Method for preparing polyimide heating film

A polyimide heating film, polyimide film technology, applied in electric heating devices, heating element materials, ohmic resistance heating and other directions, can solve the problems of large temperature fluctuation, small mechanical strength, narrow temperature resistance range, etc. The effect of fast heating rate, large mechanical properties and wide temperature range

Active Publication Date: 2012-08-08
NINGBO JINSHAN NEW MATERIAL
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, ink printing heating film, carbon fiber heating film, polytetrafluoroethylene heating film, etc. are generally used, but these films have common problems such as low mechanical strength, narrow temperature resistance range and low temperature, uneven power, and large temperature fluctuations.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The following are specific examples of the present invention to further describe the technical solutions of the present invention, but the present invention is not limited to these examples.

[0020] The preparation method of the polyimide heating film is mainly to prepare a polyimide heating film that can solve both low-temperature heating and medium-temperature heating. It is mainly prepared according to the following steps. Step A: According to the square size of the heating area of ​​the heating film S, the working voltage V and the power P required for heating, calculate the required equivalent resistance R'=V 2 / P, and then use the electrode layout, that is, the electrode relative distance W and the electrode length L, to calculate the surface resistance of the heating film R=L*R' / W.

[0021] Step B: Calculate the surface resistance R according to step A to produce a conductive polyimide film with a corresponding surface resistance of R. Here, step B specifically ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a method for preparing polyimide heating film, comprising: step A, according to the requirements of square size area S, working voltage V and heating power P of a heating area of the heating film, calculating the required equivalent resistance R'=V2 / P, and then utilizing electrode distribution quantity to calculate the surface resistance R=L*R' / W of the heating film; step B, according to the surface resistance R figured out in the step A, producing a conductive polyimide film corresponding to the surface resistance R; step C, cutting the conductive polyimide film into square heating films with the area of S, and distributing a positive electrode and a negative electrode along the L direction; step D, covering insulating films at the two sides of the heating films for compound protection; and step E, welding or riveting electric wires on the positive electrode and the negative electrode, and making insulating or dampproof protection at the connection part. The method has the advantages that the electrical heating film produced by the method not only solves the problems of low temperature heat emission and intermediate temperate heat emission, but also has wide temperature using range, etc.

Description

technical field [0001] The invention relates to a preparation method of a polyimide heating film. Background technique [0002] There is a great demand for electric heating film in the market, such as the heating film of car seat cushion, which requires high strength. However, ink printing heating film, carbon fiber heating film, polytetrafluoroethylene heating film, etc. are generally used at present, but these films have common problems such as low mechanical strength, narrow temperature range and low temperature, uneven power, and large temperature fluctuations. From the invention of electricity to the present, the way of electric heating has been developing, but at present, the heating method of medium and low temperature tends to be more and more flexible heating, especially in the middle temperature range (80 ℃ to 250 ℃) There is a lack of flexible heating, so the development of An electric heating film that can solve both low-temperature heating and medium-temperatur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H05B3/34H05B3/10C08L79/08C08K9/10C08K3/08C08K3/04
Inventor 岑建军
Owner NINGBO JINSHAN NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products