6082 aluminum alloy melted with cuh and preparation method of aluminum alloy

An aluminum alloy and eutectic technology, applied in the field of high-strength aluminum alloys, can solve the problems of increasing tensile strength and elongation, reducing the service life of parts, decreasing tensile strength and elongation, etc. Enhanced alloy strength and good thermal conductivity

Inactive Publication Date: 2013-08-21
GUIZHOU HUAKE ALUMINUM MATERIAL ENG TECH RES
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the ZAlSi7Mg aluminum alloy is quenched and heated to 555°C and the low melting point eutectic begins to melt until 558°C. The mechanical properties increase with the increase of quenching temperature, but due to the obvious overburning characteristics in the 558°C alloy, the tensile strength and elongation The rate decreases accordingly, while the ZAlCu5Mn aluminum alloy quenching heating temperature is from 540 ° C to 550 ° C, its tensile strength and elongation tend to increase, because the low melting point eutectic begins to remelt at 550 ° C, resulting in tensile strength and elongation A sharp decline
When the parts with burnt structure meet the dynamic load, the influence on the mechanical properties is more obvious, and it is easy to form a source of fatigue in the burnt remelted part, reducing the service life of the parts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A high-strength aluminum alloy, by mass percentage, including 0.7% Si, 0.5% Fe, 0.4% Mn, 0.25% Cr, 0.6% Mg, 0.2% Zn, 0.1% Ti, 0.9% Cu, the balance is Al and unavoidable impurities, the content of each impurity is not more than 0.05% of the total mass percentage, and the content of all impurities is not more than 0.15% of the total mass percentage.

[0029] The present invention also provides a method for preparing the high-strength aluminum alloy, adding CuH in a composite treatment manner, including the following steps:

[0030] Step 1: Prepare materials according to the components of the high-strength aluminum alloy, including 0.7% of Si, 0.5% of Fe, 0.4% of Mn, 0.25% of Cr, 0.6% of Mg, and 0.2% of Zn in the mass percentage of the total product , 0.1% Ti;

[0031] Step 2: Add aluminum ingots or molten aluminum into the smelting furnace first, heat it to melt it completely, add the materials prepared in Step 1 first according to the formula ratio, make it completely d...

Embodiment 2

[0036] A high-strength aluminum alloy, by mass percentage, including 0.95% Si, 0.4% Fe, 0.7% Mn, 0.2% Cr, 0.9% Mg, 0.15% Zn, 0.08% Ti, 1.45% Cu, the balance is Al and unavoidable impurities, the content of each impurity is not more than 0.05% of the total mass percentage, and the content of all impurities is not more than 0.15% of the total mass percentage.

[0037] The present invention also provides a method for preparing the high-strength aluminum alloy, adding CuH in a composite treatment manner, including the following steps:

[0038] Step 1: Prepare materials according to the components of the high-strength aluminum alloy, including 0.95% of Si, 0.4% of Fe, 0.7% of Mn, 0.2% of Cr, 0.9% of Mg, and 0.15% of Zn in the mass percentage of the total product , 0.08% Ti;

[0039] Step 2: Add aluminum ingots or molten aluminum into the smelting furnace first, heat it to melt it completely, add the materials prepared in Step 1 first according to the formula ratio, make it complet...

Embodiment 3

[0044] A high-strength aluminum alloy, by mass percentage, including 1.3% Si, 0.3% Fe, 1.0% Mn, 0.10% Cr, 1.2% Mg, 0.11% Zn, 0.06% Ti, 2.0% Cu, the balance is Al and unavoidable impurities, the content of each impurity is not more than 0.05% of the total mass percentage, and the content of all impurities is not more than 0.15% of the total mass percentage.

[0045] The present invention also provides a method for preparing the high-strength aluminum alloy, adding CuH in a composite treatment manner, including the following steps:

[0046] Step 1: Prepare materials according to the components of the high-strength aluminum alloy, including 1.3% Si, 0.3% Fe, 1.0% Mn, 0.10% Cr, 1.2% Mg, and 0.11% Zn in the mass percentage of the total product , 0.06% Ti;

[0047] Step 2: Add aluminum ingots or molten aluminum into the smelting furnace first, heat it to melt it completely, add the materials prepared in Step 1 first according to the formula ratio, make it completely dissolved and m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a 6082 aluminum alloy melted with CuH and a preparation method of the aluminum alloy. The method comprises the following steps of: heating aluminum ingots or molten aluminum till complete melting; adding Si, Fe, Mn, Mg, Cr, Zn and Ti, and completely dissolving and melting the elements; preserving the heat at the temperature of between 700 and 1,000 DEG C after refining, and obtaining an alloy melt; performing degassing purification operation on the alloy melt by using nitrogen or inert gas or mixed gas of the nitrogen and the inert gas in a random ratio, and continuously introducing the gas till the reaction is finished; adding CuH powder into the alloy melt in a fluidized form together with the gas; stirring to make the CuH distributed uniformly in the alloy melt and fully reacted with the alloy melt; and standing, regulating the temperature to 680-730 DEG C, and discharging the molten alloy for casting. By the method, the defects of the properties of the conventional aluminum alloy can be overcome, the toughness, the forming property and the hardening capacity of the aluminum alloy are improved, and a high-end base material is provided for efficient deep processing.

Description

technical field [0001] The invention relates to a high-strength aluminum alloy and a preparation method thereof. Background technique [0002] Copper (Cu) is the most important and basic alloying element in all heat-treatable aluminum alloys. It mainly forms a soluble metal compound strengthening phase with other elements to improve the strength and heat resistance of the alloy. Copper in the 6XXX series alloys can compensate for the strength loss caused by the parking effect and can refine the Mg 2 Si, to increase the strength of the T6 state. [0003] However, when the Cu content in the 6XXX series alloy exceeds 0.5% (mass percentage), it is easy to produce coarse second phase particles and eutectic structure in the casting process, as well as the inhomogeneous concentration of components inside the solid solution. [0004] The characteristics of various non-metallic inclusions and microporosity that hinder the diffusion of the second phase determine that the cast alumin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/18C22C1/02C22B21/06C22B9/05
Inventor 门三泉车云张中可李祥
Owner GUIZHOU HUAKE ALUMINUM MATERIAL ENG TECH RES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap