Method for producing low alkali cement by using high alkali raw materials

A low-alkali cement and raw material technology, which is applied in clinker production, cement production, alkali metal chloride and other directions, can solve the problems that low-alkali cement cannot meet the demand of low-alkali cement and the shortage of low-alkali raw materials, etc.

Active Publication Date: 2009-12-23
岚县金隅水泥有限公司
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006]On the one hand, there is a large demand for low-alkali cement in the market, and on the other hand, the shortage of low-alkali raw materials makes the supply of low-alkali cement far from meeting the demand for low-alkali cement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing low alkali cement by using high alkali raw materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] The production line of a cement plant has a daily output of 3,000 tons of cement clinker (consumption of about 3,000 tons of hot raw materials and about 4,500 tons of raw materials) (using a dry-process cement rotary kiln with a suspension preheater and a precalciner kiln). See Table 1 and Table 2 below for the element content of raw materials and cement products before adding Cl element.

[0042] Table 1 The content of each element in the hot raw meal entering the kiln (%)

[0043] SiO 2

[0044] Content of each element in table 2 cement (%)

[0045] SiO 2

[0046] Under this condition, the alkali equivalent of the cement product is 0.14%+0.658×1.16%=0.90328%, which is greater than 0.60%, which does not meet the requirements of low-alkali cement.

[0047] Calculate the amount of added chlorine should be greater than 14.7 tons, less than 38.97 tons, see the following formula (4) and (5). Add 30 tons of PCB to the kiln system through the kiln he...

Embodiment 2

[0054] The production line of a cement factory produces 3,000 tons of cement clinker per day (dry cement rotary kiln with suspension preheater and precalciner kiln). 5.

[0055] Table 4 The content of each element in the hot raw meal entering the kiln (%)

[0056] SiO 2

[0057] Content of each element in table 5 cement (%)

[0058] SiO 2

[0059] Calculate the amount of added chlorine should be greater than 19.07 tons, less than 41.24 tons see the following formula (6) and (7). Add 7.5 tons of fly ash per hour to the kiln system through the kiln head, with a Cl content of 12%. And 10% of the air volume of the system is drawn out by the device provided by the invention, the hot flue gas first passes through the mixing chamber to cool down and then enters the heat exchanger, heats the heat transfer oil in the heat exchanger, and the heat transfer oil provides heat for other heat-requiring equipment. The flue gas coming out of the heat exchanger is ded...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for producing low alkali cement by using high alkali raw materials, which includes the steps of: putting the raw material limestone with an alkali equivalent about 0.80% into a dry cement rotary kiln through a normal channel for putting the raw material into the kiln; adding chlorine-containing substances into the rotary kiln at the locations of a kiln head, a kiln head fuel burner, a flue chamber at kiln tail end, a pre-decomposition kiln or a pre-burning furnace; opening holes at the bottom part of the pre-decomposition kiln and inducting the chlorine-containing smoke gas enriched in the position into a smoke dust collection system and collecting the smoke dust in the smoke gas. The method for producing low alkali cement by using high alkali raw materials uses the special property that alkali metal ions, chloride ions and sulfate ions mutually affect the melting point temperature under the high temperature coexistence condition, adds the chlorine-containing substances during the production process, and leads the chlorine in wastes to be reacted with the alkali in the raw materials by controlling the proportion between the alkali metal ions, chloride ions and sulfate ions entering the cement kiln, thereby achieving the double effects of reducing the alkali in the cement and processing high-chlorine wastes.

Description

technical field [0001] The invention relates to a method for producing cement and disposing of waste, more specifically, a method for producing low-alkali cement using a dry-process cement production line with a suspension preheater and a precalciner and limestone with a high alkali content, and synergistically Disposal method of high chlorine content waste such as PCB. Background technique [0002] In cement production, the alkali equivalent of raw meal has a direct impact on the quality of cement products. If the raw meal contains a small amount of alkali (Na, K), it will improve the burnability of the raw meal and increase the early strength of the raw meal. However, if the alkali equivalent in the raw meal is too high, causing the alkali equivalent in the clinker to exceed a certain range, such as greater than about 0.80%, it will increase the free calcium in the clinker, resulting in a decrease in the compressive strength and flexural strength of the cement , and affe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B7/36C04B7/43C01D3/04
CPCY02P40/121
Inventor 赵启刚余志辉孙伟舰熊运贵渠永峰
Owner 岚县金隅水泥有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com