Plant modified polymer powder

A technology of polymerizing rubber powder and modification, applied in the direction of adhesive, adhesive type, cellulose adhesive, etc., to achieve the effect of easy batch scraping, large adjustment range, and no influence on construction performance

Active Publication Date: 2012-06-27
湖北优力帮生态涂料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a plant-modified polymer rubber powder with a large adjustment range of addition amount and a relatively small addition amount to achieve better bonding effect while not affecting the construction performance in view of the defects of tapioca starch or corn starch.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Using konjac and potato as the main ingredients, first wash them to remove impurities and peel them, weigh 25 kg of konjac and 75 kg of potato, crush and mix them, add 0.3 kg of monochloroacetic acid, 0.2 kg of soda ash React with 210 kg of water at 2atm and 120°C for 30 minutes, spray-dry or dry the resultant to 100 mesh, add 5 kg of hydroxyethyl cellulose, and mix evenly to obtain the product.

Embodiment 2

[0015] Using konjac and potato as the main ingredients, first wash and remove impurities and peel them respectively, weigh 30 kg of konjac and 70 kg of potato, crush and mix them, add 0.2 kg of monochloroacetic acid, 0.1 kg of soda ash React with 200 kg of water at 1.5atm and 130°C for 20 minutes, spray dry or dry the resultant to 100 mesh, add 4 kg of hydroxyethyl cellulose, and mix well to obtain the product.

Embodiment 3

[0017] Using konjac and potato as the main ingredients, first wash them to remove impurities and peel them, weigh 30 kg of konjac and 70 kg of potato, grind and mix them, add 0.2 kg of monochloroacetic acid, 0.2 kg of soda ash React with 210 kg of water at 1.2atm and 130°C for 40 minutes, spray-dry or dry the resultant to 100 mesh, add 3 kg of hydroxyethyl cellulose, and mix evenly to obtain the product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses plant modified polymer powder, which is characterized in that: konjac and potatoes are taken as main materials; and a preparation method comprises the following steps of: cleaning the konjac and the potatoes respectively to remove impurities, peeling, weighing the konjac and the potatoes according to a mass ratio of 1:(2-3), crushing, mixing, adding a crosslinking agent, soda ash and water, reacting at the temperature of between 100 and 130DEG C under 1 to 2 atmospheric pressure for 20 to 40 minutes, performing spray drying or drying on the obtained product, crushing into 100 meshes, adding hydroxyethylcellulose, and uniformly mixing to obtain the product. The obtained plant modified polymer powder is a novel putty powder adhesive, is prepared from natural plants serving as the raw materials, is nontoxic, free from formaldehyde pollution, harmless to a human body, low in cost and simple in process, and has the advantages of wide addition amount regulating range, small addition amount, better adhesion effect, no influence on construction property and simple compounding, so the plant modified polymer powder can directly replace cassava starch or corn starch to serve as the putty powder adhesive.

Description

technical field [0001] The invention relates to a novel putty powder binder, in particular to a plant-modified polymerized rubber powder. Background technique [0002] Putty is a decoration material for repairing and leveling the wall to achieve a smooth and delicate effect. It is mainly composed of filler (calcium carbonate), binder (glue or powder), solvent (water or other solvents) and additives (auxiliary). At present, the putty materials used for decoration mainly include on-site mixed type (such as polyvinyl alcohol urea-formaldehyde glue + calcium carbonate powder + cooked rubber powder, etc.), finished water and type (putty powder + water), etc. [0003] Among them, the on-site mixing type needs to add polyvinyl alcohol + water and add polyacrylamide, formaldehyde, urea, etc. to boil at high temperature to make glue (some manufacturers specially make glue products for sale), and then use glue and calcium carbonate, etc. The materials are mixed into paste putty const...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L3/06C08L1/28C09J103/06C09J101/28C09D5/34
Inventor 段建明
Owner 湖北优力帮生态涂料有限公司
PatSnap Eureka logo

PatSnap Eureka turns technology decisions into work you can execute. Powered by our Innovation Knowledge Graph, it runs expert workflows across engineering, life sciences, materials and intellectual property. Get your review-ready output in minutes.

X (Twitter)LinkedInYouTubeSubstack

© 2026 PatSnap. All rights reserved. 

Terms of Service

 | 

Privacy policy

 | 

Modern Slavery Act Transparency Statement