Dusting cleaning antirusting agent and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A rust inhibitor and bactericide technology, applied in the field of rust prevention and chemical cleaning, can solve the problems of weak ash removal function and rust prevention function that cannot meet the cleaning requirements, residual white spots, difficult to remove, etc. The mechanism of action is scientific, and the effect of small dosage
Inactive Publication Date: 2011-08-31
华阳新兴科技(天津)集团有限公司
View PDF4 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] After the parts are processed by machining such as cutting and grinding, a large amount of iron filings, iron powder, oil stains, etc. will remain. These dirt are closely attached to the parts by physical adsorption or electrostatic adsorption, which is difficult to remove
Although the existing cleaning agent can be used for cleaning, the existing cleaning agent has the following problems: 1. After cleaning, the oil on the surface of the metal parts is basically removed, but a large amount of fine particles such as iron powder remain; 2. Some residues are caused by the cleaning agent. 3. Rust in a short period of time after cleaning
The main reason for the above problems is that most of the existing metal cleaning agents are cleaning agents with inorganic substances and hydrophilic surfactants as the main components. Very weak and does not meet the cleaning requirements
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0026] A kind of deashing cleaning antirust agent, its raw material composition, concentration and weight percent scope are respectively:
[0027] Tetrasodium edetate: content 99% ratio 8%
[0028] Sodium polyacrylate: content 30% ratio 3%
[0029] Propylene glycol methyl ether: content 95% ratio 5%
[0030] Isomerized alcohol ether: content 60% ratio 6%
[0031] AEO-3: content 99% ratio 1.5%
[0032] Fungicide: content 90% ratio 1%
[0033] Water: ratio 75.5%
[0034] Its preparation method is as follows:
[0035] (1) Add 50kg of water into the reaction kettle, add tetrasodium ethylenediaminetetraacetic acid at 40°C, and stir to dissolve it.
[0036] (2) Keep the temperature at 40°C, add AEO-3 while stirring, and stir for 45 minutes until uniform;
[0037] (3) After the temperature drops below 30°C, add propylene glycol methyl ether, sodium polyacrylate, and isomeric alcohol ether, and stir for 25 minutes until they are uniformly dissolved;
[0038] (4) Slowly add tri...
Embodiment 2
[0041] Tetrasodium edetate: content 99% ratio 10%
[0042] Sodium polyacrylate: content 30% ratio 6%
[0043] Propylene glycol methyl ether: content 95% ratio 10%
[0044] Isomerized alcohol ether: content 60% ratio 6%
[0045] AEO-3: content 99% ratio 2%
[0046] Fungicide: content 90% ratio 2%
[0047] Water: ratio 64%
[0048] The steps of the preparation method are the same as in Example 1.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a dusting cleaning antirusting agent and a preparation method thereof. The dusting cleaning antirusting agent comprises the following components in percentage by weight: 4.5 to 10 percent of tetrasodium ethylenediamine tetraacetate, 1 to 4.5 percent of sodium polyacrylate, 2.5 to 7.5 percent of heterogeneous alcohol ether, 0.8 to 3 percent of fatty alcohol-polyoxyethylene ether (AEO)-3, 2.5 to 12 percent of propylene glycol monomethyl ether, 0.8 to 3 percent of triazine bacteriacide and the balance of water. The dusting cleaning antirusting agent is suitable for spraying and ultrasonic cleaning; parts processed by the dusting cleaning antirusting agent are not needed to be rinsed and are high in cleanness, the surfaces of the parts do not have granule residues and white dirt residues, and the brightness of the parts can be increased; and the dusting cleaning antirusting agent has long service life and low concentration, and the antirusting period is 5 to 10 days. The dusting cleaning antirusting agent is safe, environment-friendly and low in cost, made of widely and readily available raw material, and is suitable for large-scale production.
Description
technical field [0001] The invention relates to the fields of chemical cleaning and antirust, and relates to an antirust agent, in particular to an antirust agent for ash removal and cleaning with excellent ash removal performance and a preparation method thereof. Background technique [0002] After the parts are processed by machining such as cutting and grinding, a large amount of iron filings, iron powder, oil stains, etc. will remain. These dirt are closely attached to the parts by physical adsorption or electrostatic adsorption, which is difficult to remove. Although the existing cleaning agent can be used for cleaning, the existing cleaning agent has the following problems: 1. After cleaning, the oil on the surface of the metal parts is basically removed, but a large amount of fine particles such as iron powder remain; 2. Some residues are caused by the cleaning agent. 3. Rust in a short period of time after cleaning. The main reason for the above problems is that mos...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more