Crystal preparation and crystal prepared thereby
A technology of crystal and potassium aluminum sulfate, which is applied in the field of hollow pyramid crystal and its preparation, can solve problems such as inconvenient operation, insufficient ornamental value, and irregular crystal shape, and achieve strong operability, enhanced observation ability, and simple preparation process easy effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0021] Specifically, the method for preparing the hollow pyramid-shaped crystal of the present invention includes the following steps:
[0022] Step 1: Prepare a predetermined concentration of sodium chloride aqueous solution with a predetermined temperature of hot water.
[0023] Step 2: Add a predetermined mass of potassium aluminum sulfate crystals to the hot sodium chloride aqueous solution prepared in Step 1, and stop stirring after stirring to dissolve.
[0024] Step 3: After the above system is stored at room temperature for a predetermined period of time, sodium chloride and potassium aluminum sulfate precipitate together crystals, and there are inverted hollow pyramid-shaped crystals floating on the surface of the liquid (such as Figure 4 Shown).
[0025] Wherein, in the above step 1, the predetermined temperature of the hot water used for preparing the sodium chloride aqueous solution is 70-100° C., and the mass percentage concentration of the predetermined concentration...
Example Embodiment
[0032] Example 1
[0033] Add 20g of sodium chloride to 100g of hot water at a temperature of 70°C, stir until it is completely dissolved, then add 10g of potassium aluminum sulfate crystals to it, stir until it is completely dissolved, stop stirring, store at room temperature for 2 days, the liquid surface appears more An inverted floating hollow pyramid-shaped crystal with an average side length of 1.5cm at the bottom of the crystal, an average height of 1.2cm, four inner and outer surfaces with a stepped undulating structure, and an average step height of 0.1cm.
Example Embodiment
[0034] Example 2
[0035] Add 35g of sodium chloride to 100g of hot water at a temperature of 100℃, stir until it is completely dissolved, then add 7g of aluminum potassium sulfate crystals to it, stir until it is completely dissolved, stop stirring, store at room temperature for 2 days, the liquid surface appears more A hollow pyramid-shaped crystal floating upside down. Seven days later, the hollow pyramid-shaped crystal floating upside down grew. The bottom side of the crystal is 5.6cm on average, and the height is 5.1cm on average. The four sides of the crystal have a stepped undulating structure. The height of the steps is 0.1cm on average.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap