Matte glaze and production process thereof

A production process and technology of matte glaze, applied in the field of ceramics, can solve the problems of complex components of matte glaze, long firing time and high production cost, and achieve the effects of bright and stable color, short firing time and low production cost

Inactive Publication Date: 2019-06-18
福建省德化县哈维陶瓷有限公司
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Based on the above prior art, the purpose of the present invention is to provide a matt glaze and its manufacturing process to solve the problems of complex components, long firing time, high temperature and high production cost of the existing matt glaze to a certain extent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A matt glaze, comprising the following components in parts by mass: 28 parts of kaolin, 15 parts of clay, 10 parts of borax, 16 parts of matt frit, 6 parts of bentonite, 4 parts of aluminum magnesium hydrotalcite, kojic acid dipalmitate 3 parts, 5 parts of calcium phosphate, 4 parts of calcium oxide, 10 parts of stannous chloride.

[0029] The chemical composition of the matt frit includes SiO 2 、Al 2 o 3 、Na 2 O, MgO, PbO, CaCO 3 and MnO 2 , and SiO 2 、Al 2 o 3 、Na 2 O, MgO, PbO, CaCO 3 and MnO 2 The mass ratio is 2:2:1:1:1:1:1.

[0030] The manufacturing process of matte glaze comprises the following steps:

[0031] Grinding, first put the matt frit into the glaze mill and grind it for 1.5 hours until it is evenly mixed, and set aside; then mix the remaining raw material components according to the ratio of raw materials, put them into the glaze mill, and grind them for 32 hours as a mixed raw material spare;

[0032] To adjust the glaze concentration, a...

Embodiment 2

[0036] A kind of matt glaze, its raw material composition comprises the following components by mass: 25 parts of kaolin, 16 parts of clay, 8 parts of borax, 18 parts of matt frit, 5 parts of bentonite, 5 parts of aluminum magnesium hydrotalcite, kojic acid di 2 parts of palmitate, 6 parts of calcium phosphate, 3 parts of calcium oxide, 12 parts of stannous chloride.

[0037] The chemical composition of the matt frit includes SiO 2 、Al 2 o 3 、Na 2 O, MgO, PbO, CaCO 3 and MnO 2 , and SiO 2 、Al 2 o 3 、Na 2 O, MgO, PbO, CaCO 3 and MnO 2 The mass ratio is 2:2:1:1:1:1:1.

[0038] The manufacturing process of matte glaze comprises the following steps:

[0039] Grinding, first put the matt frit into the glaze mill and grind it for 1 hour, until it is evenly mixed, and set aside; then mix the rest of the raw material components according to the ratio of raw materials, put them into the glaze mill, grind for 35 hours, and set aside as a mixed raw material ;

[0040] To ad...

Embodiment 3

[0044] A kind of matt glaze, its raw material composition comprises the following components by mass: 30 parts of kaolin, 10 parts of clay, 12 parts of borax, 15 parts of matt frit, 8 parts of bentonite, 3 parts of aluminum magnesium hydrotalcite, kojic acid di 5 parts of palmitate, 3 parts of calcium phosphate, 5 parts of calcium oxide, 9 parts of stannous chloride.

[0045] The chemical composition of the matt frit includes SiO2 、Al 2 o 3 、Na 2 O, MgO, PbO, CaCO 3 and MnO 2 , and SiO 2 、Al 2 o 3 、Na 2 O, MgO, PbO, CaCO 3 and MnO 2 The mass ratio is 2:2:1:1:1:1:1.

[0046] The manufacturing process of matte glaze comprises the following steps:

[0047] Grinding, first put the matte frit into the glaze mill and grind it for 2 hours, until it is evenly mixed, and set aside; then mix the rest of the raw material components according to the ratio of raw materials, put them into the glaze mill, grind for 30 hours, and set aside as a mixed raw material ;

[0048] To ad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides matte glaze and a production process thereof. The matte glaze comprises 25-30 parts of kaolin, 10-16 parts of clay, 8-12 parts of borax, 15-18 parts of matte frit, 5-8 parts ofbentonite, 3-5 parts of aluminum-magnesium hydrotalcite, 2-5 parts of kojic dipalmitate, 3-6 parts of calcium phosphate, 3-5 parts of calcium oxide and 9-12 parts of stannous chloride. The productionprocess includes: grinding, regulating glaze concentration, applying the glaze and performing oxidation firing to obtain a ceramic product with the matte glaze on the surface. The matte glaze producedaccording to the material proportion has the advantages that the glaze can be stably combined with a green body and be solidified into a polycrystalline structure during ceramic firing to achieve a matte effect, and the glaze is moderate in surface tension, smooth and mellow in surface and fine and smooth in texture. The production process is easy in temperature control, short in firing time andlow in production cost.

Description

technical field [0001] The invention belongs to the technical field of ceramics, and in particular relates to a matte glaze and a manufacturing process thereof. Background technique [0002] Matte glaze is a special glaze between glossy glaze and matte glaze. Its glaze surface has weak reflective ability and no glassy luster on the surface, but it presents a soft silky or velvet luster. After the glaze material of the matt glaze is melted at high temperature, a part of the glaze components is separated into crystals during the cooling process, and the crystals are extremely small and regularly dispersed and embedded in the glass matrix, and the light source illuminates it to produce diffuse reflection. [0003] In order to ensure that the precipitated crystals of the matt glaze are evenly dispersed in the glass matrix, so that the obtained matt glaze has a uniform and compact texture. However, the glazes of the existing matt glazes generally have complex components, and the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/14C03C8/10C04B41/86
Inventor 曾昭育
Owner 福建省德化县哈维陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com