Silver plated fiber with anti-discoloration layer and manufacturing method thereof

A silver-plated fiber, anti-discoloration technology, used in fiber treatment, coating, sputtering and other directions, can solve the problem of quantitative test standards for antibacterial fibers that cannot include non-dissolving properties, and achieve the effect of preventing discoloration

Inactive Publication Date: 2012-07-11
INGA NANO TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

That is to say, the antibacterial fibers produced under the process parameter range of the working pressure claimed by these patent documents cannot include the quantitative test standards suitable for non-dissolving antibacterial fibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silver plated fiber with anti-discoloration layer and manufacturing method thereof
  • Silver plated fiber with anti-discoloration layer and manufacturing method thereof
  • Silver plated fiber with anti-discoloration layer and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

experiment example 1 007

[0039] Experimental Example 1 2007 / 05 / 11; serial number TX42192 / 2007 / PL

[0040] (a) The fiber body is a 30g basis weight melt-blown non-woven fabric (white), and the silver atoms are agglomerated in a vacuum of 2×10 with argon gas -3 Torr sputtering environment at 0.3w / cm 2 It is formed by sputtering with high sputtering power, the content is about 100ppm, and the anti-tarnish layer is made of titanium and matched with 5w / cm 2 The sputtering power coating is formed, the thickness is

[0041] (b) The fiber body is 50 denier knitted POLYESTER woven fabric (blue), and the silver atom reunion is at a vacuum degree of 3.75×10 -3 Torr sputtering environment at 0.3w / cm 2 It is formed by sputtering with high sputtering power, the content is about 100ppm, and the anti-tarnish layer is made of titanium and matched with 5w / cm 2 The sputtering power coating is formed with a thickness of about

[0042] (a), (b) Two kinds of silver-coated fibers are effective against Staphylococcu...

experiment example 2 007

[0043] Experimental Example 2 2007 / 11 / 24 Number: TXD0455 / 2007 / HH

[0044] The fiber body of this experimental example is a 30g basis weight melt-blown non-woven fabric (white), and the silver atoms are agglomerated at a vacuum degree of 6 × 10 -3 1.5w / cm in Torr's sputtering environment 2 It is formed by sputtering with high sputtering power, the content is about 300ppm, and the anti-tarnish layer is made of titanium and matched with 8w / cm 2 The sputtering power coating is formed with a thickness of about

[0045] The silver-plated fiber of this experimental example has a sterilizing rate of 99.9% for multidrug-resistant Staphylococcus aureus (MRSA, methicillinresistant Staphylococcus aureus), and has passed the quantitative test of AATCC100 (bacteria count determination method) in the United States, and has excellent antibacterial efficacy.

experiment example 3 008

[0046] Experimental Example 3 2008 / 01 / 03 Number: TXD1644 / 2007 / HH

[0047] The fiber body of this experimental example is a 30g basis weight melt-blown non-woven fabric (white), and the silver atoms are agglomerated at a vacuum degree of 8 × 10 -3 Torr sputtering environment at 0.5w / cm 2 It is formed by sputtering with high sputtering power, the content is about 200ppm, the anti-tarnish layer is made of titanium and matched with 8w / cm 2 The sputtering power coating is formed, the thickness is

[0048] The silver-plated fiber of this experimental example has a sterilizing rate of 99.9% against Staphylococcus aureus, and has passed the quantitative test of AATCC100 (bacteria count determination method) in the United States, and has excellent antibacterial efficacy.

[0049] Compared with the current antibacterial fiber, the present invention mainly proposes a new, dry magnetron sputtering method to make antibacterial silver-plated fiber, and the silver-plated fiber obtained b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a silver plated fiber with an anti-discoloration layer and a manufacturing method thereof, and mainly provides the silver plated fiber with the anti-discoloration layer which can prevent discoloration and has anti-bacterial effect. The silver plated fiber comprises a fiber main body which is formed by fiber materials and comprises an outside surface, a plurality of silveratom agglomerations of which the silver atoms agglomerate in a local area of the outside surface, the anti-discoloration layer and a plurality of fine cracks, wherein the anti-discoloration layer which takes metals selected from titanium, gold, platinum, palladium and the like, and / or an alloy formed from the metals as materials forms a similar film pattern to attach on the outside surface and the agglomeration groups in a mode of film coating, and the fine cracks are formed on the anti-discoloration layer so that the anti-discoloration layer is discontinuous; and therefore the silver atom agglomerations are prevented from discoloring through the anti-discoloration layer and the fine cracks, which has no influence on the anti-bacterial effect of the silver.

Description

technical field [0001] The invention relates to a fiber and its manufacturing method, in particular to a fiber with antibacterial effect and its manufacturing method. Background technique [0002] The origin of antibacterial fiber began in World War II. At that time, Germany used antibacterial-treated fiber fabrics to make military uniforms, which greatly reduced the death rate of the wounded. [0003] At present, the production of antibacterial fibers is mainly carried out in conjunction with the common wet spinning method to obtain the greatest economic benefits. [0004] For example, U.S. Patent No. 6,524,508 proposes to utilize chitin as an antibacterial agent. After dissolving it first, the acrylic fiber is immersed in a solution containing dissolved chitin, so that the chitin is coated on the acrylic fiber to obtain Fiber with antibacterial properties. [0005] Another example is the Japanese Patent No. 9059820, which uses titanium dioxide as an antibacterial agent, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M11/83C23C14/35C23C14/14
Inventor 张嘉原徐嘉鸿
Owner INGA NANO TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com