A kind of manufacturing method of ceramic massager

A production method and massager technology, which can be applied in the direction of pressure reflection point instruments, etc., can solve the problems of easy to produce dry feeling, adverse effects on the skin, insufficient lubricity, etc., and achieve the effects of strong greasy feeling, large heat capacity, and cost reduction.

Inactive Publication Date: 2011-12-21
潮州宏业陶瓷制作厂有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these ceramic massagers all have some common shortcomings, mainly made of ordinary ceramic materials, the product has high hardness and insufficient smoothness, and it is easy to produce a dry feeling when it is in contact with the human body, which will cause adverse effects on human skin.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of manufacturing method of ceramic massager
  • A kind of manufacturing method of ceramic massager
  • A kind of manufacturing method of ceramic massager

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] Below by example, in conjunction with accompanying drawing, can do further understanding to the present invention.

[0018] A method for manufacturing a ceramic massager, the method comprising the steps in the following order:

[0019] 1. Selection of porcelain clay, its main components are as follows: 70% talcum powder, 10% feldspar, 8% black clay, 5% kaolin washing mud, 3% quartz powder and 4% marble powder.

[0020] 2. Production of billet: The raw materials of the billet are weighed and mixed according to the above-mentioned formula design, and then ball milled for 22 hours with the ratio of material, ball and water: 1:1.6:0.7, and then sieved with a multi-hole sieve, the fineness The sieve residue is 0.3%. After the iron removal process, it will be stale for 7 days.

[0021] 3. Grouting molding: According to the structural characteristics of the human body and the characteristics of meridians, the product is designed so that the top surface protrudes into a turtle...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for manufacturing a ceramic massager. The ceramic massager manufactured by the method is light in weight, high in slipperiness, good in hand feeling, does not produce dry feeling when massaged for a long time, and can be effective for a long time after being heated or frozen. Massage is beneficial to the human body to invigorate water and dampness, clear away heat and relieve summer heat. The invention is realized through the following technical scheme: the formula of the product body includes talcum powder, feldspar, black clay, kaolin washing mud, quartz powder and marble powder. The product glaze formula includes feldspar, talc powder, quartz powder, marble powder, spodumene powder and kaolin clay. The production process of the product includes the combination of various components of the green body raw materials, ball milling, sieving, iron removal, aging, grouting molding, trimming, biscuit firing, grinding, glazing, placing on a special support, and firing in a kiln to complete the ceramic massager. .

Description

technical field [0001] The invention relates to a manufacturing method of a physiotherapy product, more specifically, a manufacturing method of a ceramic massager. Background technique [0002] Ceramic products have the advantages of wear resistance, corrosion resistance, high insulation, easy cleaning, easy production, and low price. They are ideal materials for making human health physiotherapy massagers. At present, there are many kinds of ceramic massagers on the market, such as known foot ceramic massagers, hand, foot and heart ceramic massagers or the like. But these ceramic massagers all have some common shortcomings, mainly are made of common ceramic material, and product hardness is higher, and smoothness is not enough, and easily produces dry feeling when rubbing with human body, causes adverse effect to human skin. Contents of the invention [0003] The purpose of the present invention is to overcome the deficiencies in the prior art, and use the principles of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): C04B35/20C04B35/622A61H39/04
Inventor李耀钦
Owner潮州宏业陶瓷制作厂有限公司