Chromatic bituminous cement and preparation method thereof

A technology of colored asphalt and binder, which is applied in the field of asphalt binder, which can solve the problems of high energy consumption, limitation of high temperature stability of colored asphalt binder, and difficulty in construction

Inactive Publication Date: 2008-06-25
SHANGHAI QUNKANG ASPHALTUM TECH CO LTD
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

A notable defect disclosed in the above-mentioned patent is that it needs to be heated to an extremely high temperature during specific construction, which not only requires a large amount of energy consumption, but also pollutes the environment, makes construction difficu...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chromatic bituminous cement and preparation method thereof
  • Chromatic bituminous cement and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～6

[0018] Raw materials used:

[0019] Refined lubricating oil, viscosity at 40°C: 3.5Pa.S, flash point: 335°C, aromatic content: 68wt%, density at 15°C: 0.98g / cm3

[0020] Petroleum resin, produced by Korea Kolon Company, trade name: Hikotack P140, softening point 145°C, average molecular weight (GPC method) 2200

[0021] Polyethylene wax, molecular weight 3000-6000, softening point 120-150℃

[0022] SBR, the grade produced by Qilu Petrochemical is 1502

[0023] Heat the extracted lubricating oil to 175°C, then add petroleum resin, polyethylene wax and SBR, and stir with a stirrer at a speed of 200 rpm for 60 minutes to prepare the finished colored asphalt binder. The specific composition ratio (percentage by weight), and the performance results of the binder and the mixture tested by the testing method specified in the JTJ052-2000 standard "Testing Procedures for Asphalt and Asphalt Mixtures in Highway Engineering" of the Ministry of Communications of China are shown in Table...

Embodiment 4

[0030] The colored asphalt cement and aggregates are mixed into Marshall specimens and rut specimens to form, among which the stones above 2.36mm are made of diabase, and the stones of 2.36mm-0.075mm are made of quartzite, and the following gradation is adopted:

[0031]

[0032]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Flash pointaaaaaaaaaa
Densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a colorful asphalt binder. The component of the colorful asphalt binder of the invention calculated by weight percentage comprises that: 20 per cent-65 per cent of petroleum resin, 30 per cent -79 per cent of lubricant refined extract oil and 1 per cent -5 per cent of polyethylene wax. By pulling a little of polyethylene wax into conventional colorful asphalt binder, temperature of mixing, spreading and rolling of asphalt mixture can be greatly reduced and negative influence on final colorful asphalt pavement is not caused. As the polyethylene wax is added, a reasonably low construction temperature can be obtained, which allows an easy construction. At the same time, the lowering of construction temperature decreases correspondingly the odor emitted by the asphalt binder, which is in favor of environmental protection. Simultaneously, the adding of SBR allows the colorful asphalt binder to be provided with a better high-temperature stability.

Description

technical field [0001] The invention relates to an asphalt binder, in particular to a binder for colored asphalt. Background technique [0002] The mechanical properties and rheological properties of colored asphalt binder are the same as those of general road heavy traffic asphalt. The main principle of colored asphalt binder pavement is to use colored asphalt binder and add various pigments to make it have various required colors. At the same time, by using colored stones or light-colored stones, it can have a longer-lasting color effect. A good colored asphalt binder should meet the following three requirements: [0003] Colored asphalt binder has good performance and should try to meet the requirements of heavy traffic asphalt or even modified asphalt; it has good anti-rutting performance and good water damage resistance. [0004] At present, there have been many patents and documents disclosing their own colored asphalt binders, some of which have been industrialized, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L95/00C08L57/02C08L23/12
Inventor 黄子章
Owner SHANGHAI QUNKANG ASPHALTUM TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap