paper-making grade bamboo wood pulp board, and paginate through the pagination machine.

[0063] 2. Dipping into 3.5% pulp porridge with 9% NaOH.

[0064] 3. Use the porridge pump to send it into the press to squeeze and loosen the dispersed fibers.

[0065] 4. Put the squeezed wood pulp into the digester for cooking. The process conditions are: (1) Cooking agent: Na 2 SO 3 +NaOH, the total acid content of the cooking liquid is 8%, and the liquid ratio is 1:4.0; (2) The initial temperature of the cooking liquid is ≥40°C; (3) Preheating for 10-15 minutes to 105±5°C; (4) After the steam is stopped Then run dry for 25-30 minutes; (5) adopt 2 times of small steam release and 3 times of heating curve, and the total heating time is 2 hours; (6) The holding temperature is 155±2°C.

[0066] 5. Send the above-mentioned wood pulp slurry obtained by cooking from the dumping tank to extrusion washing to extract the ye...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention provides denaturating production process of paper-making bamboo pulp sheet pulp superior to available denaturated wood pulp sheet producing process. The denaturating production process includes the following steps: paging paper-making bamboo pulp sheet in a paging device, alkali dipping in 6-18 % concentration alkali solution in a dip vat to form 2.5-5 % concentration pulp, extruding in a extrude, debonding fiber, digesting, washing, depurating, bleaching, washing for the second time, and fishing pulp. The process can obtain high quality wood pulp of soluble viscose fiber stably and has wide material source.

Description

technical field [0001] The invention relates to a production method for denaturing paper-making grade bamboo wood pulp board into dissolving grade viscose fiber pulp. Background technique [0002] With the development of my country's viscose fiber industry, domestic enterprises mostly use cotton pulp as the raw material for the production of viscose fiber. The resource of raw cotton linters is increasingly in short supply due to the constraints of planting area and growth cycle. Prominent, the impact of long cycle and ecological balance has seriously restricted the development of my country's viscose fiber industry. For this reason, some enterprises have used dissolving wood pulp for viscose production, but the price of imported dissolving wood pulp is high and fluctuating, which affects the normal operation and economic benefits of the enterprise. Finding a substitute for dissolving wood pulp is an important task for enterprises . [0003] At present, my country produces a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21C3/00D21B1/12D21C1/06D21C7/00D21C3/02D21C3/04D21C9/02D21C9/08D21C9/12D21C9/16D21F13/00
Inventor 冯涛邓传东孙毅薛勤徐发祥饶芳秋宋伟柳永权黄俊
Owner YIBIN GRACE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap